Evaluation of the Properties of Si3N4/Si3N4 Joint Brazed Using a Filler Alloy Containing Pd

Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the jointwere measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the SisN4/SisN4 joints were obtained bybrazing at 1373～1473 K f     

Mechanical spectroscopy in commercial Fe–6 wt.% Si alloys between 400 and 1000 K

Mechanical spectroscopy, neutron diffraction and differential scanning calorimetry (DSC) were performed on commercial Fe–6 wt.% Si alloy after quenching from high temperature. The damping spectrum shows a peak at around 800 K and an associated modulus defect. The modulus shows an increase during the second and subsequent heating runs. In addition, an anomaly in the modulus behavior has been found at around 400 K. Different thermal treatments allows to obtain two different recovery degrees of the quenched-in defects. The influence of the recovery degree on the 800 K internal friction peak and on the anelastic modulus has been evaluated and confirm the validity of the grain boundary mechanism associated to this peak. Experimental results are discussed on the basis of recovery and ordering processes.     

Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

LD钢超塑性压缩变形参数与金相组织

通过对ＬＤ（７Ｃｒ７Ｍｏ３Ｖ２Ｓｉ）模具钢起塑性压缩变形后的金相组织观察研究，分析了变形参数、原始组织对变形后金相组织的影响。     

ZnGa2O4纳米晶的制备和结构表征

采用喷射共沉淀法制备了ZnGa2O4 纳米晶，XRD、SEM和TEM结构分析结果表明，喷射共沉淀法制备的ZnGa2O4的纳米晶颗粒细小均匀，形状完整，与化学共沉淀法相比，粒子尺寸明显减小，小于10nm，同时ZnO杂相峰消失，分析了喷射共沉淀法的机理，并对实验结果进行了解释。     

Effects of Y and Ce on Microstructures and Properties of Nb-Si System Composites

The effects of yttrium and cerium on microstructures and properties of Nb-Si system composites were investigated by scanning electron microscopy( SEM), energy dispersive spectrum(EDS), X-ray diffraction(XRD) and high temperature oxidation experiments.It is found that the coarse primary silicide phase became finer and more homogeneous with Y and Ce addition.The results of high temperature oxidation experiments show that the oxidation rates of NbSi system composites with an appropriate amount of Y and Ce decrease compared with those of alloys without Y or Ce addition, and oxidation products mainly distribute along the phase boundaries between the Nb solid solution and silicide.     

注氢硅中微结构缺陷的TEM观察

通过透射电子显微镜观察到注氢硅片中存在损伤带，损伤带的位置和注人氢的分布几乎一致，推断损伤带是由于氢的注入引起的。损伤带内主要以平行于正表面的{111}面状缺陷为主，另外还有斜交于正表面的{111}面状缺陷以及{100}面状缺陷，这是由于氢朝能量低的位置的迁移聚集而形成的。在损伤带的中间还可见到晶格紊乱团块和空洞，这是由于损伤带中间存在高浓度的氢和高密度的面状缺陷面导致形成的。     

Effect of Y2O3, CeO2 on Sintering Properties of Si3N4 Ceramics

The effect of rare earth oxides Y203 or Ce02 on sintering properties of Si3N4 ceramics was studied and the mechanism of assisting action during sintering was analyzed. The results in dicate that the best sintering properties appear in Si3N4 ceramics with 5% Y203 or 8% CeO2. Secondary crystallites are formed at grain boundaries after heat treatment,which decreases the amount of glass phase and contributes to the improvement of high-temperature mechanical properties of silicon nitride.     

薄Si膜对基底表面粗糙度的影响

利用ＺＹＧＯ光学干涉测量仪，散射积分测量法观测了光学元件表面均方根粗糙度．详细分析了薄Ｓｉ膜对基底均方根粗糙度的影响，由此认为薄膜并不总是复制基底表面的粗糙度，结果出现了薄膜降低表面粗糙度的现象．提出了一定厚度范围的薄Ｓｉ膜的表面粗糙度存在着一个稳定值的新设想．     

Preparation and Properties of Sintering Additives Coated Si3N4 from Heterogeneous Nucleation Processing

The sintering additives such as Al2O3 and /or Y2O3 were coated on the surfaces of Si3N4 particles via heterogeneous nucleation processing using a buffered pH solution as the precipitation reagent .They nucleated and grew only on the surfaces of Si3N4 and did not form sol particles in solution by TEM observation .The isoelectric point(IEP) of coated Si3N4 was different from that of as-received Si3N4.The IEP of Al(OH)3-coated Si3N4 occurred at pH8.4, which is close to that of alumina .When Al(OH)3-coated Si3N4 particles were coated with Y(OH)3,the IEP of coated Si3N4 powder shifted from pH8.4 to pH9.2 ,similar to that of yttria.In addition ,the rheological data showed that Al2O3 and /or Y2O3 coated Si3N4 suspension is nearly Newtonian and that added Si3N4 suspension shows a shear rate thinning behavior.