Annealing temperature dependent structural and optical properties of electrodeposited CdSe thin films

Cadmium selenide films were synthesized using simple electrodeposition method on indium tin oxide coated glass substrates. The synthesized films were post annealed at 200 °C, 300 °C and 400 °C. X-ray diffraction of the films showed the hexagonal structure with crystallite size <3 nm for as deposited films and 3–25 nm for annealed films. The surface morphology of films using field emission scanning electron microscopy showed granular surface. The high resolution transmission electron microscopy of a crystallite of the film revealed lattice fringes which measured lattice spacing of 3.13 Å corresponding to (002) plane, indicating the lattice contraction effect, due to small size of CdSe nanocrystallite. The calculation of optical band gap using UV–visible absorption spectrum showed strong red-shift with increase in crystallite size, indicating to the charge confinement in CdSe nanocrystallite.     

Formation of ST12 phase Ge nanoparticles in ZnO thin films

In this work, we focus on the Ge nanoparticles (Ge-np) embedded ZnO multilayered thin films. Effects of reactive and nonreactive growth of ZnO layers on the rapid thermal annealing (RTA) induced formation of Ge-np have been specifically investigated. The samples were deposited by sequential r.f. and d.c. sputtering of ZnO and Ge thin film layers, respectively on Si substrates. As-prepared thin film samples have been exposed to an ex-situ RTA at 600 °C for 60 s under forming gas atmosphere. Structural characterizations have been performed by X-ray Diffraction (XRD), Raman scattering, Secondary Ion Mass Spectroscopy (SIMS), and Scanning Electron Microscopy (SEM) techniques. It has been realized that reactive or nonreactive growth of ZnO layers significantly influences the morphology of the ZnO: Ge samples, most prominently the crystal structure of Ge-np. XRD and Raman analysis have revealed that while reactive growth results in a mixture of diamond cubic (DC) and simple tetragonal (ST12) Ge-np, nonreactive growth leads to the formation of only DC Ge-np upon RTA process. Formation of ST12 Ge-np has been discussed based on structural differences due to reactive and nonreactive growth of ZnO embedding layer.     

Inhibition of microbial growth in ready‐to‐eat food stored at ambient temperature by modified atmosphere packaging

This study was undertaken to develop a modified atmosphere package to control microbial growth in ready‐to‐eat (RTE) products stored at ambient temperature. Ethanol and/or limonene associated with modified atmosphere (CO₂ : O₂ : N₂ = 30% : 5% : 65%) was used to inhibit the growth of total air‐borne microorganisms and Escherichia coli in RTE products stored at 25°C. The results indicated that 0.05% ethanol vapour in the headspace was effective to inhibit the growth of air‐borne microorganisms and E. coli at 25°C for 72 h in a model study, and the effectiveness was related to ethanol content. Both 73 ppm limonene and 0.05% ethanol vapour enhanced the bacteriostatic effect of modified atmosphere in RTE sushi roll products, and no off‐flavour was detected using this formulated gas; however, no significant inhibitory effect was observed for RTE cold noodle products. This study concludes that combinations of carbon dioxide, ethanol or limonene vapours are effective to inhibit microbial growth in RTE food at ambient temperature, and the outcome may be due to the hurdle effect. Copyright © 2003 John Wiley & Sons, Ltd.     

Effect of select parameters on the properties of edible film from water-soluble fish proteins in surimi wash-water

Edible film from water-soluble fish proteins were developed by casting film solution on leveled trays and effects of pH (9.5, 10.0 and 10.5), heating temperature (60, 70 and 80 °C), and heating time (10, 20 and 30 min) of the film solution on various film properties were determined using Response Surface Methodology (RSM). The impact of pH and heating temperature of film solution was more significant, overall, on the film's properties than heating time. Contour plots of tensile strength and elongation at break was highest at pH of 10.0 at 70 °C (2.75-3.02 MPa) but low in elongation at break (6.35-9.16%), while water vapor permeability and oxygen permeability were at their lowest (58.55-65.96 g mm/m² d kPa and 351.33-624.18 cm³ μm/m² d kPa). There was a direct correlation between the films’ and proteins’ solubility on one hand, and heating temperature of film solution on the other, which reversed with change in pH of film solution. Film color was darker and more yellowish with increase in the pH of film solution.     

