Fe-based bulk metallic glasses (BMGs) with high boron content have potential application as a coating material used in the framework for storing spent nuclear fuels to support their safe long-term disposal. The high glass forming ability (GFA) and large supercooled liquid region are therefore required for such Fe-based BMGs in either the glassy powder fabrication or the subsequent coating spraying. In order to meet these requirements, the influence of Nb content on the GFA of Fe57Cr10Zr8B18Mo7−xNbx (x=1–5, at.%) alloys was investigated, as Nb has positive roles in GFA and thermal stability of BMGs. The results indicate that a fully amorphous phase in the as-cast samples with 3 mm in diameter is obtained for both the Fe57Cr10Zr8B18Mo5Nb2 and Fe57Cr10Zr8B18Mo4Nb3 alloys. The corresponding supercooled liquid regions of the two BMGs are 78 K and 71 K, respectively. The mechanism for improving their GFA was analyzed based on the principle of metal solidification, the parameters for glass formation and thermal properties of the alloys. The compression strength and Vicker’s hardness of the two BMGs are 1,950 MPa and 1,310 HV, 2,062 MPa and 1,180 HV, respectively. The developed BMGs with high B content, good GFA, and very high hardness can be used as coating materials to the framework for spent nuclear fuels.
The formation of micro-cracks in Ni-rich LiNi0.8Co0.1Mn0.1O2 (NCM811) cathode particles is an extremely important factor affecting the electrochemical characteristics after long-term cycling. Generally, cracks can be divided into intergranular crack and intracrystalline crack according to their positions. Coating has been confirmed as a highly effective strategy to relieve intergranular cracks. However, the intracrystalline cracks of primary-like particles have rarely been studied. In this work, ethoxy functional polysiloxane (EPS) was directly coated on the surface of original NCM811 by tetraethyl orthosilicate (TEOS) hydrolytic polycondensation method without any additives. Then, the microstructure, micromorphology, surface state and electrochemical properties were investigated in detail by XRD, SEM, TEM, CV and EIS. The results displayed that the micro-cracks of primary-like particles were effectively suppressed under appropriate EPS coating. Accordingly, excellent capacity retention of 95.6% (100 cycles, 1C) and rate performance (144.6 mA h/g, 5C) were obtained. These improved mechanical and electrochemical properties are considered to be related to the EPS stress buffer layer, suppressed oxygen vacancies, inhibited phase transition and reduced volume change. 相似文献
Transparent terbium aluminum garnet (TAG) ceramics were achieved by the vacuum sintering plus HIP post-treating from the coprecipitated TAG nanoparticles. The influences of vacuum sintering temperature and sintering aid TEOS on the optical quality of the TAG ceramics were studied. The results show that with the increase of sintering temperature, the optical quality of TAG ceramics is improved gradually, and the in-line transmittance of the TAG ceramics treated at 1720°C for 20 hours under vacuum and then HIP post-treated at 1700°C for 3 hours under 200 MPa argon gas is 81.6% at 1064 nm. The sintering additive TEOS can improve the optical quality of TAG ceramics and inhibit the valence state change of Tb3+ ions to Tb4+ during the annealing process. The Verdet constant of the TAG ceramics at 632.8 nm is about −178 rad·T−1·m−1 at room temperature, which is 1.3 times that of the commercial TGG crystals (−134 rad·T−1·m−1). 相似文献