Influence of high energy ball milling on structural,microstructural and optical properties of TiO2 nanoparticles

The influence of high-energy ball milling on structural, microstructural, and optical properties of TiO₂ by modifying the nanoparticle size was studied. Five samples were extracted at different milling times (0, 2, 4, 8, and 13 h). The average particle sizes estimated by dynamic light scattering (DLS) were 205, 155.8, 116.8, 82.9, and 82.7 nm at 0, 2, 4, 8, and 13 h, respectively. X-ray diffraction analysis confirmed progressive broadening of the peaks as the milling time elapsed. Besides, a correlation was found between d spacing and the average crystal size. The UV–Vis diffuse reflectance spectra of TiO₂ revealed a decrease in reflectance due to particle size reduction. Similarly, an alteration of the bandgap transition energy was presented, whose values gradually decreased from 2.966 eV to 2.861 eV for the sample without and with the maximum duration milling performed (13 h), respectively. Likewise, the SEM analysis showed a distribution in nanoparticle size that became more homogeneous and smaller average grain size as the milling duration was longer.     

水力空化改质对重质原油沥青质及性质的影响

利用水力空化过程产生局部的高温、高压、高射流以及强大的剪切力等极端化学物理条件改质处理沙特重质原油，试验结果表明：沙特重质原油经过水力空化改质后粘度由13.61降低至7.22mm2/s，残碳由7.16%降低至6.48%，实沸点蒸馏后减压渣油降低1个百分点。进一步采用APPI FT-IR MS、XRD、FT-IR、SEM和粒度分布等技术研究了水力空化改质对沙重原油分子组成，沥青质团聚体微晶结构、沥青质胶束粒径分布、沥青质官能团、沥青质形貌等方面的影响，从分子角度阐述空化改质重油的机理。研究结果表明：水力空化改质后沙重原油分子量分布、芳烃类化合物缔合作用变小；沥青质对低DBE化合物吸附性能降低；沥青质团聚体微晶结构更加松散；沥青质胶束粒度分布降低；沥青质分子相互团聚作用力减弱。进一步考察了水力空化改质前后减压渣油延迟焦化性能，改质处理后焦炭产率降低1.85个百分点，液体收率和气体产率分别增加1.52和0.33个百分点，水力空化改质对沥青质性质、结构特点的改善能够有效的提高其加工性能。     

Post-erosion mechanical responses of internally unstable gap-graded soil under drained torsional simple shear and triaxial compression

Internal erosion is a major threat to hydraulic earth structures, such as river levees and dams. This paper focuses on suffusion and suffosion phenomena which are caused by the movement of fine particles in the granular skeleton due to seepage flow. The present study investigates the impact of internal erosion on the dynamic response under cyclic torsional shear and monotonic responses under triaxial compression and torsional simple shear. A series of experiments, using a gap-graded silica mixture with a fines content of 20%, is performed under loose, medium, and dense conditions using a novel erosion hollow cylindrical torsional shear apparatus. The erosion test results indicate that the critical hydraulic gradient and the rate of erosion are density-dependent, where a transition from suffosion to suffusion is observed as the seepage continues. Regardless of the sample density, variations in the radial strain and particle size distribution, along the specimen height after erosion, are no longer uniform. Furthermore, the dynamic shearing results show that the small-strain shear modulus increases, but the initial damping ratio decreases after internal erosion, probably due to the removal of free fines. In addition, the elastic threshold strain and reference shear strain values are found to be higher for the eroded and non-eroded specimens, respectively. Finally, based on drained monotonic loading, the post-erosion peak stress ratio increases remarkably under triaxial compression, while that under torsional simple shear depends on the relative density where the direction of loading is normal to the direction of seepage. These observations indicate that the horizontal bedding plane becomes weaker, while the vertical one becomes stronger after downward erosion.     

Effect of the particle size ratio on macro- and mesoscopic shear characteristics of the geogrid-reinforced rubber and sand mixture interface

As a new type of material for civil engineering projects, the rubber and sand mixture is widely used in roadbed fillers, offering environmental benefits over traditional tyre disposal methods. This study uses a large-scale direct shear apparatus to examine the interface shear properties of the geogrid-reinforced rubber and sand mixture, considering different particle size ratios (r), rubber contents, and normal stresses. Based on indoor tests, direct shear models of the mixture with different values of r are established in PFC^3D, revealing the meso-mechanical mechanism of the mixture in the direct shear process. The results show that when r is greater than 1, incorporating a certain amount of rubber particles can increase the shear strength of the mixture. The r values of 15.78, 7.63, and 3.98 correspond to an optimal rubber content of 30%, 10%, and 20%, respectively. When r is less than 1, mixing rubber particles can only reduce the shear strength of the mixture. When the rubber content is low, the smaller the value of r, the greater is the thickness of the shear band. Furthermore, the normal and tangential contact forces are greater. The fabric anisotropy evolution law of the mixture is consistent with the change in the contact force distribution.     

