Fe-based bulk metallic glasses (BMGs) with high boron content have potential application as a coating material used in the framework for storing spent nuclear fuels to support their safe long-term disposal. The high glass forming ability (GFA) and large supercooled liquid region are therefore required for such Fe-based BMGs in either the glassy powder fabrication or the subsequent coating spraying. In order to meet these requirements, the influence of Nb content on the GFA of Fe57Cr10Zr8B18Mo7−xNbx (x=1–5, at.%) alloys was investigated, as Nb has positive roles in GFA and thermal stability of BMGs. The results indicate that a fully amorphous phase in the as-cast samples with 3 mm in diameter is obtained for both the Fe57Cr10Zr8B18Mo5Nb2 and Fe57Cr10Zr8B18Mo4Nb3 alloys. The corresponding supercooled liquid regions of the two BMGs are 78 K and 71 K, respectively. The mechanism for improving their GFA was analyzed based on the principle of metal solidification, the parameters for glass formation and thermal properties of the alloys. The compression strength and Vicker’s hardness of the two BMGs are 1,950 MPa and 1,310 HV, 2,062 MPa and 1,180 HV, respectively. The developed BMGs with high B content, good GFA, and very high hardness can be used as coating materials to the framework for spent nuclear fuels.
Polyamines are ubiquitous, low-molecular-weight aliphatic compounds, present in living organisms and essential for cell growth and differentiation. Copper amine oxidases (CuAOs) oxidize polyamines to aminoaldehydes releasing ammonium and hydrogen peroxide, which participates in the complex network of reactive oxygen species acting as signaling molecules involved in responses to biotic and abiotic stresses. CuAOs have been identified and characterized in different plant species, but the most extensive study on a CuAO gene family has been carried out in Arabidopsis thaliana. Growing attention has been devoted in the last years to the investigation of the CuAO expression pattern during development and in response to an array of stress and stress-related hormones, events in which recent studies have highlighted CuAOs to play a key role by modulation of a multilevel phenotypic plasticity expression. In this review, the attention will be focused on the involvement of different AtCuAOs in the IAA/JA/ABA signal transduction pathways which mediate stress-induced phenotypic plasticity events. 相似文献
Barium strontium alumino silicate (BSAS); (Ba0.6Sr0.4Al2Si2O8) was synthesized through solid state reaction between BaCO3, SrCO3, Al2O3 and SiO2 subjected to wet milling in isopropanol for about 24 h. The sequence of the solid state reaction was studied by subjecting to DG/DTG from room temperature to 1550 °C. The crystallographic phase evolution was confirmed by X-ray diffraction of the powders calcined in the range 1000 to 1300 °C for 2 h. The monoclinic celsian phase obtained at 1300 °C, pelletized through uniaxial pressing was sinterable to 67 to 78% density in the temperature range of 1300 to 1500 °C. The density improved to 75 to 94% after ball milling for 76 h, while ZrO2 addition further improved the density by 2%. The celcian phase of BSAS was dispersed in isopropyl alcohol, milled for about 24 h and spray coated on to plain SiC and mullite precoated SiC substrates. Sintering of coated samples and characterization for weight gain/loss, microstructure, scratch test prove that mullite + BSAS coating is more effective than single layer coating of BSAS on SiC substrates. 相似文献
A numerical model is developed for surface crack propagation in brittle ceramic coatings, aiming at the intrinsic failure of rare-earth silicate environmental barrier coating systems (EBCs) under combustion conditions in advanced gas turbines. The main features of progressive degradation of EBCs in such conditions are captured, including selective silica vaporization in the top coat due to exposure to water vapor, diffusion path-dependent bond coat oxidation, as well as crack propagation during cyclic thermal loading. In light of these features, user-defined subroutines are implemented in finite element analysis, where surface crack growth is simulated by node separation. Numerical results are validated by existing experimental data, in terms of monosilicate layer thickening, thermal oxide growth, and fracture behaviors. The experimentally observed quasi-linear oxidation in the early stage is also elucidated. Furthermore, it is suggested that surface crack undergoes rapid propagation in the late stage of extended thermal cycling in water vapor and leads to catastrophic failure, driven by both thermal mismatch and oxide growth stresses. The latter is identified as the dominant mechanism of penetration. Based on detailed analyses of failure mechanisms, the optimization strategy of EBCs composition is proposed, balancing the trade-off between mechanical compliance and erosion resistance. 相似文献
In this study,nano-sized SnO_2 decorated on carbon cloth(SnO_2/CC) is prepared through a simple and facile solid method.The nano-sized SnO_2 is uniformly distributed on the surface of carbon fibers in carbon cloth,providing sufficient free space to relieve volume expansion and reduce electrode pulverization during cycling.The as-prepared SnO_2/CC as a flexible,self-supporting and additive-free anode electrode for sodium-ion/lithium-ion batteries(SIBs/LIBs) can demonstrate outstanding electrochemical performance.SnO_2/CC after annealing at 350℃(SC-350) as an anode for SIBs can deliver a reversible capacity of 0.587 mA h cm~(-2) at the current density of 0.3 mA cm~(-2) after 100 cycles.In addition,when cycling at 1.5 mA cm~(-2),SC-350 can maintain 1.69 mA h cm~(-2) after 500 cycles when used as LIB anode.These results illustrate that the as-prepared SnO_2/CC can be a promising flexible anode material for flexible SIBs/LIBs and provide a simple and practical method for designing new flexible electrode materials. 相似文献