Accelerating the decarbonization of carbonaceous gold ore by suspension oxidation roasting towards the improvement of gold leaching efficiency

Eliminating the gold preg-robbing effect of carbonaceous matter in carbonaceous gold ores is crucial for gold leaching. In this study, suspension oxidation roasting was proposed to accelerate the decarbonization of carbonaceous gold ore. The characteristics of oxidation reaction process and gas release were analyzed by TG-DTA-FTIR. The phase transformation and microstructure evolution of samples during roasting were analyzed by XRD, SEM and BET. The results show that the gold preg-robbing effect was eliminated after the gasification of carbonaceous matter, and the CaO generated by decomposition of carbonates can effectively capture the SO₂. After roasting for 75 min at 650 °C in a 20% O₂ atmosphere, the total carbon removal rate reached 99.42%, the distribution of exposed gold increased from 28.85% to 77.10% and the gold leaching efficiency increased from 4.55% to 84.83%. In addition, about 70% sulfur was mainly fixed in the roasted products in the form of sulfate. Therefore, the suspension oxidation roasting process is an efficient and clean pretreatment method for carbonaceous gold ores.     

井下硐室大爆破实践

酒钢镜铁山矿运用硐室大爆破处理山头岩体，以便为２号（中）矿体的开采形成良好的覆盖层。由于爆破设计合理，工程质量较好，达到了预期的目的。     

Ceramics composites from iron ore tailings and blast furnace slag

The search for materials and methods capable of reducing human impacts on the environment is of utmost importance nowadays. This study's primary purpose was to analyze the technical feasibility of ceramic composites production utilizing Fundão Dam's Iron Ore Tailings (IOT), Blast Furnace Slag (BFS) from charcoal, and Foundry Sand (FS) as partial substitutes for the traditional raw materials – sand and clay – for application in building industry materials. The composites were molded in rectangular specimens and fired at temperatures of 900, 950, 1000, 1050, and 1200 °C. The developed materials were analyzed and characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), Thermogravimetry (TGA), and Differential Thermal Analysis (DTA). The obtained materials had flexural strength modulus of up to 12.19 MPa, water absorption ranging from 2 to 22%, linear shrinkage ranging from 0.02 to 6.50%, and apparent density ranging from 2.03 to 1.63 g/cm³. The study of the internal structure formation process revealed the formation of amorphous structures in the composites. The results demonstrated that these waste materials may be jointly used in construction materials, contributing to the reduction of natural resource extraction, besides enabling their correct disposal, minimizing environmental impacts, and improving the life quality of the surrounding communities.     

S/Se dual-doping promotes the formation of active Ni/Fe oxyhydroxide for oxygen evolution reaction of (sea)water splitting

Surface reconstruction produces metal oxyhydroxide (1OOH) active sites, and promoting surface reconstruction is essential for the design of OER electrocatalysts. In this paper, we reported that a large amount of active NiFeOOH was generated in-situ on the surface of nickel-iron sulfide selenide, thus exposing more active sites and efficiently catalyzing OER. In 1 M KOH solution, NiFeOOH(S,Se) achieves an ultra-low overpotential of 195 mV at the current density of 10 mA cm^?2, and the Tafel slope is only 31.99 mV dec^?1, showing excellent catalytic performance. When the current density is 100  mA cm^?2, the over-potential of NiFeOOH(S,Se) in KOH + seawater solution is 239 mV, which is almost equivalent to 231 mV in KOH solution. The excellent OER stability of the NiFeOOH(S,Se) catalyst in alkaline electrolytes was confirmed, and the overpotential did not change significantly after 4 days of testing in KOH + seawater solution.     

