脱硫胶粉在乳化改性沥青中的应用

考察了不同规格胶粉及不同脱硫程度的脱硫胶粉对橡胶改性乳化沥青性能的影响,结果表明,采用100目胶粉即可制备出橡胶改性乳化沥青,但乳化沥青的性能较差;采用活化度为50%左右的100目脱硫胶粉制备乳化沥青时,脱硫胶粉的用量相比于胶粉可大幅提高;在通过外掺100目50%左右活化度的脱硫胶粉(质量分数15%,以沥青计,下同)和质量分数2%的苯乙烯-丁二烯-苯乙烯嵌段共聚物改性的乳化沥青中添加质量分数1%的丁苯胶乳,所制备橡胶改性乳化沥青无筛上剩余物,5 d储存稳定性为2.9%,蒸发残留物的25℃针入度、软化点和5℃延度分别为55 (0.1 mm)、64.5℃和22.5 cm,能够满足乳化改性沥青的技术指标要求。     

磁流变阻尼器抑制转子系统振动试验

针对大型旋转机械通过临界转速时振动过大及运行中故障频发等问题,搭建转子试验台,模拟启停机过程和碰摩、不对中故障。不改变原有支撑形式,安装自主设计的磁流变阻尼器,在不停机的情况下,试验研究阻尼器抑制转子通过临界转速时振动过大及各类故障振动。试验结果表明,阻尼器可以有效抑制转子系统临界转速附近的振动,降幅在60%以上;转子发生碰摩或不对中故障时,阻尼器可以降低其高倍频振动。     

Protoplast from <Emphasis Type="Italic">β</Emphasis>-carotene-producing fungus <Emphasis Type="Italic">Blakeslea trispora</Emphasis>: Preparation,regeneration and validation

The effects of key parameters on the preparation and regeneration of protoplast from the β-carotene-producing fungus Blakeslea trispora were discussed in this paper, including the combination of various enzymes, mycelial age, digesting time and temperature, pH value, osmotic stabilizers, pretreatment, culture medium and culture method. Under the condition of mixed enzymes in osmotic stabilizer (0.6 M NaCl) combined with 2% lysozyme, 3% cellulase and 3% snailase, the highest protoplast yield, as high as 7.48×106 protoplasts/mL, was obtained when mycelial age was 60 h at pH 5.0–6.0 with digesting for 14–16 h at 28 °C. After purification of the obtained protoplasts, they were regenerated in PDA regenerative medium using bilayer plate culture method. To validate the usability of the protoplasts, a novel plasmid with green fluorescent protein (GFP) was used in transformation for easy visual observation. The results showed that the protoplasts prepared by the optimized method were active and applicable in further gene manipulation experiments. This work was presented at 13 ^th YABEC symposium held at Seoul, Korea, October 20–22, 2007.     

A Golden Section approach to optimization of automotive friction materials

A Golden Section approach combined with relational grade analysis is proposed as an experimental design tool helpful in the development of new automotive friction materials. Golden Section was used to design the volume fraction of the components systematically. The changes in friction performance (friction coefficient and wear) measured using Friction Assessment and Screening Test (FAST) can be correlated with component variations by use of relational grade analysis. This approach was utilized to optimize a non-metallic friction material containing seven ingredients including two fibers (aramid and slag fiber), four fillers (Al₂O₃, BaSO₄, graphite and nitrile rubber) and one binder (benzoxazine). The volume fraction of seven components was varied simultaneously in order to optimize the parameters of friction coefficient and wear with a minimum number of tests. Three phases were performed to find the optimal proportion of the components. The optimized friction performance was obtained after doing 19 formulation experiments.     

Aroused problems in the deposition of diamond-like carbon films by using the liquid phase electrodeposition technique

Hydrogenated diamond-like carbon (DLC) films were prepared by using liquid phase electrodeposition technique. The effects of the applied potential and the carbon sources on the deposition process and film structures were studied. It has been found that the organic liquids with high dielectric constants, small viscosities and the methyl group bonding to the polar group are appropriate carbon sources. The increasing of potential improves the formation of sp³ carbon during the deposition process. In a high electric field, organic molecules are polarized and reacted on the surface of the electrode, turning out DLC and other products. It is believed that the reaction follows a polarization-reaction mechanism.     

Preparation of ultra-fine polyimide fibers containing silver nanoparticles via in situ technique

Ultra-fine polyimide fibers containing silver nanoparticles were prepared by electrospinning from poly(amic acid)/(trifluoroacetylacetonoto)silver(I) (PAA/AgTFA) solution. Thermal curing of the silver(I)-containing fibers led to cycloimidization of the poly(amic acid) into polyimide with concomitant silver(I) reduction. The polyimide–silver fibers were characterized by FT-IR, X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The average diameters of silver nanoparticles and ultra-fine PI fibers electrospun from solutions with different amounts of AgTFA were studied, and the crystal structure of silver nanoparticles was also presented.     

In Situ Formation of a Novel Nanocomposite Structure Based on MCM-41 and Polyethylene

M41S materials are prepared by in situ assembly of inorganic precursors and organic template and can be viewed as nanocomposites of the siliceous phase and organic surfactant. Calcination of these precursors gives the M41S materials that have been used to prepare novel nanocomposite structures, in which the organic phase inside the nano-sized pores is isolated by the nano-sized inorganic pore walls. The nanocomposite structures can be formed by in situ polymerization of monomers inside the channels. Polymerization of ethylene takes place inside the nano-sized pores, producing the desired nanocomposite structure. The resulting polyethylene was found to be a mixture of crystalline and amorphous phases.