Inconel 690传热管GTAW对接焊接头组织及力学性能研究

对Inconel 690传热管材进行钨极气体保护焊(GTAW)对接焊,采用拉伸试验机、压扁试验机和光学显微镜测试和分析传热管焊接接头,同时利用ANSYS软件开展焊接接头在设计工况失压时的一次应力强度校核。研究结果表明:焊缝中心为树枝胞状晶,熔合线附近为粗大柱状晶。室温时接头的平均抗拉强度为619 MPa,平均屈服强度为292 MPa,350℃时接头平均抗拉强度为475 MPa,平均屈服强度为206 MPa,拉伸接头断裂从熔合区开始贯穿整个焊缝组织,呈塑性断裂。压扁试验和反向压扁试验结果表明管接头完好。通过ANSYS分析可知,设计工况下传热管接头350℃许用应力强度150 MPa限值可满足其一次应力强度要求,且裕量较大。     

Evaluation of a sulfidogenic system fed with microalgal biomass of Chlorella pyrenoidosa as an electron donor: Sulfate reduction kinetics

In this study, a sulfidogenic reactor fed with microalgal biomass of Chlorella pyrenoidosa as an electron donor was operated in a continuous mode. This study evaluated the influence of various initial sulfate concentration from 1.0 to 2.5 g/L on anaerobic sulfate reduction kinetics by a sulfidogenic enrichment culture predominantly Desulfovibrio sp. VSV2. It was observed that volumetric sulfate reduction rate (VSRR) was consistently increasing with an increase in volumetric sulfate loading rate (VSLR) across the retention time of 7–10 days. For a retention time of 7 days, the maximum VSRR was noted as 0.0050 g/(L.h) with a corresponding VSLR of 0.0089 g/(L.h). When retention time was maintained for 10 days, a maximum sulfate reduction of 65% and a maximum bacterial concentration of 1.632 g/L were achieved for an initial sulfate concentration of 1.5 g/L. It was concluded that VSLR facilitated through both dilution rate and initial sulfate concentration had a significant influence over sulfate reduction kinetics. The results of the study suggested that the microalgal-fed sulfidogenic system could be effectively employed for reduction of sulfate from sulfate-rich wastewater.     

Syndecan-1 (CD138), Carcinomas and EMT

Cell surface proteoglycans are known to be important regulators of many aspects of cell behavior. The principal family of transmembrane proteoglycans is the syndecans, of which there are four in mammals. Syndecan-1 is mostly restricted to epithelia, and bears heparan sulfate chains that are capable of interacting with a large array of polypeptides, including extracellular matrix components and potent mediators of proliferation, adhesion and migration. For this reason, it has been studied extensively with respect to carcinomas and tumor progression. Frequently, but not always, syndecan-1 levels decrease as tumor grade, stage and invasiveness and dedifferentiation increase. This parallels experiments that show depletion of syndecan-1 can be accompanied by loss of cadherin-mediated adhesion. However, in some tumors, levels of syndecan-1 increase, but the characterization of its distribution is relevant. There can be loss of membrane staining, but acquisition of cytoplasmic and/or nuclear staining that is abnormal. Moreover, the appearance of syndecan-1 in the tumor stroma, either associated with its cellular component or the collagenous matrix, is nearly always a sign of poor prognosis. Given its relevance to myeloma progression, syndecan-1-directed antibody—toxin conjugates are being tested in clinical and preclinical trials, and may have future relevance to some carcinomas.     

Microscopic Methods for Identification of Sulfate-Reducing Bacteria from Various Habitats

This paper is devoted to microscopic methods for the identification of sulfate-reducing bacteria (SRB). In this context, it describes various habitats, morphology and techniques used for the detection and identification of this very heterogeneous group of anaerobic microorganisms. SRB are present in almost every habitat on Earth, including freshwater and marine water, soils, sediments or animals. In the oil, water and gas industries, they can cause considerable economic losses due to their hydrogen sulfide production; in periodontal lesions and the colon of humans, they can cause health complications. Although the role of these bacteria in inflammatory bowel diseases is not entirely known yet, their presence is increased in patients and produced hydrogen sulfide has a cytotoxic effect. For these reasons, methods for the detection of these microorganisms were described. Apart from selected molecular techniques, including metagenomics, fluorescence microscopy was one of the applied methods. Especially fluorescence in situ hybridization (FISH) in various modifications was described. This method enables visual identification of SRB, determining their abundance and spatial distribution in environmental biofilms and gut samples.     

Controlled galvanic decoration boosting catalysis: Enhanced glycerol electro-oxidation at Cu/Ni modified macroporous films

We report on glycerol electro-oxidation in alkaline medium at macroporous Ni electrodes decorated with Cu particles. Macroporous Ni film is electrodeposited, using hydrogen bubbles as dynamic templates, atop of a Cu substrate. This film shows good electrocatalytic activity towards glycerol oxidation reaction (GOR). The Ni film is further decorated with Cu via spontaneous deposition from CuSO₄ solution. This is done to enhance the catalytic activity of the film towards GOR. The morphology of the Cu-decorated Ni film is controlled using various additives such as KCl and (NH₄)₂SO₄ which are added to the Cu deposition bath. The as-prepared Cu-decorated Ni films are characterized by electrochemical measurements, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). It is found that these additives have tremendous effects on the morphology and the electrocatalytic activity of the decorating Cu particles.The decorated Ni foam showed superior electrocatalytic activity towards the GOR, as confirmed by the negative shift in the onset oxidation potential (ca. 100 mV) together with an increase in oxidation current that is up to 1.5-fold during the cyclic voltammetry (CV) measurements, compared to the undecorated Ni foam.     

