Crowding as an Agronomic Factor Determining the Development of Plants and the Productivity of Linseed (Linum usitatissimum L.)

ABSTRACT

Nine sowing densities of linseed were compared in a two-year experiment. Self-regulation of the density of a linseed stand resulted in a differentiated branching of the plants. The number of capsules on a linseed shoot, as well as seeds in the capsule, and the number of seeds from the shoot were highly varied from year to year, and there is even a stronger differentiation in the weight of 1000 seeds. Linear relationships were noted between the mass of seeds from the linseed plant and the number of capsules. The yield of linseed was affected by both factors. An increasing sowing rate reduced the seed yield from the shoot and the plant. At lower seeding rates, the lateral shoots contributed in the seeds yield of the plant to a higher degree compared to the main ones.     

氧化沟模型处理亚麻沤制废水的研究

利用液可清(ACF32)培养污泥,水解酸化、氧化沟工艺进行亚麻沤制废水处理。结果表明,该系统处理高浓度有机废水效果良好,COD去除率可达95%-97%,TN去除率可达78%-82%,TP去除率可达78%-86%。     

Further compositional analyses of flax: Mucilage,trypsin inhibitors and hydrocyanic acid

Registered Canadian cultivars of flax, and laboratory-prepared and commercially obtained samples of linseed meal (LM), were used to determine extract viscosity and mucilage, trypsin inhibitors and hydrocyanic acid (HCN) concentrations. The mucilage readily leached out from the seed coat (hull) fragments soaked in water, leaving behind pentagon-shaped cells that could be seen clearly in scanning electron micrographs. Extract viscosity significantly varied in the laboratory-prepared (23–48 cS) and commercially obtained (30–68 cS) samples of LM and may be used to obtain an indirect, qualitative estimate of flax mucilage. Mucilage was extracted from whole seed in 5.0–5.3% yields and contained 20–24% protein (about 10% ash and 30% total carbohydrates). Laboratory-prepared LM (raw) contained 42–51 units of trypsin inhibitor activity, commercially obtained samples, 14–37 units, and raw rapeseed and soybean meals, 99 and 1650 units, respectively. Picric acid tests (qualitative) showed only traces of HCN in ten cultivars of freshly ground flax. The acid silver nitrate titration procedure measured HCN quantitatively, but showed its presence only in three of the five cultivars investigated. HCN was conveniently measured by a colorimetric procedure (barbituric acidpyridine reaction), which may be used to screen flax cultivars. HCN content of flax was significantly influenced by environments (growth location and season) and, to a less extent, by cultivar.     

亚麻非织造布的缝合加固及其复合材料成型性研究

亚麻纤维通过针刺工艺加工成非织造布,再经缝合加固后,作为复合材料的增强体,与不饱和聚酯树脂复合,制成亚麻/不饱和聚酯复合材料板材及异型件。利用真空辅助树脂传递模塑法制备出的板材,亚麻纤维和树脂结合较为均匀、充分。模压法形成的亚麻非织造布异型件成型良好,无褶皱与破洞。对板材及异型件拉伸、弯曲及压缩等性能的测试结果表明,板材拉伸强度最大值达58.59MPa,弯曲强度最大值为120.26MPa;采用平行缝合工艺的异型件最大破坏载荷为8.99kN。     

原色纱亚麻织物麻皮漂白去除方法探讨

在亚麻织物前处理加工过程中较难去除的是亚麻麻皮木质素,针对亚麻织物前处理工艺中亚麻麻皮的漂白或去除难易程度进行了试验,并探讨了原色纱亚麻织物中麻皮木质素漂白或去除适用的加强煮练、氯漂、酸洗等工艺方法.     

高支纯亚麻嵌入式复合纱的工艺探讨

探究了利用嵌入式复合纺纱技术纺制高支纯亚麻纱.通过改造多功能纺纱小样机以实现嵌入式复合纺纱技术并对雨露沤麻过后的亚麻纤维进行化学脱胶和剪切处理,以70/30的比例和水溶性维纶短纤维混合制条做成粗纱后,在细纱机上纺制了嵌入式亚麻水溶性维纶复合纱,通过对成纱的强伸性、毛羽、条干均匀度的测试与比较进行了纺纱工艺的优化.结果表明,纺制20.7 tex亚麻水溶性维纶嵌入式复合纱的工艺最佳值为捻系数420、长丝预加张力7.5 cN、长丝与长丝间距8 mm、长丝与粗纱间距1.5 mm;经优化工艺试纺的20.7 tex亚麻水溶性维纶嵌入式复合纱,经退维处理后的纱线细度为8.9 tex;亚麻水溶性维纶嵌入式复合纱结构稳定、强力较高、条干均匀、毛羽少,为开发高档亚麻类面料提供了新的途径.     

亚麻/聚丙烯复合材料的制备及拉伸、顶破性能

以亚麻纤维作为增强纤维,以聚丙烯纤维作为树脂基体,通过模压成型工艺方法,制备了绿色环保型亚麻/聚丙烯复合材料,主要研究了纤维长度、模压温度及保温时间对复合材料拉伸性能及顶破性能的影响.结果表明:模压温度对复合材料性能的影响最显著;当纤维长度为5 mm、模压温度为180℃、保温时间为40 min时,复合材料的拉伸性能最优;在纤维长度为5 mm、模压温度为170℃、保温时间为40 min时,复合材料的耐顶破性能最优.     

亚麻针织产品的酶整理工艺探讨

为改善亚麻针织物的舒适性能，探讨用生物酶整理工艺来提高其柔软性。选取酶剂浓度、pH值、温度和时间4个因素作为正交实验的因子，进行了四因素四水平的正交实验。通过对实验结果的分析，确定了合理的生物酶整理工艺条件。工艺参数分别为：酶整理温度为50℃，整理液pH值为5，酶剂浓度为2%，整理时间为60min,亚麻针织坯布经过这种优化的酶整理后柔软性改善效果十分显著。     

Effect of water aging on the mechanical properties of flax fiber/bio-based resin composites

Present work investigates the effect of hydrothermal aging of flax fiber-reinforced bio-based epoxy resin laminates on the mechanical and thermomechanical properties of the composites. Three different types of bio-based resins were used. Plates reinforced with eight layers plain weave flax fibers of 150 g/m², manufactured using Resin Transfer Molding (RTM), compression molding or autoclave technique depends on type of the resin. One dimensional Fickian behavior shows a good fitting to the experimental data derived from weight measurements. The water uptake at the equilibrium state in the case of 60 °C temperature was slightly greater than that at 40 °C. The mechanical properties after hydrothermal aging show a significant reduction and do not return to their initial values even after the drying process. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2020 , 137, 48787.