Dual-phase rare-earth-zirconate high-entropy ceramics with glass-like thermal conductivity

A series of rare earth zirconates (RE₂Zr₂O₇) high-entropy ceramics with single- and dual-phase structure were prepared. Compared with La₂Zr₂O₇ and Yb₂Zr₂O₇, the smaller “rattling” ions (Yb³⁺, Er³⁺, Y³⁺) have been incorporated into pyrochlore lattice in (La_0.2Nd_0.2Y_0.2Er_0.2Yb_0.2)₂Zr₂O₇ (LNYEY) while larger ions (La³⁺, Nd³⁺, Sm³⁺, Eu³⁺) incorporated into fluorite lattice in (La_0.2Nd_0.2Sm_0.2Gd_0.2Yb_0.2)₂Zr₂O₇ (LNSGY). Due to high-entropy lattice distortion and resonant scattering derived from smaller ions Yb³⁺, Er³⁺, and Y³⁺, LNYEY shows a lower glass-like thermal conductivity (1.62-1.59 W m^-1 K^-1, 100-600℃) than LNSGY (1.74-1.75 W m^-1 K^-1, 100-600℃). Moreover, LNYEY and LNSGY exhibit enhanced Vickers’ hardness (LNYEY, H_v = 11.47 ± 0.41 GPa; LNSGY, H_v = 10.96 ± 0.26 GPa) and thermal expansion coefficients (LNYEY, 10.45 × 10^-6 K^-1, 1000℃; LNSGY, 11.02 × 10^-6 K^-1, 1000℃). These results indicate that dual-phase rare-earth-zirconate high-entropy ceramics could be desirable for thermal barrier coatings.     

地应力条件下的凿岩爆破数值模拟

为了研究地应力对凿岩爆破的影响,采用DDA方法模拟爆炸应力波作用下考虑地应力条件时的单孔和多孔凿岩爆破破岩过程。模拟发现,随着初始地应力水平的增加,裂纹扩展半径和破岩区域面积减小,裂纹发育主方向趋于地应力的最大主应力方向,初始地应力对裂纹的抑制和引导作用明显;初始地应力水平的增加,对拉伸裂纹的抑制作用更为显著,从而降低了拉伸破坏对爆破破岩的贡献。模拟也表明,在初始地应力存在的条件下,通过对爆破载荷和炮孔布置进行针对性的优化,可以克服地应力带来的影响,并取得预期的爆破效果。本研究对地应力条件下的凿岩爆破工程具有理论和参考意义。     

离子型稀土矿山淋洗及尾水富集试验研究

对浸矿后离子型稀土原地浸矿场采用清水进行淋洗，在184天的清水淋洗过程中，尾水氨氮值从最开始的507mg/L，降低至140mg/L，淋洗尾水pH4.52~3.10。淋洗尾水采用两级反渗透膜分离，既回收有价资源稀土，又能使出水氨氮达标。结果表明，产水氨氮浓度稳定低于15mg/L，对稀土的截留率高于98.25%，浓水中稀土离子平均浓度313.4mg/L，可进一步回收稀土资源。     

Rare earth metals co-doped ZnO/CNTs composite as high performance photocatalyst for hydrogen production from water_triethanolmine mixture

This study investigated the zinc oxide (ZnO) based heterojunction photocatalysts for improved hydrogen production from water splitting. A sol-gel route was adopted to produce terbium (Tb) and samarium (Sm) co-doped ZnO/CNTs composites where CNTs worked as a support material. The built-in redox couples of lanthanides in co-doped TS-ZnO/CNTs composite showed higher hydrogen evolution activity than Sm doped (Sm-ZnO/CNTs) and Tb doped (Tb–ZnO/CNTs) photocatalysts. When triethanolamine was utilized as a sacrificial agent, the TS-ZnO/CNTs photocatalyst result in a remarkable hydrogen evolution rate of 2683 molh^?1g^?1 under visible light illumination. The optimum photocatalyst also showed high stability over five successive hydrogen evolution cycles. The better hydrogen evolution rate with TS-ZnO/CNTs was referred to its fine particle size, high reactive surface area, small optical band gap, suppressed reunification of charge carriers and built-in redox couples. The photocatalytic mechanism, involved in water splitting with TS-ZnO/CNTs photocatalyst, is also deduced in this study. This study can stimulate the attempts towards construction of lanthanides based co-doped semiconductor photocatalysts for efficient hydrogen evolution.     

基于分形理论的黄河内蒙古段河势演变特征及其与凌汛灾害关联研究

寒区河道凌汛灾害河势“弯道效应”的量化评估十分重要。基于分形理论提出河道横断面-纵剖面-平面多维度河势分形维数计算方法及其物理机制，并探讨黄河内蒙古段不同维度河势演变分形特征及其与凌汛灾害的关联关系。结果表明，黄河内蒙古段不同维度河势均具有多尺度自相似分形特征，且具有多年记忆周期的长程相关性；冰坝（严重性冰塞）发生频次与河道主槽弯曲分形维数呈正相关指数型函数关系，与河相系数、深泓点高程和河段平均底坡分形维数负相关，与水深-面积分形维数正相关，总体表明冰坝灾害更易发生于主槽偏移摆动大、蜿蜒曲折、河湾发育程度高的宽浅型弯曲河道，研究成果可为凌汛期冰塞冰坝灾害易发河段诊断及预测提供重要理论依据。     

