木片筛余物高得率半化学法清洁制浆技术研究

以太阳纸业备料车间木片筛选碎料（筛余物）为原料，对其烧碱法半化学制浆的实验室工艺和生产试验进行了研究。结果表明，筛余物采用半化学法制浆可获得较高得率和环压强度的纸浆，且用碱量对纸浆性能有显著影响。相对8%NaOH （相对于绝干原料）化学预处理，采用14%NaOH化学预处理结合两段浆浓22%的高浓磨浆工艺，所制半化学浆抄造浆张的裂断长和环压指数分别达2.89 km和9.76 N·m/g，是前者的1.9倍和1.2倍，而且优于现用国内OCC废纸浆抄造浆张；生产试验得到的浆张性能指标与实验室相吻合，其中紧度和环压强度分别达到GB/T 13023—2008瓦楞芯（原）纸AA级和A级优等品要求。     

Behavior of Decayed Spruce (Picea abies) during Kraft Pulping

This study indicated that by applying an improved classification system to decayed large-diameter Norway spruce (Picea abies) wood, its use as raw material for kraft pulping without loss of pulp quality could be essentially increased. This is based on the fact that although the cooking yield of decayed spruce material which has been sorted according to these new recommendations is somewhat lower and Kappa number higher than those of sound wood material, the greatest part of the decayed stem (the outer part of the stem) contains long-fiber wood material which produces pulp of good quality. Therefore, large-diameter spruce logs can also be separately used, for example, in the manufacture of reinforcement pulp.     

Moulded pulp products manufacturing with thermoforming

For an effective optimization of pulp thermoforming and of the moulded pulp products manufactured by this process, a full understanding of the process physics combined with full knowledge of the pressing equipment is necessary. For this reason, in this Addendum, we clarify how the process parameters “Holding time,” “Vacuum time,” “Cycle time,” and “Temperature” were interpreted and subsequently defined for the analysis of the process and product‐related outputs of the thermoforming experiments.     

Corrosion inhibition of mild steel in 1 M HCl using Tamarindus indica extract: electrochemical,surface and spectroscopic studies

Abstract

We report, here, the corrosion inhibition of mild steel specimen in 1?M HCl by tamarind fruit pulp aqueous (TFPA) extract. The inhibition property in the presence of TFPA extract is studied using weight loss, polarization measurement and electrochemical impedance spectroscopy (EIS). The inhibitor efficiency is found to vary from 74% to 88% (weight loss method) with TFPA concentration of 100–600?ppm. The reduction in Tafel slopes shows that TFPA acts as a mixed-type inhibitor. The adsorption of the inhibitor on the metal surface follows Langmuir isotherm. The standard Gibbs free energy of adsorption value of –40?kJ/mol suggests the chemisorption of inhibitor molecules via coordinate bond. AFM results exhibit a decrease in the surface roughness of mild steel, exposed to 1?M HCl from 299?±?12 to 154?±?6.6?nm, with increasing concentration of inhibitor from 0 to 600?ppm due to the uniform coverage of inhibitor molecules on the metal surface. X-ray photoelectron spectroscopy de-convoluted high resolution profiles of C 1?s (carbon) for mild steel exposed to 1?M HCl with 600?ppm inhibitor show major peaks corresponding to sp³ C–C/C–H (284.9?eV) and oxygen bondings in C–OH, C=O, COOH with a binding energy of 285.9, 286.9, 288.5?eV, respectively, thereby confirming the adsorption of organic moieties on mild steel surface. Fourier transform infrared spectroscopy further confirms the adsorption of inhibitor molecules on the metal surface. Therefore, tamarind fruit pulp extract is a potential corrosion inhibitor for mild steel, which is cost-effective, green and non-toxic.     

Bond strength and adaptation of pulp capping materials to dentin

This study evaluated the shear bond strength (SBS) and internal marginal adaptation of pulp‐capping materials to dentin. Flat occlusal deep dentin surfaces were produced and randomly assigned to two groups (sound or artificial caries‐affected dentin). The specimens in each group were assigned to one of seven subgroups according to the materials used: Biodentine, Theracal LC, Ultra‐Blend plus, Calcimol LC, ApaCal ART, EQUIA Forte, and Ionoseal. Buildups (3‐mm inner diameter and 2‐mm deep) were made over the dentin surfaces. The bonded specimens were tested under shear forces at a crosshead speed of 0.8 mm/min and fracture modes were determined using a stereomicroscope at 25× magnification. The materials were applied to the pulp floor of prepared Class I cavities and then the cavities were restored with composite resin. Restored molar teeth were subjected to 5,000 thermocycles and sectioned in a bucco–lingual direction. Resin replicas were made to determine the adaptation at the pulp floor with scanning electron microscopy. Significant differences were determined among both bond strengths and gap formations of the materials. EQUIA Forte applied to both dentin substrates had a significantly higher SBS than the other materials. The bond strength of each material was not influenced by the dentin condition. Biodentine (3.03%), EQUIA Forte (7.83%), and Theracal LC (13.37%) had lower gap formations compared to other materials but were not significantly different from each other.     

BDAS-I型在线矿浆浓度计的设计

矿浆浓度是选矿流程中各环节的重要指标参数,是工艺调控决策的重要依据。本文基于浓度壶测量原理,通过将简单可靠的浓度壶测量结构和测量过程流程化、自动化,设计了一套结构简单、测量稳定、测量精度优于1.5%的单流道在线浓度测量系统。配套代表性的取样器,BDAS-I型浓度计可灵活安装在搅拌桶、浮选机、矿浆槽、浓密机等测量点附近,满足浮选原、精、尾及中间流程矿浆的浓度测量需求。     

两台竹浆碱回收锅炉NOx、SO2排放的探讨

根据两台竹浆碱回收锅炉的实际运行情况,对其结构与运行对污染物排放的影响进行了比较、分析。     

基于纸浆纤维的贵重物品内包装塑造系统研究

为解决贵重物品与其内包装“契合度”不高的问题，提出基于纸浆纤维的贵重物品内包装塑造系统。系统通过三维扫描获取待包装物品的点云信息，经主控计算机进行数据处理，以下位机为执行中枢，辅之其他外部设备，利用纸浆纤维为贵重物品塑造“量身定制”的内包装，提升内包装契合度，增强保护效果，绿色环保，安全稳定。     

应用树脂矿浆法吸附Ag+的研究

实验研究了吸附时间和pH值对树脂吸附Ag^＋的性能的影响，Ag^＋的浓度对D061树脂饱和吸附容量的影响，温度对D061树脂吸附Ag^＋性能的影响。研究结果表明，D061树脂对Ag^＋有较好的吸附能力，最佳吸附条件为：吸附时间2h，pH值为2．99～4．98，树脂的饱和吸附容量为200mg／L，温度为35℃。而X-5、NKA、NKA-9、D4006等树脂对Ag^＋几乎不吸附。