Cr doped ZnAl2O4 spinel samples were prepared by the traditional solid state reaction and co-precipitation synthetic route, and the results suggest that the co-precipitation method has some superiority in contrast to the solid state reaction method. XRD, FT-IR, and XPS spectra confirmed that the well-crystallized spinel cubic phase of ZnAl2O4: Cr3+ samples were successfully formed. The morphology of the samples was investigated by FE-SEM and FE-TEM, and the results show that the samples by the co-precipitation route can generate a smaller size of particles compared to the solid state reaction. Photoluminescence excitation spectra monitored at 686 nm are comprised of two broad excitation bands near 530 nm and 395 nm, and the emission spectra show emissions ranging from 640 to 780 nm, due to the 2E?→?4A2 spin-forbidden transition of Cr3+ ions in spinel lattices. The optimized concentration monitored at 686 nm is 1%, while at 693 nm is 3.5%. Compared with the samples by solid state reaction method, the samples by co-precipitation method show preferable luminescent properties, such as the higher photoluminescence intensity and higher quantum efficiency. Several phosphor-converted LEDs were to investigate the applicability of the prepared samples. The results confirm that the phosphor has potential applications in plant growth and supplementing the red region in white-LEDs and the phosphors prepared by co-precipitation are more suitable to be used in phosphor-converted LED devices due to their preferable luminescent properties.
Thermal action in extraction process had effects on characteristic tryptic peptides identification and gelling properties of porcine gelatin. SDS-PAGE, HPLC-LTQ/Orbitrap high-resolution mass spectrometry, texture analyser and rheometer were used to evaluate collagen depolymerisation degree, characteristic tryptic peptides and gelling properties of gelatins prepared in various thermal actions. Results showed that with increasing temperature and time, depolymerisation degree enlarged, while gel strength, gelling and melting temperature decreased. Mass spectra showed that 47 and 49 common characteristic tryptic peptides were identified in gelatins extracted at 50 °C and 100 °C with various times, respectively. Moreover, 34 common characteristic tryptic peptides were identified in all gelatin samples. Further comparison between this work and our previous investigations yielded 20 common characteristic tryptic peptides, which stably exist in various thermal actions. These common characteristic tryptic peptides may be very helpful for the accurate authentication of porcine gelatin. 相似文献
A high-throughput (105.5 g/h) passive four-stage asymmetric oscillating feedback microreactor using chaotic mixing mechanism was developed to prepare aggregated Barium sulfate (BaSO4) particles of high primary nanoparticle size uniformity. Three-dimensional unsteady simulations showed that chaotic mixing could be induced by three unique secondary flows (i.e., vortex, recirculation, and oscillation), and the fluid oscillation mechanism was examined in detail. Simulations and Villermaux–Dushman experiments indicate that almost complete mixing down to molecular level can be achieved and the prepared BaSO4 nanoparticles were with narrow primary particle size distribution (PSD) having geometric standard deviation, σg, less than 1.43 when the total volumetric flow rate Qtotal was larger than 10 ml/min. By selecting Qtotal and reactant concentrations, average primary particle size can be controlled from 23 to 109 nm as determined by microscopy. An average size of 26 nm with narrow primary PSD (σg = 1.22) could be achieved at Qtotal of 160 ml/min. 相似文献