Structural,optical, cytotoxicity,and antimicrobial properties of MgO,ZnO and MgO/ZnO nanocomposite for biomedical applications

In this study, MgO nanoparticles were successfully fabricated and incubated inside ZnO NPs to form MgO/ZnO nanocomposite for biomedical applications. The x-ray diffraction analysis of MgO, ZnO, and MgO/ZnO has shown the single-phase x-ray diffraction patterns through X'pert High score. The crystallite sizes were calculated as 18 nm, 42 nm, and 53 nm, respectively. The average particle size of MgO, ZnO, and MgO/ZnO nanopowders depicted from secondary electron images of field emission electron microscopy were 56 nm, 400 nm, and 450 nm, respectively. The presence of MgO NPs inside ZnO NPs was confirmed by transmission electron microscopy. The elemental dispersive spectroscopy of MgO, given the peaks of oxygen and magnesium, also showed only zinc and oxygen peaks in ZnO, which confirms no other impurities in MgO and ZnO powders. The elemental analysis of MgO/ZnO nanocomposite showed the peaks of Zinc and Oxygen, along with a tiny peak of Mg. The photoluminescence and UV–vis spectroscopy revealed the absorbance fluorescence limit of the nanomaterials. Fourier transform infrared spectroscopy confirmed the several groups present in the nanocomposite. The biocompatibility of MgO, ZnO, and MgO/ZnO was observed with human peripheral blood mononuclear cells. The cytotoxicity studies were also performed against human cancer (liver and breast) cell lines. The MgO, ZnO, and MgO/ZnO exhibited the antimicrobial properties against Escherichia coli and Staphylococcus aureus.     

Grain size influence on the flexibility and luminous intensity of inorganic CaTiO3:Pr3+ crystal nanofibers

Traditional inorganic materials exhibit rigidity owing to the lack of polymer chains in polymer materials or atom slipping in metals. However, nanometerization has been recently proposed for the conversion of inorganic oxide materials into flexible materials. Herein, the flexible inorganic luminescent material, CaTiO₃:0.2%Pr³⁺, was synthesized through electrospinning, and the macroscopic flexibility of pure inorganic CaTiO₃:0.2%Pr³⁺ was achieved. The flexible membrane was characterized via X-ray diffraction, thermogravimetry, scanning electron microscopy (SEM), and photoluminescence analyses. The grain size was analyzed at various calcination temperatures via SEM, and the results suggested that the increase in the calcination temperature resulted in the growth of crystal grains. Studies have reported that the growth of crystal grains is beneficial for improving the luminescence performance; however, to obtain better flexibility, smaller crystal grains are required. This study provides an important reference for the design of flexible inorganic materials.     

High energy-storage performance of lead-free AgNbO3 antiferroelectric ceramics fabricated via a facile approach

AgNbO₃ lead free AFE ceramics are considered as one of the promising alternatives to energy storage applications. In the majority of studies concerning the preparation of AgNbO₃ AFE ceramics, an oxygen atmosphere is required to achieve high performance, increasing the complexity of the fabrication process. Herein, a facile approach to preparing AgNbO₃ ceramics in the ambient air was reported, in which the AgNbO₃ ultrafine powder with stable perovskite structure was synthesized by hydrothermal method instead of the conventional ball milling process, leading to a lower temperature of phase formation and thus smaller grain size. The resulting ceramics sintered at 940 °C displayed high breakdown strength (216 kV/cm) and a recoverable energy density of 3.26 J/cm³ with efficiency of 53.5 %. Also, the high thermal stability of recoverable energy density (with minimal variation of ≤20 %) and efficiency (≤ 10 %) over 30–150℃, enables AgNbO₃ ceramics achieved to be a promising candidate for energy storage applications.     

Process parameters influence on zone refining and thermodynamics analysis of 1,2-diphenylethane

Effective distribution coefficients of 9 impurities in 1,2-diphenylethane have been calculated by directional crystallization under different ambient frozen temperature. The effect of varied zone size, temperature difference between the melt and ambient frozen environment, number of zone on purity of 1,2-diphenylethane have been also investigated during the process of zone refining. The results indicate that the product purity in the intermediate purified region with varied zone size is higher 0.04%-0.2% than that with constant zone size. The product purity increases with temperature difference between the melt and ambient frozen environment. The appropriate temperature difference is adopted 50℃. The product purity in the intermediate region of sample bar with 2 molten zones is higher 0.05%-0.43% than that with 1 molten zone. In addition, the change of enthalpy and entropy between impurities and 1,2-diphenylethane have been determined.