Influence of Polyalkylmethacrylate VII on Boundary Film Formation,Friction,Wear and Efficiency of Lubricants

1 Influence of PAMAon Boundary Fil mFormation and Friction1.1 Experi mental methodsUltra-thin optical interferometry has been used tostudy thinlubricating fil ms for more than a decade and theexperi mental details of this technique have been reportedpreviously[1].The principle of the test setup is shown inFigure1.A polished steel ball is loaded and rolled againstthe flat surface of a glass disc that is coated with a thinsemi-reflecting chromiumlayer and a silica spacer of about500nmthickne…     

Nonstationary Simulation Model of Absorber with Falling Film of Suspension

A nonstationary model of SO₂ absorption from a gas phase to a countercurrent falling film of absorbing slurry was developed. Laminar, wavy and turbulent film structures were considered based on published information. Resistances to the mass transfer on the gas and the liquid sides of the interphase were considered, together with chemical reactions in the liquid phase. Relevant chemical equilibria in the liquid phase were modeled. Original experimental data on the neutralization reagent dissolution rate presented as a polydispersed two‐phase system of solids and on the rate of dissolved sulfite oxidation were used. The model was verified with experimental data from a laboratory‐scale falling‐film absorber using a single vertical tube under various geometrical and operating conditions, and a very good agreement was found with the experiment. Parametric sensitivity analysis showed the critical parts of the model.     

Gamma-irradiation-induced Ag/SiO2 composite films and their optical absorption properties

Small Ag particles or clusters dispersed mesoporous SiO₂ composite films were prepared by a new method: First the matrix SiO₂ films were prepared by sol-gel process combined with the dip-coating technique, then they were soaked in AgNO₃ solutions followed by irradiation of γ-ray at room temperature and in ambient pressure. The structures of these films were examined by X-ray diffraction (XRD), high-resolution transmission electron microscope (HRTEM), and optical absorption spectroscopy. It has been shown that the Ag particles grown within the porous SiO₂ films are very small, and they are isolated and dispersed from each other with very narrow size distributions. With increasing the soaking concentration and an additional annealing, an opposite peakshift effect of the surface plasmon resonance (SPR) was observed in the optical absorption measurements.     

二氧化锡溅射工艺研究

SnO2 是最早使用也是目前使用最广泛的一种气敏材料 ,使用该材料设计制作的气敏传感器具有许多优点。在简要介绍溅射镀膜的成膜过程和特点的基础上 ,着重介绍了SnO2 膜的制备流程 ,分析了功率和温度变化对成膜质量的影响     

Low temperature delamination of plastic encapsulated microcircuits

Plastic encapsulated microcircuits (PEMs) are increasingly being used in applications requiring operation at temperatures lower than the manufacturer’s recommended minimum temperature, which is 0°C for commercial grade components and −40°C for industrial and automotive grade components. To characterize the susceptibility of PEMs to delamination at these extreme low temperatures, packages with different geometries, encapsulated in both biphenyl and novolac molding compounds, were subjected to up to 500 thermal cycles with minimum temperatures in the range −40 to −65°C in both the moisture saturated and baked conditions. Scanning acoustic microscopy revealed there was a negligible increase in delamination at the die-to-encapsulant interface after thermal cycling for the 84 lead PQFPs encapsulated in novolac and for both 84 lead PQFPs and 14 lead PDIPs encapsulated in biphenyl molding compound. Only the 14 lead novolac PDIPs exhibited increased delamination. Moisture exposure had a significant effect on the creation of additional delamination.