石膏转化制硫酸钾结晶动力学及结晶添加剂研究

研究了浓氨介质中石膏与氯化钾直接转化制硫酸钾的结晶动力学及结晶添加剂的作用效果。结果表明 ,硫酸钾在氨介质中的成核速率与晶体生长速率、悬浮密度、搅拌速率存在如下关联式 :B0 =5 .64 13×10 8G3.32 0 8Mt0 .0 559np0 .2 92 8。加入异丙醇、OP乳化剂及十二烷基苯磺酸钠等添加剂 ,可使硫酸钾结晶产品纯度提高 ,晶体形态整齐均匀     

Continuous precipitation of calcium sulfate dihydrate from waste sulfuric acid and lime

Precipitation of calcium sulfate dihydrate, gypsum, from (i) a pure sulfuric acid/lime suspension and (ii) a waste sulfuric acid/lime suspension in a continuous pilot plant in the temperature range from 40 °C to 80 °C was studied. It was observed that in the case of waste sulfuric acid with a high content of Mg²⁺ and Fe²⁺ ions, several hours after the beginning of the precipitation, partial dissolution of the product and modification of the crystals from needle‐ and plate‐like to agglomerated structures occurred. It is suggested that the secondary changes occur due to the increased concentration of Mg²⁺ and Fe²⁺ ions in the reactor. Below 60 °C, and above 70 °C plate‐like and needle‐like single crystals respectively were formed. The mean size (d₅₀) of the crystals was found to increase with increasing temperature and decrease with the initial concentration of lime. Gypsum produced between 70 °C and 80 °C is suitable for further processing for construction plaster. In a precipitation process with pure sulfuric acid only single perfect needle‐like crystals occurred. Copyright © 2005 Society of Chemical Industry     

亚硫酸钙氧化为石膏的研究

进行了亚硫酸钙氧化为二水石膏的研究 ,考察了初始 p H值、反应温度、空塔气速、固含量和停留时间对氧化率的影响 ,给出了适宜的反应条件 .在这些条件下 ,氧化率达 96 %以上     

石膏制品防水防潮剂的研制与开发

本文提出采用高分子有机材料配合，生产石膏制品防水防潮剂的生产方法和工艺。该剂还可以应用到氧化镁系列板材，同时提出开发珠光或彩色防水防潮剂，能达到满足的装饰效果，值提开发推广。     

高纯天然石膏水热法制备硫酸钙晶须研究

以高纯天然石膏为原料，加压水热法制备高品质硫酸钙晶须。采用常规分析方法、XRD和扫描电镜等手段分析和表征石膏原料和硫酸钙晶须产品。结果表明，制备硫酸钙晶须的最优条件为：料浆质量分数为6.0%，转晶剂氯化镁加入量为石膏质量的0.05%，硫酸加入量为水体积的1.0%，反应时间为4.0 h，快速过滤干燥即得硫酸钙晶须产品。分析结果表明：硫酸钙晶须长度最大为280.4 μm，最小为19.59 μm，平均长度为80 μm；硫酸钙晶须直径最大为5.86 μm，最小为0.20 μm，平均直径为2.67 μm；通过统计分析可知，长径比范围为10～80。     

3000m~3/h排烟循环流化床脱硫工艺中试实验研究

介绍了采用真实烟气的 30 0 0m3 /h排烟循环流化床烟气脱硫工艺 (CFB FGD)及其中间试验装置 ,通过实验研究了钙硫摩尔比 (Ca/S)、近绝热饱和温度差 (ΔT)、烟气湿度、喷水量、入口SO2 浓度、浆液雾化质量、脱硫灰循环等对脱硫效果的影响。实验表明 ,CFB FGD工艺在停留时间小于 6s、烟气流速v =4— 6m/s、Ca/S =1.2、ΔT =10— 12℃时可实现高达 90 %的脱硫效率。     

钴钼系耐硫变换催化剂硫化与水解问题探讨

钴钼系耐硫变换催化剂硫化与水解问题一直受到人们的关注。许多研究人员对硫化水解做了大量的报道，但都以热力学平衡为基础，计算出的结果存在理论和实际相背离。因此，作者想从化学平衡和动力学双重角度对硫化与水解问题做一探讨。     

Hydration Study of the System Ca3Al2O6–CaSO4· 2H2O–Ca(OH)2–H2O with and without Citric Acid

Hydration occurring in the system Ca₃Al₂O₆–CaSO₄· 2H₂O–Ca(OH)₂–H₂O has been studied at different temperatures and it was found that the reactions are diffusion controlled. The kinetic data obeyed Jander's equation and the rate of reaction increased with increasing temperature. X-ray diffraction studies and calorimetric measurements show that when gypsum is consumed, ettringite is converted into monosulfate. The rate of this conversion also increased with the increasing temperature and decreased in the presence of citric acid. Spectroscopic studies showed that there was some interaction between citric acid and the cement and that the product of hydration is of colloidal nature. Zeta potential measurements show that retardation of Ca₃Al₂O₆ hydration in the presence of gypsum and Ca(OH)₂ is not due to SO²⁻₄ adsorption. Electrical conductivity and thermoelectric potential measurements of solid Ca₃Al₂O₆ show that Ca₃Al₂O₆ is an n -type semiconductor and contains defects. The retardation of Ca₃Al₂O₆ may be due to poisoning of reaction sites by gypsum and Ca(OH)_2.     

钛石膏作水泥缓凝剂的试验研究

试验了钛石膏中亚铁含量对水泥性能的影响，并检测了用处理后的钛石膏作缓凝剂的水泥物理性能及所配混凝土的收缩值，结果表明，掺钛石膏的水泥与掺天然石膏的水泥标准稠度用水量、凝结时间基本一致；钛石膏的掺量达4％～7％时，水泥的各龄期强度均比掺天然石膏的高；所配混凝土的收缩值基本相同。并进行了大磨中试，表明处理后的钛石膏完全可以代替天然石膏作水泥缓凝剂。     

利用工业废石膏作水泥缓凝剂的技术研究

介绍了利用生产混凝土外加剂时排放的工业废石膏作为水泥缓凝剂的研究。研究结果表明,废石膏作为水泥缓凝剂单独使用时虽然可能会影响水泥的凝结时间和强度,但如果与天然石膏搭配使用,并控制适当的SO3掺量,就可以在原有生产工艺参数基本不变的条件下,生产出合格的水泥,而且可以配制出符合建筑工程要求的高性能混凝土。