道路用聚氨酯改性沥青的制备工艺探讨

结合不同改性剂掺量单因素试验,确定了采用88mm叶轮、115mm容器、圆盘锯齿式搅拌器(转速1400r/min)、175℃共混温度、改性剂掺量4.27%、单次搅拌300g的制备工艺参数。在此条件下制备的聚氨酯改性沥青具有优异的水稳定性、储存稳定性且耐老化、耐高温,拥有比普通聚合物改性沥青更高的车辙因子G*/sinδ和15℃动态模量,基本满足高模量沥青要求。     

浅谈彩色沥青混凝土在路面工程中的使用

公路建设不断发展，对公路的要求越来越高。彩色沥青混凝土有多种特殊用途，被广泛应用和普及。本文就彩色沥青混凝土的应用进行了分析研究。     

Comparisons with high viscosity additive effects on base and modified asphalt

In this research, three types of high viscosity additives with different volumes were added to both 70# base asphalt and SBS modified asphalt, the dynamic viscosity and high temperature performance tests were conducted. The results show that with the same volume and type of the additive, SBS modified asphalt has a much higher dynamic viscosity and high temperature grade than those of the base asphalt. When the volume of each additive type increases from 0% to 12%, the dynamic viscosity would increase in a different trend, which could be described as three stages with different increasing speeds, and the variability and the demarcation point of the adjacent two stages depend on the asphalt modification, additive type and the volume. With regard to the high temperature grade, it was found that the effect of different additive types on high temperature performance should be separated from asphalt modification.     

脱硫胶粉在乳化改性沥青中的应用

考察了不同规格胶粉及不同脱硫程度的脱硫胶粉对橡胶改性乳化沥青性能的影响,结果表明,采用100目胶粉即可制备出橡胶改性乳化沥青,但乳化沥青的性能较差;采用活化度为50%左右的100目脱硫胶粉制备乳化沥青时,脱硫胶粉的用量相比于胶粉可大幅提高;在通过外掺100目50%左右活化度的脱硫胶粉(质量分数15%,以沥青计,下同)和质量分数2%的苯乙烯-丁二烯-苯乙烯嵌段共聚物改性的乳化沥青中添加质量分数1%的丁苯胶乳,所制备橡胶改性乳化沥青无筛上剩余物,5 d储存稳定性为2.9%,蒸发残留物的25℃针入度、软化点和5℃延度分别为55 (0.1 mm)、64.5℃和22.5 cm,能够满足乳化改性沥青的技术指标要求。     

贵州省干线公路沥青路面典型病害研究

"十二五"期间,随着贵州省交通建设的飞速发展,干线公路的里程及施工质量也迅速提高。但同时,干线公路沥青路面出现了许多早期病害,并且病害种类也更加多样化。本文对贵州省9个地市的干线公路沥青路面进行了系统调查,并就路面典型病害的成因进行了分析。     

30号硬质道路沥青组成结构对使用性能影响的机理研究

30号硬质道路沥青对提高路面高温稳定性能有显著效果,为探索影响沥青质量的内在因素,以溶剂脱沥青工艺制备的阿曼30号沥青和沙中30号沥青为研究对象,研究组成结构对使用性能的影响机理。结果表明,两种30号沥青均满足GB/T 15180—2010的要求,相比沙中30号沥青,阿曼30号沥青具有较好的高低温性能、抗老化性能和感温性能。组成结构研究表明,沥青的使用性能与其组成结构有着重大关联,不仅与组成存在比例关系,同时也与其内部结构紧密相关。相对于沙中30号沥青,阿曼30号沥青中各组分相对分子质量分布较宽,同时平均相对分子质量较高,各组分之间f_A,H/C,R_A/R_N,H_(AU)C_A等结构参数的差异性较小,胶体稳定指标I_c较高,主要组分芳香分、胶质和沥青质具有较长的侧链。高胶体稳定系数、较宽的相对分子质量分布、较小的组分结构差异性和具有长侧链等特点有利于形成稳定的胶体结构,进而使30号沥青体现出良好的高低温性能和抗老化性能。     

微波胶粉比表面积对橡胶沥青流变性能的影响

通过考察不同微波辐射时间对胶粉活化处理并制备胶粉改性沥青的效果,研究微波辐射对胶粉表观特性与其改性沥青流变性能的影响。采用气体吸附仪、动态剪切流变仪分别测定胶粉活化前后的比表面积及改性沥青的流变性能,并将胶粉的比表面积与沥青流变性能进行关联。在此基础上,结合扫描电镜,从微观角度揭示活化胶粉对沥青流变性能的影响机理。结果表明:在测定时间内,微波辐射使得胶粉表面变得蓬松,孔隙增多,比表面积增长显著;一定时间范围内(60～120s)的微波辐射对胶粉改性沥青的高温抗车辙能力有显著影响;胶粉微波活化后其比表面积与改性沥青流变性能之间有很好的相关性,胶粉比表面积越大,其复数剪切模量越大,相位角越小,沥青的高温抗变形能力越好。     

High-temperature performance and microstructure of composite modified hard asphalt

Composite modified hard asphalt (CMHA) was prepared by four-step high-speed shearing method adding crumb rubber, styrene-butadiene-styrene (SBS) copolymer, and hard asphalt to QHD AH-70 neat asphalt. The high-temperature performance and microstructure of CMHA were evaluated by rotational viscometer, fluorescence microscopy, and infrared spectroscopy, through which the modification mechanism was proposed. The results show that the shearing time had great influence on the high-temperature performance of CMHA. A significant variation in phase morphology of CMHA during preparation was observed. It is found that phase morphology was converted from a continuous asphalt phase with dispersed polymer phase to two twisted continuous phases, then to a continuous asphalt phase with dispersed polymer phase again. Preparation of CMHA was a complex physical and chemical process. A fraction of SBS took part in the chemical reaction and others were dispersed in net structure, which is beneficial for workability and performance of asphalt.     

Evaluation of polyphosphoric acid on the performance of polymer modified asphalt binders

The aim of this research is to evaluate the effect of polyphosphoric acid (PPA) on the mechanical performance of styrene–butadiene–styrene (SBS) and styrene–butadiene–rubber (SBR) modified asphalt. Conventional properties, multiple stress creep recovery (MSCR), bending beam rheometer (BBR), and linear amplitude sweep (LAS) tests were conducted to evaluate the performance characteristics of asphalt at different PPA inclusions. Gel-permeation chromatography (GPC), saturates, aromatics, resins, and asphaltenes (SARA), and Fourier transform infrared (FTIR) were carried to reveal the molecular weight, component and infrared spectra of asphalt. Results showed that PPA hardened the asphalt, improved the rutting and fatigue performances of polymer modified asphalt (PMA) binder, but weakened the anti-cracking performances. Besides, storage stability had a significant improvement as the addition of PPA. The addition of PPA brought more macromolecules into asphalt and led to more high-average molecular weight compounds. Furthermore, PPA changed four component ratios of asphalt. Both PMA with or without PPA have similar absorption peaks. This may be due to absorption peak of PMA covered the changes in PPA modification process as the low content of PPA. 0.8% dosage of PPA may be considered optimum for composite modified binder combining the above experimental results for this binder source.     

抗凝冰乳化沥青涂层的性能研究

为了研究自制融雪剂对抗凝冰乳化沥青涂层性能的影响,将自制固态型融雪剂按5%、10%、15%的比例加入乳化沥青制备涂层乳液,采用水煮法、摆式摩擦仪、电导率试验分别对涂层材料的粘附性、抗滑性能和抗凝冰性能进行了测试。结果表明:自制型融雪剂对乳化沥青与集料的粘附性影响不大;随着融雪剂掺配比例的增大,抗凝冰乳化沥青涂层的摩擦系数有所降低,但均满足规范要求;相比于普通沥青涂层,抗凝冰乳化沥青涂层的抗凝冰性能得到改善,且随着融雪剂掺配比例的增大,凝冰性能逐渐提高。