A new solid‐state mode of hot corrosion at temperatures below 700°C

Preliminary results on a single‐crystal nickel‐based superalloy indicated that hot corrosion can occur at temperatures as low as 550°C, where liquid formation, generally believed to be responsible for Type II hot corrosion, is not predicted. Additional tests were conducted on pure‐nickel samples at 650°C and below to more clearly elucidate the mechanism of this very low‐temperature hot corrosion. Environments in dry air and O₂‐(2.5, 10, 100, and 1000) ppm SO₂ were studied. Based on the results obtained, a solid‐state corrosion mechanism was inferred. The mechanism relies on the formation of a previously unreported compound phase, which was identified using transmission electron microscope analysis that indicated the stoichiometry of Na₂Ni₂SO₅. Furthermore, it was nanocrystalline in structure and metastable. It was deduced that the Na₂Ni₂SO₅ formation was responsible for the rapid nickel transport required for the observed accelerated corrosion process. Moreover, its eventual decomposition resulted in a mixed product of porous NiO with embedded particles of Na₂SO₄. Application of the proposed mechanism to nickel‐based alloys is discussed.     

电感耦合等离子体原子发射光谱法测定辛酸铑催化剂中铂钯铅铁铜铝镍

准确测定辛酸铑催化剂中杂质元素含量,是判定产品是否合格的重要指标之一。以往常采用直流电弧发射光谱法(摄谱法)进行检测,但测定周期长,且重复性较差。用电感耦合等离子体原子发射光谱法(ICP-AES)测定辛酸铑催化剂中微量杂质元素时,辛酸铑催化剂样品中含有的大量有机组分和铑基体会对测定有严重干扰。实验采用反复滴加硝酸消解样品中有机组分,再用王水溶解盐类,选用合适背景点扣除的方式消除铑基体的干扰,建立了使用ICP-AES测定辛酸铑催化剂中0.001%~0.1%(质量分数)Pt、Pd、Pb、Fe、Cu、Al、Ni等7种微量杂质元素的方法。各元素在0.10~10.00μg/mL范围内与其发射强度呈线性关系,相关系数均大于0.9999;方法检出限(μg/mL)为0.075(Pt)、0.0033(Pd)、0.015(Pb)、0.0036(Fe)、0.010(Cu)、0.001(Al)、0.012(Ni)。实验方法用于测定辛酸铑催化剂样品中Pt、Pd、Pb、Fe、Cu、Al、Ni,结果的相对标准偏差为(RSD,n=7)为1.4%~9.6%。按照实验方法测定辛酸铑催化剂中Pt、Pd、Pb、Fe、Cu、Al、Ni,并与直流电弧发射光谱法的测定结果进行比对,结果相一致。     

氟橡胶包覆硝酸肼镍及其对雷管撞击感度的影响

利用水悬浮法将氟橡胶包覆在硝酸肼镍(NHN)表面制备出了NHN造型粉,并将其应用于基础雷管。通过DSC研究了NHN造型粉的热性能，测试了NHN造型粉的机械感度和火焰感度以及工业基础雷管的撞击感度和起爆能力。研究结果表明:氟橡胶包覆能够提高NHN的热稳定性，且热稳定性随着氟橡胶包覆量的增加而提高；NHN造型粉的机械感度均低于原料NHN，当氟橡胶包覆量（质量分数）为9%时，撞击感度下降幅度明显，可达142.9%；NHN造型粉用在基础雷管中做起爆药，可以降低基础雷管的撞击感度并保持其起爆能力。     

Metal sulfate decomposition using green Pd-based catalysts supported on γAl2O3 and SiC: A common step in sulfur-family thermochemical cycles

Thermochemical water splitting cycles (TWSCs) are processes with the potential for large-scale production of carbon-free hydrogen. Among these, the sulfur-family thermochemical cycles are considered the most promising due to both, the use of readily affordable chemical reagents and the temperature required to thermally decompose oxygenated sulfur compounds, which is achievable by solar means. Indeed, solar heat assisted metal sulfate decomposition is a key step, where catalysis can be employed to reduce decomposition temperature. Here we present a green route to synthesize Ag-Pd and Fe-Pd intermetallic alloy catalysts supported over γ-Al₂O₃ and Si-C by a microwave-assisted method using glycerol both as a solvent and as a reducing and stabilizing agent. The obtained supported catalysts were physicochemically characterized. Fe-Pd/Al₂O₃ catalyst exhibited the best performance, abating the zinc sulfate decomposition temperature by ca. 85 °C in comparison with other reported catalysts.     

Development of microbially influenced corrosion on carbon steel in a simulated water injection system

Microbially influenced corrosion (MIC) on internal pipeline surfaces has become a severe problem during the water injection process in secondary oil recovery. The formation of a biofilm, normally dominated by sulfate‐reducing bacteria (SRB), is believed to be the critical step of the MIC process. A continuously fed biofilm simulating the water injection process was operated to investigate the influence of biofilm development on MIC behavior in the early phase of corrosion development. The development of the corrosion product film and biofilm was monitored for 5 months with electrochemical impedance spectroscopy, linear polarization resistance, scanning electron microscopy, 3D optical profiling, and direct weight measurement. MIC development was found to comprise three phases: initialization, transition, and stabilization. The initialization phase involved the formation of the corrosion product layer and the initial attachment of the sessile microbes on metal surface. In the transition phase, the MIC process gradually shifted from charge‐transfer‐controlled reaction to diffusion‐controlled reaction. The stabilization phase featured mature and compact biofilm on the metal surface, and the general corrosion rate (CR) decreased due to the diffusional effect, while the pitting CR was enhanced at a lower carbon source level, which supported the mechanism of direct electron uptake from the metal surface by SRB.