Wavelength-dependent photoactivity of ZnxCd1−xS and ZnCo2O4/ZnxCd1−xS for H2 and H2O2 production

Zinc cadmium sulfide (Zn_xCd_1?xS) is a good photocatalyst for hydrogen evolution reaction (HER), but an optimum x (x_m) at which a maximum HER rate is reached varies from one report to another. In this work, we examine the effect of light wavelength, not only for the HER to H₂ in the presence of Na₂S and Na₂SO₃, but also for oxygen reduction reaction (ORR) without addition of any sacrifices. For the HER under a 365 and 420 nm LED lamp, the x_m were 0.9 and 0.7, respectively. For the HER under a 330 and 395–515 nm cut-off xenon lamp, the x_m were 0.7 and 0.5, respectively. For the ORR under a 420 nm cut-off halogen lamp, a maximum production of H₂O₂ was observed at x = 0.3. Furthermore, after 4% ZnCo₂O₄ loading, Zn_xCd_1?xS had an increased activity and stability, either for the HER or for the ORR. Through a (photo)electrochemical measurement, it is proposed that the photocatalytic activity of Zn_xCd_1?xS is determined by its light absorptivity and electron reactivity. The improved performance of n-type Zn_xCd_1?xS by p-type ZnCo₂O₄ is due to formation of a p-n junction, promoting the HER (ORR) on Zn_xCd_1?xS, and the sulfide (water) oxidation on ZnCo₂O₄. This work highlights that Zn_xCd_1-xS is a promising photocatalyst for H₂ and H₂O₂ production, respectively.     

Degradation mechanism of high alumina refractory bricks by reaction with deposits in a rotary kiln for fluxed iron ore pellets production

The formed deposits wear out of refractory wall linings in the rotary kiln and may cause production disturbances. This study describes the chemical composition and mineralogical phase components at the deposit/refractory interface in the rotary kiln for fluxed iron ore pellets production. The main phases of refractory bricks are corundum and mullite, while the deposits mainly contain hematite and silicates. The main phases in the deposit/refractory brick contact zone are hematite, anorthite (CaAl₂Si₂O₈), mullite, corundum, and silicates. Moreover, the hematite phases in the deposit/brick interface averagely contain 6.98 wt% Al and 1.38 wt% Ti. The silicates in the contact zone contain higher aluminium content and lower iron content than the silicates in the deposits. Finally, the thermodynamic analysis indicates that the main phases in the deposits can react with the refractory to form Al₂Fe₂O₆, CaAl₂Si₂O₈, feldspar, and liquid phases lead to the degradation of bricks in the kiln during the iron ore pellets production.     

四川某低品位金矿非氰浸出试验研究

对金品位为1.55 g/t的氧化矿采用非氰药剂进行浸金的工艺流程,考察了磨矿细度、药剂DZC浓度和浸出时间对金浸出率的影响。确定该金矿适宜的非氰浸出条件:磨矿细度-74μm含量占69.90%、石灰用量4 000g/t、矿浆液固比为2∶1、浸出药剂DZC浓度0.08%、浸出时间8 h,可获得金的浸出率为93.33%的良好指标。表明该氧化金矿在常温常压下,采用非氰浸出工艺是可行的。     

内蒙古某银铅锌矿选矿试验研究

对内蒙古含银铅锌矿石进行了浮选分离工艺研究。在查明矿石的主要矿物组成及嵌布特征的基础上,依据矿石特性采用铜铅混选-锌浮选的工艺流程进行选矿试验,从含银310.92g/t、铅6.10%、锌4.95%的矿石中获得含铅76.63%、含银3 659.74g/t、铅回收率为91.50%、银回收率为87.11%的铅精矿和含锌55.48%、含银282.84g/t、锌回收率为89.15%、银回收率为7.34%的锌精矿。实现了矿石中银、铅、锌的综合回收。     

安徽省铜陵市铁山头铜矿床地质特征及找矿潜力

铁山头铜矿床处于铜陵矿集区的中东部，属于扬子陆块下扬子凹陷中的铜陵隆起。矿床位于凤凰山矿田北侧，成矿潜力较大。综合研究分析认为：①接触交代作用使得岩体接触带及附近变质形成矽卡岩矿化带；②区内凤凰山岩体（花岗闪长岩）系成矿母岩；③矿体主要赋存于花岗闪长岩与三叠系下统南陵湖组石灰岩接触带上；④矿床成因类型为高—中温热液交代矽卡岩型矿床。