高面板坝全寿命周期变形控制方法及应用

高面板坝的变形对面板的安全运行有着特别重要的影响，国内外已建的高面板坝工程中，因坝体变形大导致防渗面板挤压破损，坝体渗漏量大的实例较多，不得不降低水库水位进行修复处理，造成较大的经济损失乃至给大坝的长期运行留下安全隐患。通过发生挤压破损的实例分析，发现变形控制缺乏系统性是发生面板挤压破损的主要因素，为预防面板破损，系统提出了“控制坝体总变形，转化有害变形，适应纵向变形”的坝体变形控制方法，并在使用软硬岩混合料筑坝的董箐面板堆石坝中得到的应用，取得了良好效果，该工程运行至今达十余年，未见面板有挤压破损迹象，该方法对建设200 m以上乃至300 m级超高面板坝具有重要借鉴意义。     

成分配比对稀土钨电极材料组织及力学性能影响

通过固液掺杂、等静压压制、中频烧结的方法，制备了不同的氧化镧、氧化钇、氧化锆三元掺杂成分比例的钨电极材料烧结棒材，探究了不同成分配比对样品显微组织、第二相粒子分布以及宏观力学性能的影响。结果表明，氧化镧、氧化钇、氧化锆三元复合添加能够有效改善第二相粒子在钨基体中的分布形态，降低第二相在晶界的过度富集，提高钨电极材料的综合力学性能。并且当添加成分镧、钇、锆质量比为3:1:1时，材料具有最好的综合力学性能，致密度可达96.04%，显微硬度可达549.37HV0.3，抗压强度可达3785MPa，原因是此配比下第二相粒子最为细小均匀，弥散程度最高，对基体晶粒的细化作用最好，该配比下钨基体平均晶粒尺寸达到10.3μm。     

Full scale investigation of GCL damage mechanisms in small earth dam retrofit applications under earthquake loading

This paper reports results of full scale testing to further explore potential GCL damage mechanisms in earth dam retrofit applications in seismically active areas; in particular, to a) investigate whether shear displacements could reduce the magnitude of GCL panel overlap during earthquake shaking; b) explore the influence of gravel particles on GCL thickness at localised point of contact; and c) observe the consequences of an accidental exposure of an uncovered GCL to short duration rainfall in terms of moisture content and effects during subsequent compaction. The results of these experiments indicate that even under severe shaking no movements were detected at the GCL panel overlap. Whereas gravel particles were observed to locally reduce the thickness of the GCL to 2.2 mm, no plowing of the particle into the GCL occurred due to a lack of shear displacement at the interface, resulting in no localised internal erosion through the barrier. Furthermore, hydration of GCL panels during construction due to surface wetting was observed to result in a state of hydration less than its post-construction state. These results indicate that although each of the three GCL damage mechanisms cannot be ruled out to ever be relevant in practice, the performance of the GCL retrofitted earth dam tested was satisfactory under even severe Level 2 earthquake shaking, and suggests that the retrofitting of small earth dams with GCLs is a promising strategy to improve their static and seismic resistance.     

新型地锚张弦梁式泥石流格栅坝构件受力的简化计算方法

针对常见泥石流防治结构被冲击破坏的问题，基于“柔性消能”理念，结合张弦梁结构和竖向预应力锚杆技术，提出一种既能改善结构受力性能、增加结构整体抗冲击能力、保证结构安全可靠，又能减小结构构件截面尺寸、节约成本、便于现场施工组装和后期运营维护的新型地锚张弦梁式泥石流格栅坝，并阐述其技术原理。根据泥石流荷载分布和新型地锚张弦梁式泥石流格栅坝的受力特征，给出其简化的内力计算方法；并利用SAP2000建立新结构有限元模型，分析了结构的整体受力，验证了构件简化计算方法的合理性；结合Python语言和Qt De? signer软件开发了相应的设计计算软件，对新型地锚张弦梁式泥石流格栅坝的内力进行求解。结果表明：提出的新结构抗冲击性能好，构件受力均匀；以后设计中应关注竖杆的剪切脆性破坏和立柱偏心受力情况，保证结构安全；变形协调仅使底层张弦梁与竖杆内力偏大，实际工程应用时，应着重验算底层构件，防止其破坏；文中提出的简化计算方法能较准确的反映结构的受力特性，具有一定的合理性，研究可为新型地锚张弦梁式泥石流格栅坝的设计计算和推广应用提供理论依据和技术支持。     

Cold crucible melting and characterization of titanate-zirconate pyrochlore as a potential rare earth/actinide waste form

La-Ce-Gd titanate-zirconate pyrochlore-based ceramics was synthesized at the lab-scale inductive melting unit with a 56?mm inner diameter cold crucible. Batch feeding rate and melting ratio were 3?kg/h and 3?kW?h/kg respectively. The ceramics is composed of 85–90?vol% zoned grains of the pyrochlore structure phase, the sample has excellent chemical durability in hot water and may be considered as a promising matrix for actinide – rare earth fraction of high level waste.