尖锐端头碳纳米管的制备与场发射特性

采用氢电弧法制备了尖锐端头的碳纳米管,获得了具有三种特殊形貌的尖端,即锥形、颈缩形和铅笔状尖端.该特殊彤貌的彤成可归因于在原料中加入硅粉进而形成的结构缺陷.研究了所得碳纳米管的场发射特性,发现其阈值电场较低,仅为3.75V/mm;场发射电流密度可高达～1.6×105A/cm2;且场发射稳定性好.以上优异的场发射性能归结于该碳纳米管具有良好的结构完整性和独特的尖端结构特征.

Abstract：

Carbon nanotubes (CNTs)with sharp tips were synthesized by a hydrogen arc discharge method. Three unusual morphologies,i.e. ,a cone-shaped tip,a suddenly-shrinking tip,and a pencil point-like tip were observed. These novel tip structures are considered to be related to the addition of a small amount of silicon powder in the raw material,which may introduce structural defects in the CNTs. The field emission properly of the sharp-tip CNTs was investigated,and a low threshold electric field of 3.75 V/m,a high field emission current density of ～1.6× 105 A/cm2,and a good emission stability were demonstrated. The superior field emission performance of the CNTs can be attributed to their good crystallinity and unique tip structures.     

RFID系统防碰撞协议研究设计与优化

碰撞问题是影响射频识别(RFID)系统读取效率的关键问题。该文提出了两种新的防碰撞协议CDCA协议和CDCA-2D协议,并且对两种协议进行了详细的理论分析和优化。新协议将RFID系统的读取过程分为两个阶段,利用第1阶段的碰撞检测信息实现在第2个阶段的无碰撞通信。仿真结果表明,和目前国际上流行的RFID防碰撞算法相比,两种新协议极大地提高了读取的效率。     

研磨碳酸钙涂层材料的渗吸特性与分析研究

针对研磨碳酸钙(GCC)纸张涂层材料的渗吸特性及经典的Lucas-Washburn(LW)渗吸模型,对材料的渗吸特性进行了实验测试,揭示了材料的渗吸性能。结果表明,涂层材料渗吸量与渗吸的根时间(t)服从线性关系,但是出现了实验渗吸分区现象(即渗吸被分为两个阶段),与经典的LW渗吸机制相矛盾,因此经典的LW渗吸在解释涂层材料渗吸时仍存在一定的缺陷。基于渗吸实验的分区现象,考虑材料粗糙表面的润湿行为及液膜平滑效应,对实验渗吸现象进行了科学的解释,探究并分析了形成渗吸分区的本质原因。因此在开发具有特定渗吸特性的涂层材料时,材料本身的粗糙表面或孔墙的粗糙度应是重点关注的因素之一。