盐和水蒸气协同作用下TiAl合金腐蚀性能研究及其防护

研究了在700℃盐和水蒸气协同作用下TiAlNb合金的腐蚀行为以及溅射涂层对TiAlNb合金的防护作用。结果表明，在盐和水蒸气协同作用下，溅射TiAlCrAg涂层对TiAlNb合金具有一定的保护作用。盐和水蒸气协同作用加速了合金以及涂层的腐蚀。挥发性气体氯化物对α2相的循环作用是TiALNb合金腐蚀的主要原因。涂层中较少的α2相以及Laves相中较高的Cr含量是腐蚀有所减缓的主要原因。     

钼酸铵复合缓蚀剂对LY12铝合金的缓蚀作用

采用电化学方法研究了钼酸盐、锌盐和苯并三氮唑 (BTA)对LY12铝合金在 3 5 %NaC1溶液中的缓蚀作用。结果表明 ,随着钼酸盐浓度的增大 ,缓蚀效率增大 ,达到一个最大的值后基本保持不变。钼酸盐通过抑制铝合金的阴极反应和阳极溶解实现缓蚀作用。钼酸盐与锌盐和BTA复合后 ,明显提高了对铝合金的缓蚀作用 ,表现出良好的协同效应     

PVC五金件专用料的热稳定性研究

研究了多种稳定剂以及它们之间的相互协同作用对PVC五金件专用料的热稳定性的影响 ,结果表明 :选用三盐基硫酸铅作为主稳定剂 ,二盐基亚磷酸铅、硬脂酸钡和硬脂酸作为助稳定剂 ,在适当的配比下 ,再配合使用环氧大豆油和亚磷酸三苯酯将可使PVC的动态热稳定时间提高到 36min     

聚合物防老化稳定剂的协同作用机理

从聚合物热氧老化和光氧老化机理出发，介绍了不同稳定剂间的相互作用，可能产生的协同及反协同作用机理以及一些实用实例。     

Role of La2O3 in Pd-Supported Catalysts for Methanol Decomposition

Systems of Pd supported on various La₂O₃-modified -Al₂O₃ and CeO₂–Al₂O₃ catalysts were tested for catalytic methanol decomposition and characterized by means of XRD, BET, TPR, H₂-chemisorption and CO–FTIR. The addition of lanthanum significantly improved the selectivity of CO and H₂ for all the catalysts but showed a different influence on the catalytic activity in two systems. Methanol conversion decreased on La₂O₃-modified Pd/-Al₂O₃ catalysts, in line with the reduction of Pd dispersion, while the addition of La₂O₃ improved the dispersion of Pd and reinforced Pd–CeO₂ interaction for La₂O₃-modified Pd/CeO₂–Al₂O₃ catalysts, which resulted in a high production rate of CO and H₂. Thus, a synergistic effect between CeO₂ and La₂O₃ was observed on -Al₂O₃-supported Pd catalyst for methanol decomposition.     

镁铝水滑石及其复合体系对PVC热稳定性能的调控

采用比色法、热失重法等研究了不同镁铝摩尔比的水滑石(LDHs)对PVC糊热稳定性能的影响。结果表明,在镁铝比分别为2、3、4的样品中,镁铝比为2的LDHs对PVC的热稳定效果最佳;将其与传统的铅盐、有机锡稳定剂复配,均具有良好的协同效应,可以实现对PVC糊热稳定性能的控制。其中,PVC/Mg-AlLDHs/Sn以100∶1.5∶1.5(质量份数,下同)比例复合后的体系,不仅热稳定性能优于传统的的铅盐体系,而且具有较低的糊黏度及较好加工流变性能。     

SnO2和SiO2用于PVC的阻燃消烟及协同作用

研究了二氧化锡和二氧化硅对软PVC阻燃消烟性的影响。通过对极限氧指数、剩炭率、烟密度的测定和DTATG曲线的分析证明,添加8g二氧化锡/二氧化硅复合阻燃剂的PVC的氧指数和剩炭率比未添加的分别增高5.5个单位和4.1%,烟密度降低16.4%,降解活化能分别降低38kJ/mol和23.1kJ/mol,从而证明二氧化锡/二氧化硅复合阻燃剂对于PVC是一种很好的阻燃消烟剂,二氧化锡和二氧化硅有很好的协同作用。同时证明这种复合阻燃剂能代替三氧化二锑,使产品的成本进一步降低。     

The synergistic effect of dicyandiamide and resorcinol in the curing of epoxy resins

The synergistic effect of dicyandiamide (Dicy) and phenolic substances was studied, with resorcinol as a model compound. It was found that when Dicy and resorcinol are used jointly, the curing temperature of epoxy resin can be significantly lowered. FTIR and DSC data were used to illustrate the mechanism of the synergism. The addition of the phenolic hydroxyl group to epoxide was facilitated by Dicy, which favors the formation of phenoxy anions. The reaction of Dicy with epoxide was facilitated by resorcinol, which can exert “electrophilic assistance” for the addition of the amino group to epoxide. The presence of resorcinol also favors the addition of the hydroxyl group to the cyano group. The thermal and mechanical properties of the epoxy resins cured with Dicy/resorcinol or Dicy/phloroglucinol were studied. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 1869–1874, 2003     

Synergistic effects of doped Fe3+ and deposited Au on improving the photocatalytic activity of TiO2

Fe³⁺ doped together with Au deposited TiO₂ (Au/Fe³⁺–TiO₂) was successfully prepared, which shows excellent photocatalytic activity for degradation of methyl orange (MO) under both UV and visible light (λ > 420 nm) illumination. Fe³⁺ has been confirmed by EPR to substitute for Ti⁴⁺ in the TiO₂ lattice, and Au exists as Au⁰ on the surface of the photocatalyst indicated by the results of XRD. Fe³⁺ and Au have synergistic effects on improving the photocatalytic activity of TiO₂. A proposed mechanism concerning the synergistic effects is discussed to explain the improvement of the photocatalytic activities.     

Mechanical and dynamic mechanical properties of jute fibers–Novolac–epoxy composite laminates

A study was done of jute composite using a polymer matrix of epoxidized Novolac resin (ENR), diglycidyl ether of bisphenol A (DGEBA)–based epoxy, and their blends with different weight percentages of the resins. It was found that on blending ENR with DGEBA, the storage modulii at room temperature are enhanced by about 100% or more in the case of 30 and 40% ENR‐containing matrices, whereas the enhancement in the case of 20 and 12% ENR‐containing matrices is only 50% that of the pure matrix. It was also observed that the tan δ peak heights of the composites containing 30 and 40% ENR are closer to that of 20% ENR‐containing composite. The probable explanation drawn on the basis of experimental findings of DMA and mechanical analysis is that by blending ENR with DGEBA epoxy it is possible to manufacture jute composites with increased stiffness without sacrificing their ductility. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 2800–2807, 2002