Inconel 690传热管GTAW对接焊接头组织及力学性能研究

对Inconel 690传热管材进行钨极气体保护焊(GTAW)对接焊,采用拉伸试验机、压扁试验机和光学显微镜测试和分析传热管焊接接头,同时利用ANSYS软件开展焊接接头在设计工况失压时的一次应力强度校核。研究结果表明:焊缝中心为树枝胞状晶,熔合线附近为粗大柱状晶。室温时接头的平均抗拉强度为619 MPa,平均屈服强度为292 MPa,350℃时接头平均抗拉强度为475 MPa,平均屈服强度为206 MPa,拉伸接头断裂从熔合区开始贯穿整个焊缝组织,呈塑性断裂。压扁试验和反向压扁试验结果表明管接头完好。通过ANSYS分析可知,设计工况下传热管接头350℃许用应力强度150 MPa限值可满足其一次应力强度要求,且裕量较大。     

致密砂岩油藏能量补充方式评价及优化

针对致密砂岩油藏大规模体积压裂开发后能量补充困难的问题,利用自主设计制作的大型人造三维岩心物理模型和物理模拟实验舱,开展致密砂岩油藏能量补充方式优化研究。实验结果表明:致密砂岩油藏压裂开发过程中,地层能量损耗严重,采取注水或注气的方式可有效进行能量补充;地层中裂缝规模越大,越有利于原油渗流,后续补充能量的传播范围越广,有助于进一步提高原油采收率;从提高驱油效率和扩大波及系数方面优选吞吐渗吸介质,CO₂均优于活性水,CO₂吞吐开发在矿场试验中取得了显著的增油效果,因此,CO₂吞吐作为一种有效的能量补充方式在致密油开发中展现了良好的应用前景。该文分析了致密砂岩储层水平井压裂开发的渗流规律,优选出致密砂岩储层大规模压裂开发后最佳渗吸介质,可为致密砂岩油藏开发设计提供重要的理论依据。     

煤峪口矿81010工作面煤层底板裂隙发育特征及防治

针对煤炭开采过程中出现的突水事故,采用RFPA数值模拟软件建立采动模型,对底板裂隙破断过程和声发射进行模拟,研究煤层底板采动裂隙扩展突水通道,结果表明:离断层越近,断层内水压导升高度越高,断层出现活化,裂隙扩展发育,最终贯通形成导水通道,在进行注浆改造后,单个钻孔的最大涌水量为8 m³/h,说明注浆加固防治水效果较好,能确保工作面的安全回采。     

Dense and core-rim structured B4C-TiB2 ceramics with Mo-Co-WC additive

B₄C-TiB₂ ceramics (TiB₂ ranging 5~70 vol%) with Mo-Co-WC as the sintering additive were prepared by spark plasma sintering. In comparison with B₄C-TiB₂ without additive, the enhanced densification was evident in the sintered specimen with Mo-Co-WC additive. Core-rim structured grain was observed around TiB₂ grains. The interface of the rim between TiB₂ and B₄C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B₄C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B₂ rim around the TiB₂ core may occur as a result of the solid solution and dissolution-precipitation between TiB₂ phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB₂ content increased, alongside the decreased hardness. B₄C-30 vol% TiB₂ specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m^1/2.     

Precipitous weakening of quartz at the α–β phase inversion

Crystalline quartz has long been identified as among the weakest of abundant crustal minerals. This weakness is particularly evident around the α–β phase inversion at 573°C, in which Si–O bonds undergo a displacive structural transformation from trigonal to hexagonal symmetry. Here we present data using indentation testing methodologies that highlight the precipitous extent of the transformational weakening. Although the indentations are localized over relatively small specimen contact areas, the data quantify the essential deformation and fracture properties of quartz in a predominantly (but not exclusively) compressive stress field, at temperatures and pressures pertinent to conditions in the earth's crust.     

