The effects of washing a collagen sample prior to TEM examination

Transmission electron microscopy (TEM) is an important analysis technique to visualize (bio)macromolecules and their assemblies, including collagen fibers. Many protocols for TEM sample preparation of collagen involve one or more washing steps to remove excess salts from the dispersion that could hamper analysis when dried on a TEM grid. Such protocols are not standardized and washing times as well as washing solvents vary from procedure to procedure, with each research group typically having their own protocol. Here, we investigate the influence of washing with water, ethanol, but also methanol and 2-propanol, for both mineralized and unmineralized collagen samples via a protocol based on centrifugation. Washing with water maintains the hydrated collagen structure and the characteristic banding pattern can be clearly observed. Conversely, washing with ethanol results in dehydration of the fibrils, often leading to aggregation of the fibers and a less obvious banding pattern, already within 1 min of ethanol exposure. As we show, this process is fully reversible. Similar observations were made for methanol and propanol. Based on these results, a standardized washing protocol for collagenous samples is proposed.     

Machine fault diagnosis with small sample based on variational information constrained generative adversarial network

In actual engineering scenarios, limited fault data leads to insufficient model training and over-fitting, which negatively affects the diagnostic performance of intelligent diagnostic models. To solve the problem, this paper proposes a variational information constrained generative adversarial network (VICGAN) for effective machine fault diagnosis. Firstly, by incorporating the encoder into the discriminator to map the deep features, an improved generative adversarial network with stronger data synthesis capability is established. Secondly, to promote the stable training of the model and guarantee better convergence, a variational information constraint technique is utilized, which constrains the input signals and deep features of the discriminator using the information bottleneck method. In addition, a representation matching module is added to impose restrictions on the generator, avoiding the mode collapse problem and boosting the sample diversity. Two rolling bearing datasets are utilized to verify the effectiveness and stability of the presented network, which demonstrates that the presented network has an admirable ability in processing fault diagnosis with few samples, and performs better than state-of-the-art approaches.     

DP980高强钢连续退火后的组织与性能

研究了不同工艺参数对980 MPa级连续退火双相钢组织及力学性能的影响,利用光学显微镜、透射电镜(TEM)以及拉伸试验对双相钢的微观组织和力学性能进行测试及分析。结果表明:DP980钢的退火组织主要由铁素体、马氏体岛和少量的贝氏体组成,马氏体岛附近的位错密度较高。随着均热温度的升高,DP980钢的抗拉强度呈现先降低后升高的趋势,屈服强度与抗拉强度的趋势一致,伸长率先升高后降低。随着过时效温度的升高,DP980钢的抗拉强度和屈服强度降低,降低幅度较小,伸长率上升,但变化不明显,说明通过调整过时效温度来调控其力学性能的作用较小。     

Corrosion behavior of under‐, peak‐, and over‐aged 6063 alloy: A comparative study

The mechanical property of age‐hardenable Al‐alloys is governed by the state of ageing, which determines the microstructure and consequently, their corrosion behavior which is a vital aspect for a number of applications. This article presents a comparative assessment of corrosion behavior of under‐, peak‐ and over‐aged Al‐Mg‐Si alloy. Corrosion characteristics have been determined via immersion tests in 0.1 M ortho‐phosphoric acid solution and intergranular corrosion (IGC) tests. Corroded surfaces are examined by field emission scanning electron micrographs‐energy dispersive spectroscopy and 3D optical profilometer. The obtained results reveal that the corrosion rate at a specific immersion time as well as the depth of IGC increases in the order for under‐, peak‐, and over‐aged states. Irrespective of the state of ageing, corrosion loss increases linearly but the rate of corrosion decreases rapidly with increasing immersion time. The dominant mode of corrosion in under‐aged alloy is identified as localized pitting, while peak‐aged is highly susceptible to IGC in contrast extensive pitting corrosion is observed for over‐aged alloy. The observed differences in corrosion behavior are explained considering characteristics of precipitates. Formation of β (Mg₂Si) in case of over‐aged alloy and presence of inclusions like AlFeMnSi particles are found to accelerate pitting corrosion.     

