Wear and corrosion properties of wollastonite and boron nitride doped,hydroxyapatite-based HAp-Wo-BN composite coatings prepared by pulsed laser deposition

In this study, hydroxyapatite-based hydroxyapatite-wollastonite-boron nitride (HAp-Wo-BN) composite film was formed on the surface of Ti6Al4V by pulsed laser deposition (PLD). Based on a survey in scientific literature, it is presumed that this is the first time such a process is being undertaken. The wear and corrosion resistance of this film were analyzed comparatively in simulated body fluid (SBF) to simulate the human body environment. In the coating, HAp was used to form a bone-like layer, wollastonite was to enhance bone-tissue regeneration and BN was used for its bone-tissue healing and anti-bacterial properties. The results showed that the wear as well as the corrosion resistance of all samples after PLD treatment increased. Relatively the best wear resistance was achieved from boron nitride and wollastonite doped hydroxyapatite layers, where the best corrosion resistance was from the ones that consisted of only hydroxyapatite.     

Electrodeposition of B,Ni co-doped diamond-like carbon films on AZ91D magnesium alloy: Corrosion and wear resistance

Diamond-like carbon (DLC) possesses brilliant and excellent properties, including excellent corrosion resistance as well as outstanding wear resistance. Ni and B co-doped DLC films were deposited on AZ91D magnesium alloy by electrodeposition under mild conditions (300 V and 25°C). Uniform and dense morphology of co-doped DLC films were observed, and Ni and B were uniformly incorporated into the carbon-based films. Among all the electrodeposits, the appearance of D and G peaks near 1330 and 1570 cm⁻¹ revealed that the as-deposited films were typical DLC films. As the addition of Ni was increased to 0.05 g, the highest microindentation hardness, the lowest friction coefficient, and wear loss were achieved to be 164.5 HV, 0.3, and 0.6 × 10⁻⁵ kg/m, respectively. The amorphous carbon films fabricated at 0.05 g Ni had the lowest corrosion current density and the most positive corrosion potential, which was mainly due to the small and dense granular structure effectively hindering the penetration of corrosion media.     

Effect of laser power density on the electrochromic properties of WO3 films obtained by pulsed laser deposition

Pulsed laser deposition (PLD) was used to prepare tungsten trioxide (WO₃) films on ITO substrates with a varying laser power density of 4.0–5.5 W/cm². XPS indicated that when the laser power density decreased, the peak positions of the W 4f and O 1s orbits shifted slightly to low energy due to the difference in oxygen vacancies. As the laser power density decreased, W⁶⁺ gradually replaced the lattice position of O^2?, increasing oxygen vacancies in the lattice. The transmittance modulated values (ΔT) were over 44% at 830 nm, indicating strong absorption by the WO₃ thin films in the near-infrared ray. The switching time of the WO₃ thin films between bleached states and coloured states decreased as the laser power density increased due to the amorphous structure, morphology, and lower oxygen deficiency at a high power density. The high ΔT and very fast switching time of t_b (1.09 s) and t_c (6.01 s) demonstrated the excellent electrochromic (EC) properties of the WO₃ films prepared by PLD.     

Phase constitution,microstructure and mechanical properties of a Ni-based superalloy specially designed for additive manufacturing

In this study, a kind of Ni-based superalloy specially designed for additive manufacturing (AM) was investigated. Thermo-Calc simulation and differential scanning calorimetry (DSC) analysis were used to determine phases and their transformation temperature. Experimental specimens were prepared by laser metal deposition (LMD) and traditional casting method. Microstructure, phase constitution and mechanical properties of the alloy were characterized by scanning electron microscopy (SEM), transmission scanning electron microscopy (TEM), X-ray diffraction (XRD) and tensile tests. The results show that this alloy contains two basic phases, γ/γ', in addition to these phases, at least two secondary phases may be present, such as MC carbides and Laves phases. Furthermore, the as-deposited alloy has finer dendrite, its mean primary dendrite arm space (PDAS) is about 30-45 μm, and the average size of γ' particles is 100-150 nm. However, the dendrite size of the as-cast alloy is much larger and its PDAS is 300-500 μm with secondary and even third dendrite arms. Correspondingly, the alloy displays different tensile behavior with different processing methods, and the as-deposited specimen shows better ultimate tensile stress (1,085.7±51.7 MPa), yield stress (697±19.5 MPa) and elongation (25.8%±2.2%) than that of the as-cast specimen. The differences in mechanical properties of the alloy are due to the different morphology and size of dendrites, γ', and Laves phase, and the segregation of elements, etc. Such important information would be helpful for alloy application as well as new alloy development.     

Vapor linker exchange of partially amorphous metal–organic framework membranes for ultra-selective gas separation

Metal–organic framework (MOF) membranes are promising for efficient separation applications. However, the uncontrollable pathways at atomic level impede the further development of these membranes for molecular separation. Herein we show that vapor linker exchange can induce partial amorphization of MOF membranes and then reduce their transport pathways for precisely molecular sieving. Through exchanging MOF linkers by incoming ones with similar topology but higher acidity, the resulted metal-linker bonds with lower strength cause the transformation of MOF membranes from order to disorder/amorphous. The linker exchange and partial amorphization can narrow intrinsic apertures and conglutinate grain boundary/crack defects of membranes. Because of the formation of ultra-microporous amorphous phase, the MOF composite membrane shows competitive H₂/CO₂ selectivity up to 2400, which is about two orders of magnitude higher than that of conventional MOF membranes, accompanied by high H₂ permeance of 13.4 × 10⁻⁸ mol m⁻² s⁻¹ Pa⁻¹ and good reproducibility and stability.     

