氟碳-纳米自清洁粉末涂料的制备

采用自制的全氟聚醚聚酯树脂与活性纳米Al2O3微粒,制备出F-C纳米自清洁粉末复合涂料。经扫描电镜、接触角测试仪等测定,涂层表面呈F元素的纳米微观结构,接触角大于150°。实验表明,这种F-C纳米自清洁涂料具有超强的耐候性、抗强碱性及明显的超疏水性。     

A Study on the FTIR Spectroscopy of Polylactide Doped with Nano-Aluminium Oxide and Nano-Cupric Oxide

Elucidation of the structure of naturally existing or synthesized substances is an important criterion in the study of materials to predict the application of the substance. In this study, polylactide was doped with nano-aluminium oxide and nano-cupric oxide with 1 and 3 mg of concentration variants. The interaction between the polymer matrix and the nanoparticles has been studied using Fourier transform infrared. Successful doping of the polymer has been observed. Attention has been drawn to check the intermolecular bonding in films having varying thicknesses, films prepared at higher sonication temperatures, and chemical homogeneity of the doped polymer films.     

反应体系组成对Al/PS微胶囊粒径及分布的影响

在纳米A l粒子表面的苯乙烯原位聚合反应中,反应体系的组成(单体用量、引发剂用量、稳定剂用量及A l粒子用量)会对A l/PS微胶囊的形态、粒径大小及分布产生一定的影响。当纳米A l粒子用量小于5%,苯乙烯用量为20%,引发剂及稳定剂用量分别为单体用量的0.5%和1.5%时,制备出的A l/PS微胶囊呈球形,表面光滑无明显缺陷,颗粒之间分散性很好,粒径为1.345μm,分散系数为13.1%。     

纳米片状铝浆料的研制及其对镜面银油墨的性能影响

介绍了物理气相沉积法(PVD)制备纳米片状铝浆料的工艺流程。重点研究镀铝层厚度、PET(聚酯)薄膜与镀铝层之间的剥离层用树脂的黏度、纳米片状铝浆料中的防沉剂和溶剂对镜面银油墨镜面效果的影响。     

纳米铝粉微胶囊的制备及表征

以苯乙烯为聚合单体，无水乙醇为反应介质，在无氧、无水的条件下进行了纳米铝粉的包裹聚合反应，成功地制备出了粒径为2μm左右，且分布较均匀的球形纳米铝粉微胶囊，并运用SEM、TEM、FTIR、XRD、XPS等测试手段对纳米铝粉微胶囊进行了结构表征。     

纳米铝粉的活性分析及寿命预测

采用气体容量法测试了不同铝粉的活性,结果表明,球形纳米铝粉的活性为76．1％,片状普通铝粉的活性为43．0％,铝粉颗粒尺寸对活性有显著影响。采用加速老化试验和Berthlot方法对纳米铝粉进行了寿命预测,以铝粉活性变化10％、20％和30％作为失效判据,预测25℃下纳米铝粉的贮存寿命分别为4．73、9．77和14．80年。     

纳米Al/PS微胶囊中铝粉含量及活性分析

采用优化的工艺条件,制备了不同铝粉含量的纳米铝粉/聚苯乙烯(Al/PS)微胶囊,随着铝粉添加量的增加,铝粉的包覆率逐渐降低。纳米Al/PS微胶囊呈球形,表面光滑无明显缺陷,粒子与粒子之间分散性很好。对纳米铝粉复合前后的活性变化进行了实验分析,结果表明,不同纳米铝粉含量的纳米Al/PS微胶囊中的活性铝含量基本相同,未经贮存、自然条件下密闭贮存30 d及氧气罐中贮存30 d后,活性铝含量分别为76.07%,76.06%和74.81%,纳米铝粉被PS包覆后可长期保持活性。     

Effects of Nano-Aluminium on The Combustion of A PolyNIMMO-Based Propellant

Propellants containing micro-aluminium particles have been shown to produce faster burn rates than conventional gun propellants.However,they are also more abrasive than conventional propellants.Nano-ma...     

无机纳米粉体改性亚胺环氧胶黏剂的研究

采用直接掺杂法制备了无机纳米粉体改性亚胺环氧胶黏剂,探讨了纳米粉体的种类和用量对胶黏剂性能的影响.结果表明:进口Al2O3纳米粉体对胶黏剂的改性效果较好.Al2O3含量在10%左右时室温下的剪切强度达到最大值(约32MPa),提高了约30%;Al2O3含量在14%左右时200℃下的剪切强度达到最大值(18.5MPa),提高了约1.5倍;但引入纳米Al2O3并不能提高胶黏剂的耐热性和耐油性.     

干滑动下端羟基聚丁二烯液体橡胶-环氧树脂复合材料的摩擦性能

用端异氰酸酯基聚丁二烯液体橡胶与环氧树脂制得端异氰酸酯基聚丁二烯橡胶-环氧树脂聚合物(ETPB)。在ETPB中分别加入质量分数为5%和10%的纳米三氧化二铝,并用胺类固化剂固化,制得ETPB/纳米三氧化二铝复合材料。测试了环氧树脂、ETPB和ETPB-纳米三氧化二铝复合材料在干滑动下的摩擦性能,考察了磨损率及摩擦系数与载荷和滑动速度之间的关系,用扫描电子显微镜对几种材料磨损表面进行了观察。结果表明,用端异氰酸酯基聚丁二烯液体橡胶改性环氧树脂可提高干滑动条件下环氧树脂的抗磨损性能;填充纳米三氧化二铝可显著提高ETPB的抗磨损性能,其最佳填充质量分数为5%。