不同制样方法对直流辉光放电质谱法测定氮化硼中27种杂质元素的影响

讨论了3种制样方法对直流辉光放电质谱法(dc-GDMS)检测氮化硼中的Na、Mg、Al、Si等27种杂质元素的影响。3种制样方法分别如下所示:方法1,直接把氮化硼压在铟薄片上;方法2,把氮化硼压在铟薄片上后,再盖上一层铟罩;方法3,把压碎后的氮化硼放在针状钽勺上。在优化的辉光放电参数下对比了3种不同制样方法对基体信号强度的影响。试验表明:在方法1中,当氮化硼尺寸约为3mm×3mm,厚度小于1mm时,基体¹¹B的信号可达1.8×10⁷ cps;在方法2中,选择铟孔大小合适的铟罩,基体¹¹B的信号可达1.0×10⁷ cps;方法3获得基体信号强度比方法1、方法2高一个数量级。大部分元素在中分辨率下可获得较好的结果,而对于在高分辨率下也较难分离的元素,可选择丰度较低的同位素在中分辨率下进行测定,如Ge选择⁷⁰Ge⁺,Se选择⁸²Se⁺,Cd选择¹¹¹Cd⁺,Sn选择¹¹⁹Sn⁺,Ag选择¹⁰⁹Ag⁺,Pt选择¹⁹⁴Pt⁺。氮化硼中的杂质元素含量可通过样品片中待测元素含量减去来自于铟薄片或钽勺中该元素贡献的含量来计算获得。将样品平行测定5次,相对标准偏差均在20%以内。对于Al、Si、Ti等元素的测定,3种制样方法的测定结果基本一致;方法1、方法2中检测到的In含量较大,使得铟中的Ni、Cu对氮化硼的测定值影响较大;方法3由于钽中Fe、Cu的贡献导致氮化硼中Fe、Cu的检测值较大,但方法3获得的基体信号强度大,可降低部分元素的检出限,如Cr、Mn、Ga、Ge等。综上所述,方法3为优选方法。     

对空监视雷达探测威力检飞的几个问题

以新的观点论证了对空监视雷达探测威力检验飞行中所需的采样点数和飞行架次，讨论了预警机雷达威力检飞的特殊问题，包括地区选择、航线设计和目标机标定等。     

基于自适应加权Fisherface算法的人脸识别

提出了一种改进的Fisherface算法。算法首先利用Karhunen-Loeve（K-L）变换降维，在降维的子空间内，根据样本与同类样本间的距离赋予该样本一权值，再用加权后的样本求取类均值，以新的类均值重建类内散布矩阵和类间散布矩阵，从而改进Fisher判别函数。在ORL和Yale人脸库上的实验结果表明，该算法优于传统的主成分分析（PCA）方法和Fisherface方法，并能有效解决小样本情况下训练样本类均值偏离类中心的问题。     

径向基函数神经网络的再学习算法及其应用

为了应用径向基函数神经网络逐步地识别待研究系统,文章针对径向基函数神经网络的再学习算法开展了深入的研究.应用严格的数学推理方法,将径向基函数神经网络的再学习问题转化为矩阵求逆的附加运算.详细给出了径向基函数神经网络再学习算法中增加新训练样本和增加新基函数的数学公式,同时对如何获取新的训练样本进行了研究.     

串行及并行A/D转换器在高速数据采集中的采样差别性分析

串行和并行接口模式是A/D转换器诸多分类中的一种,但却是应用中器件选择的一个重要指标.在同样的转换分辨率及转换速度的前提下,不同的接口方式不但影响了电路结构,更重要的是将在高速数据采集的过程中对采样周期产生较大影响.本文通过12位串行ADC ADS7822和并行ADC ADS774与AT89C51的接口电路,给出二者采样时间的差异性.