Dielectric and ferroelectric properties of multilayer BaTiO3/NiFe2O4 thin films prepared by solution deposition technique

In this work different lead-free multilayered structures, composed of perovskite BaTiO₃ and spinel NiFe₂O₄ thin layers, were obtained by solution deposition method. Structural characterization of the sintered thin films confirmed the well-defined layered structure with overall thickness from 160 to 600 nm, crystalline nature of perovskite BaTiO₃ and spinel NiFe₂O₄ phases without secondary phases (after sintering below 900 °C) and grains on nanometer scale. Dielectric properties of the multiferroic multilayer BaTiO₃/NiFe₂O₄ thin films were analyzed in temperature and frequency range from 30 °C to 200 °C and 100 Hz to 1 MHz, respectively. In comparison to the pure BaTiO₃ films, the introduction of ferrite layer reduces dielectric response and increases low frequency permittivity dispersion of the multilayer thin films. The multilayer samples have shown relatively low dielectric loss with stronger contribution of conductivity at higher temperatures, and characteristic broad peak representing “relaxation” of the interface charge accumulation.     

A review of thin film electrolytes fabricated by physical vapor deposition for solid oxide fuel cells

The ohmic resistance in solid oxide fuel cells (SOFCs) mainly comes from the electrolyte, which can be reduced by developing novel electrolyte materials with higher ionic conductivity and/or fabricating thin-film electrolytes. Among various kinds of thin-film fabrication technology, the physical vapor deposition (PVD) method can reduce the electrolyte thickness to a few micrometers and mitigate the issues associated with high-temperature sintering, which is necessary for wet ceramic methods. This review summarizes recent development progress in thin-film electrolytes fabricated by the PVD method, especially pulsed laser deposition (PLD) and magnetron sputtering. At first, the importance of the substrate surface morphology for the quality of the film is emphasized. After that, the fabrication of thin-film doped-zirconia and doped-ceria electrolytes is presented, then we provide a brief summary of the works on other types of electrolytes prepared by PVD. Finally, we have come to the summary and made perspectives.     

Investigation of La0.6Sr0.4Co1-xNixO3-δ (x=0, 0.2, 0.4, 0.6, 0.8) catalysts on solid oxide fuel cells anode for biogas dry reforming

The introduction of catalyst on anode of solid oxide fuel cell (SOFC) has been an effective way to alleviate the carbon deposition when utilizing biogas as the fuel. A series of La_0.6Sr_0.4Co_1-xNi_xO_3-δ (x = 0, 0.2, 0.4, 0.6, 0.8) oxides are synthesized by sol-gel method and used as catalysts precursors for biogas dry reforming. The phase structure of La_0.6Sr_0.4Co_1-xNi_xO_3-δ oxides before and after reduction are characterized by X-ray diffraction (XRD). The texture properties, carbon deposition, CH₄ and CO₂ conversion rate of La_0.6Sr_0.4Co_1-xNi_xO_3-δ catalysts are evaluated and compared. The peak power density of 739 mW cm^?2 is obtained by a commercial SOFC with La_0.6Sr_0.4Co_0.4Ni_0.6O_3-δ catalyst at 850 °C when using a mixture of CH₄: CO₂ = 2:1 as fuel. This shows a great improvement from the cell without catalyst for internal dry reforming, which is attributed to the formation of NiCo alloy active species after reduction in H₂ atmosphere. The results indicate the benefits of inhibiting the carbon deposition on Ni-based anode through introducing the La_0.6Sr_0.4Co_0.4Ni_0.6O_3-δ catalyst precursor. Additionally, the dry reforming technology will also help to convert part of the exhaust heat into chemical energy and improve the efficiency of SOFC system with biogas fuel.     

Diluted chemical bath deposition of CdZnS as prospective buffer layer in CIGS solar cell

In this study, dilute chemical bath deposition technique has been used to deposit CdZnS thin films on soda-lime glass substrates. The structural, morphological, optoelectronic properties of as-grown films have been investigated as a function of different Zn²⁺ precursor concentrations. The X-ray diffractogram of CdS thin-film reveals a peak corresponding to (002) plane with wurtzite structure, and the peak shift has been observed with the increase of the Zn²⁺ concentration upon formation of CdZnS thin film. From morphological studies, it has been revealed that the diluted chemical bath deposition technique provides homogeneous distribution of film on the substrate even at a lower concentration of Zn²⁺. Optical characterization has shown that the transparency of the film is influenced by Zn²⁺ concentration and when the Zn²⁺ concentration is varied from 0 M to 0.0256 M, bandgap values of resulting films range from 2.42 eV to 3.90 eV while. Furthermore, electrical properties have shown that with increasing zinc concentration the resistivity of the film increases. Finally, numerical simulation validates and suggests that CdZnS buffer layer with composition of 0.0032 M Zn²⁺ concentration would be a promising candidate in CIGS solar cell.