(K0.5Na0.5)1-2xSrx(Nb0.94 Sb0.06)O3无铅压电陶瓷结构及性能研究

以传统电子陶瓷工艺制备了(K_0.5Na_0.5)_1-2xSr_x(Nb_0.94 Sb_0.06)O₃ 无铅压电陶瓷，研究了适量锶、锑取代对陶瓷结构及电性能的影响. 结果表明，少量的锶、锑取代没有改变(K_0.5Na_0.5) NbO₃陶瓷的相结构，仍为单相正交结构的钙钛矿型铁电体；适量的锶取代使得晶粒大小均匀一致,提高了陶瓷的致密度；锶、锑取代降低了陶瓷的居里温度，但对正交四方相变温度的影响不大，且在0~200℃的温度范围，介电常数几乎不依赖频率的变化而变化；在x=0.008处，得到较好综合性能的陶瓷材料：d₃₃=155pC/N，k_p=0.361，Q_m=120，N_p=2862，P_r=23μC/cm²，E_c=1.4kV/mm，ρ=4.411g/cm³.     

Preparation of Ni/PZT core-shell nanoparticles and their electromagnetic properties

The Ni nanoparticles coated with Pb(Zr,Ti)O_3(PZT) were synthesized by a sol-gel method and in situ reaction. And their structure, oxidation resistance, and electromagnetic properties were investigated. The X-ray diffraction patterns(XRD) exhibited that a small amount of impure phase characterized to Ni(OH)_2 was detected from the ammonia-treated Ni nanoparticles and the ammonia-treated Ni nanoparticles coated with PZT. After being pre-treated with aqueous ammonia, the PZT coating layer was more uniform and about 10 nm in thickness. The oxidation resistance of the ammonia-treated Ni nanoparticles coated with PZT, compared with that of the non-treated ones, was improved by about 66 ℃. The PZT shell layer prepared by in-situ reaction can greatly reduce the dielectric constant and improve the natural resonance loss at high frequency, so as to obtain the optimal impedance matching performance of the electromagnetic wave transmission.     

Ba~(2+)取代对PSN-PZT瓷结构和压电性能的影响

研究了Ba2+A位取代对铌锑锆钛酸铅陶瓷结构及压电性能的影响,XRD分析结果表明:所有样品具有钙钛矿结构,同时Ba2+取代Pb2+使得晶胞体积增大,c/a轴比减小。当Ba2+取代量增大时,样品中三方相和四方相共存。随着Ba2+取代量的增大,陶瓷样品的密度降低,εr(2863)和d33(507pC·N–1)显著提高,居里点向室温移动。     

无铅压电陶瓷(Bi1/2Na1/2)TiO3-KNbO3制备工艺研究

采用传统陶瓷工艺制备了(1-x)(Bi1/2Na1/2)TiO3-xKNbO3(x=0.01,0.02,0.04,0.6,0.08,0.12)无铅压电陶瓷。利用热重-差热(TG-DSC)、X-射线衍射(XRD)和扫描电镜(SEM)等分析技术,研究了(1-x)(Bi1/2Na1/2)TiO3-xKNbO3无铅压电陶瓷的制备工艺条件对陶瓷晶体结构、压电性能的影响。TG-DSC、XRD的结果表明,该体系的的最佳预合成温度在800~850℃;SEM及性能测试的结果表明,该体系随KNbO3含量的增加,烧结温度提高,烧结的温度范围变窄,当x>0.1时,烧结的温度范围只有5~10℃。     

(1-x)ZnWO4-xTiO2陶瓷的微波介电性能研究

用固相反应法在1150℃烧结2h得到了致密的(1-x)ZnWO4-xTiO2 (0.1≤x≤0.8)系列微波介质陶瓷,对陶瓷的相组成、显微结构及微波介电性能进行了研究.结果表明:在(1-x)ZnWO4-xTiO2 (0.3≤x≤0.5)陶瓷样品中存在ZnWO4、TiO2及Zn2TiO4三相,当Zn2TiO4相的量较多时,样品的微波介电性能较好.随着TiO2的含量增加,(1-x) ZnWO4-xTiO2陶瓷的εr及τf值单调递增,而Q·f值则先上升后下降.当x=0.4时,(1-x)ZnWO4-xTiO2陶瓷样品的微波介电性能为:εr=26.56、Q·f=42 278 GHz及τf =61.37× 10-6/℃.它是一种具有中等介电常数,中低烧结温度且性能优良的微波介质陶瓷新体系.     

预烧温度对PZN-PZT压电陶瓷电性能的影响

采用传统固相法制备了化学计量比为0.3Pb(Zn1/3Nb2/3)O3-0.35PbTiO3-0.35PbZrO3的压电陶瓷,研究了所制陶瓷的预合成温度对其微观结构和压电介电性能的影响。结果显示,当预合成温度大于800℃时可以获得纯钙钛矿相,低于800℃钙钛矿主晶相不明显且有很多杂相产生。当预烧温度为775℃时,经1 125℃保温3 h烧结的陶瓷具有最佳综合性能:d33=431 pC/N、k31=0.36、Ec=9.98×103 V/mm、Pr=22.52×10–6 C/cm2、εr=1 874、tanδ=0.024、ρ=7.88 g/cm3。     

Zn-B玻璃掺杂的(K0.5Na0.44Li0.06)(Nb0.84Ta0.1Sb0.06)O3陶瓷相变及电学性能研究

研究了Zn-B玻璃掺杂的(K0.5Na0.44Li0.06)(Nb0.84Ta0.1Sb0.06)O3(KNLNTS)陶瓷的制备、相变及电学性能.研究发现,Zn-B玻璃能够有效地促进铌酸钾钠基无铅压电陶瓷的烧结特性.XRD结果显示Zn-B玻璃掺杂的KNLNTS陶瓷为正交-四方共存结构,随掺杂量的增加正交结构相的含量逐渐增加;并且降低烧结温度能够有效地抑制第二相的产生.介电温谱测试结果显示Zn-B玻璃掺杂的KNLNTS陶瓷其居里温度先降后增在x=0.1时达到最小值.在1050℃保温5 h条件下烧结可以获得最佳的压电性能:d33=197 pC/N,kp=0.37,εr=975,tanδ=0.028.     

ZnO掺杂对PSN-PZT陶瓷烧结温度及压电性能的影响(英文)

为了降低PZT压电陶瓷的烧结温度,研究了ZnO掺杂对Ba、Fe改性的PSN-PZT陶瓷的烧结温度和压电特性的影响。通过XRD和SEM测试手段,分析了微观结构和材料性能的关系。XRD结果显示所有样品均呈现四方钙钛矿结构。在w(ZnO)<0.1%时陶瓷压电性能随ZnO的增加而提高;当w(ZnO)=0.1%时,陶瓷样品同样展现出了优良的压电性能。这些结果证明了适量的ZnO掺杂可以降低陶瓷的烧结温度并提高压电性能。