In flotation, metal ions possess significant roles that are usually fulfilled by either selectively activating or depressing the target minerals. Despite that tremendous efforts have been made to address the roles of metal ions in flotation, it still lacks a comprehensive review, especially to compare various ions instead of focusing on a specific one. This review begins by elaborately categorizing the factors involved in affecting the roles of metal ions in flotation. After that, well-accepted mechanisms are updated and discussed from the ore type. Furthermore, typical approaches to explore the underlying mechanisms are emphasized, including traditional techniques such as micro-flotation, contact angle measurement, zeta potential measurement, and other recent prevailing methodologies, like computational method, solution chemistry calculation, and cyclic voltammetry. This work will pave the way to promote flotations via activities like selectively adding/reducing metal ions, choosing reagents, and regulating the slurry chemistry. 相似文献
Metal organic frameworks (MOFs) containing zirconium secondary building units (SBUs) in UiO-67 and related MOFs, are highly active for neutralizing both the chemical warfare agents and simulants, such as dimethyl methylphosphonate (DMMP). However, two recent publications gave conflicting reports of DMMP reaction with UiO-67 under ultra high vacuum (UHV) conditions, with one reporting chemisorption and reaction (Wang et al., J Phys Chem C, 2017, 121, 11261–11272) and the other reporting only physisorption and reversible desorption (Ruffley et al., J Phys Chem C, 2019, 123, 19748–19758) from very similar temperature programmed desorption experiments. We show that the discrepancy between these experiments may be explained by different levels of missing linker defects in the UiO-67 samples. We present density functional theory calculations showing that SBU sites having two-adjacent missing linkers exhibit reaction barriers that are about 30 kJ/mol lower than SBU sites having a single missing linker. We also show that topology of the undercoordinated sites plays an important role in the reaction barrier under UHV conditions. 相似文献
During sintering of the silica-based ceramic core of turbine blades, a phenomenon called “nonuniform sintering” occurs that negatively affects the thermal and mechanical properties of the core. Standard samples of silica-based core were prepared by an injection molding method and sintered with alumina backfilling powder with different sodium contents. The effect of sodium content on the nonuniform sintering of silica-based cores and the thermal and mechanical properties was evaluated. Results show that the sintering level and the content of α-cristobalite in the surface layer are significantly higher than that of the sample interior. A considerable number of microcracks are found in the surface layer due to the β to α-phase transition of cristobalite. As the sodium content in the alumina powder decreases, the level of the nonuniform sintering and the amount of crystallized cristobalite in the surface layer decrease, which is beneficial to the thermal expansion and flexural strength at ambient temperature. The flexural strength and thermal deformation at high temperature are improved by reducing the surface cracks, but deteriorated with the decrease of the cristobalite crystallization when the surface cracks are macroscopically invisible.