Prediction of mode I fracture toughness of rock using linear multiple regression and gene expression programming

Prediction of mode I fracture toughness (K_IC) of rock is of significant importance in rock engineering analyses. In this study, linear multiple regression (LMR) and gene expression programming (GEP) methods were used to provide a reliable relationship to determine mode I fracture toughness of rock. The presented model was developed based on 60 datasets taken from the previous literature. To predict fracture parameters, three mechanical parameters of rock mass including uniaxial compressive strength (UCS), Brazilian tensile strength (BTS), and elastic modulus (E) have been selected as the input parameters. A cluster of data was collected and divided into two random groups of training and testing datasets. Then, different statistical linear and artificial intelligence based nonlinear analyses were conducted on the training data to provide a reliable prediction model of K_IC. These two predictive methods were then evaluated based on the testing data. To evaluate the efficiency of the proposed models for predicting the mode I fracture toughness of rock, various statistical indices including coefficient of determination (R²), root mean square error (RMSE), and mean absolute error (MAE) were utilized herein. In the case of testing datasets, the values of R², RMSE, and MAE for the GEP model were 0.87, 0.188, and 0.156, respectively, while they were 0.74, 0.473, and 0.223, respectively, for the LMR model. The results indicated that the selected GEP model delivered superior performance with a higher R² value and lower errors.     

Pressure-induced transparency of MgO,Al2O3, AlN,and cBN ceramics at room temperature

The in situ axial X-ray diffraction patterns of four ceramic powder samples (MgO, Al₂O₃, AlN, and cBN) that were compressed in a diamond anvil cell under uniaxial non-hydrostatic conditions were recorded. The microscopic deviatoric stress as a function of the pressure was determined from the X-ray diffraction peak broadening analysis: the curves increased approximately linearly with the pressure at the initial compression stage and then levelled off under further compression. Pressure-induced transparency was observed in all of the samples under compression, and the pressure at the turning point on the curves of the microscopic deviatoric stress versus pressure corresponded to the pressure at which the samples became transparent. Analysis of the microstructural features of the pressure-induced transparent samples indicated that the compression caused the grains to fracture, and the broken grains bonded with each other. We demonstrated that the ceramics’ pressure-induced transparency was a process during which the grains were squeezed and broken, the pores were close between the grains, and the broken grains were re-bonded under compression.     

Features of crystal structures and thermo-mechanical properties of weberites RE3NbO7 (RE=La,Nd, Sm,Eu, Gd) ceramics

The features of crystal structures, thermo-mechanical properties and their dominant mechanisms of weberites RE₃NbO₇ were studied as high-temperature oxides. We concentrated on connections between structures and thermo-mechanical properties, the influences of bond lengths, lattice distortion degrees and microstructures on these properties were estimated. The shortening of bond length and increment of bonding strength would lead to the increase of mechanical properties. The Vickers hardness (4.5-7.8 GPa) and toughness (0.5-1.6 MPa·m^1/2) of weberites RE₃NbO₇ are enhanced by grain refinement and increment of bond strength, while crystal structures, bond lengths, and lattice distortion degrees influenced their Young's modulus (100-170 GPa). Nano-indentation was applied to test the influence of microstructures on modulus and hardness. The dominant mechanisms for mechanical properties and thermal conductivity were proposed, which was conducive to properties tailoring and engineering applications of weberites RE₃NbO₇ oxides.     

超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性

针对100 mm超厚板TC4钛合金电子束焊接接头，采用慢应变速率拉伸方法评价接头在人造海水中的应力腐蚀敏感性，分析接头的显微组织和断口形貌，对接头的腐蚀机制进行研究. 结果表明，室温条件下应变速率为ε=1×10-6 s-1时，母材在海水中未表现出应力腐蚀敏感性；焊缝上部、中部和下部具有轻微应力腐蚀敏感性. 焊缝在海水中发生阳极溶解，产生氢吸附，导致裂纹的萌生. 同时氢扩散诱导α'相界及α'相内发生位错塞积，进而使裂纹在更低的应力水平下发生扩展.     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .