Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm²h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. These results stress the importance of controlling the content of HAGBs during the production process of SiC.     

Green preparation of vanadium carbide through one-step molten salt electrolysis

Vanadium carbide (VC) as excellent ceramic and functional material is usually prepared by carbothermal reduction of V₂O₅ which must be extracted from a typical V slag by complex processes. Pollutants, such as ammonia-nitrogen wastewater, NH₃ and CO₂ are inevitably discharged. A novel and green method for VC preparation was proposed by one-step co-electrolysis of soluble NaVO₃ and CO₂ in molten salt. It was found that VC with high purity was easily obtained by reducing electrolysis temperature and CO₂ flow rate to 600 °C and 10 mL min⁻¹ at 3.0 V. Besides VC with particles and layered stacking structure in products, a small amount of carbon and oxygen elements existed. The atomic percentage contents of C, V, and O elements in VC were about 50.0%, 44.5% and 3.8%, respectively. During electrolysis, CO₃²⁻ and VO₃⁻ was reduced at about −0.55 V (vs. Ag/AgCl) and −1.38 V (vs. Ag/AgCl), respectively. CO₃²⁻ ions were more easily reduced than VO₃⁻, and was firstly reduced to CO₂²⁻ and then converted to C. Then, VC was prepared by two routes from CO₂ and NaVO₃. One route is that VO₃⁻ ions are firstly electroreduced to VO₂⁻ ions and then are further electroreduced to VC with C. Another route is that VO₃⁻ ions are electroreduced to V which in-situ reacted with C to VC. Both VO₃⁻ and CO₃²⁻ ions are electroreduced by two-step process. In final, VC is in-situ deposited on cathode. It provides a novel and green way to prepare VC and also achieves the high value-added utilization of vanadium slag and CO₂.     

微纳层叠聚丙烯腈凝胶流动特性的数值模拟研究

建立了层叠流道的三维模型和有限元网格模型，根据流变测试数据，采用Polymat对物料的黏度模型参数进行拟合，并利用Polyflow软件对聚丙烯腈（PAN）凝胶在层叠流道内的三维等温流动过程进行了数值模拟分析。研究发现，当入口流量增大时，层叠流道出口速度的不均匀性增加；沿流动方向流道内压力逐渐降低，并在出口处降低至同一最低值；流道进出口压力差与入口流量大小具有正相关性；在流道的中心截面上剪切速率分布均匀，波动较小。     

电石汽车卸料、破碎、除尘、输送一体化智能系统——中吴天玺系统

针对PVC企业电石车间存在的粉尘污染严重、人工操作安全隐患大等问题,江苏中吴环境工程设计研究有限公司开发了电石汽车卸料、破碎、除尘、输送一体化智能系统(即中吴天玺系统),对该系统的工艺流程、系统组成、占地空间、经济效益和社会效益簣方面进行了介绍。     

High-temperature deformation in bulk polycrystalline hafnium carbide consolidated using spark plasma sintering

In this study, we report the three-point flexural strength and fracture toughness of monolithic hafnium carbide up to 2000 °C. HfC with different grain sizes was consolidated using the spark plasma sintering method. Coarse-grained monoliths showed a weak dependence on the strain rate during high-temperature tests at 1600 °C–2000 °C. In contrast, results for the ceramics with a grain size below 20 μm indicated a positive dependence of the yield strength vs strain rate. This allowed us to identify the activation energy for high-temperature deformation in flexure as 370 kJ/mol. This level of activation energy is in satisfactory agreement with reports about the diffusion of C in hafnium carbide.     

Low/intermediate temperature pyrolyzed polysiloxane derived ceramics with increased carbon for electrical applications

This study focuses on the chemistry, thermal stability, and electrical conductivity of low/intermediate pyrolysis temperature (700?900 °C) polysiloxane derived ceramics. These ceramics were modified with additional carbon derived from divinylbenzene (DVB) added to the precursor. Their electrical properties were investigated for potential uses in micro-electrical mechanical systems (MEMS) and anodes for lithium batteries. The microstructure and chemical composition was investigated by attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), Raman spectroscopy, and x-ray photoelectron spectroscopy (XPS); thermogravimetric analysis (TGA) provided insight into the thermal stability; and electrochemical impedance spectroscopy (EIS) into the electrical properties of the material. The increase of pyrolysis temperature and carbon content lead to an enhancement of the electrical conductivity, higher than previously reported values for intermediate pyrolysis temperature SiOC polymer derived ceramics. A limit of the amount of DVB that can be added to PHMS to produce a hybrid precursor has also been obtained.     

Investigation of thermal residual stresses during laser ablation of tantalum carbide coated graphite substrates using micro-Raman spectroscopy and COMSOL multiphysics

Laser ablation of high-temperature ceramic coatings results in thermal residual stresses due to which the coatings fail by cracking and debonding. Hence, the measurement of such residual stresses during laser ablation process holds utmost importance from the view of performance of coatings in extreme conditions. The present research aims at investigating the effect of laser parameters such as laser pulse energy, scanning speed and line spacing on thermal residual stresses induced in tantalum carbide-coated graphite substrates. Residual stresses were measured using micro-Raman spectroscopy and correlated with Raman peak shifts. Transient thermal analysis was performed using COMSOL Multiphysics to model the single ablated track and residual stresses were reported at low, moderate and high pulse energy regimes. The results showed that the initial laser conditions caused higher tensile residual stresses. Moderate pulse energy regime comprised higher compressive residual stresses due to off centre overlapping of the laser pulses. Higher pulse energy (250 μJ), higher scanning speed (1000 mm/s) and moderate line spacing (20 μm) caused accumulation of tensile residual stresses during the final stage of laser ablation. The deviation of experimental residual stresses from COMSOL numerical model was attributed to unaccounted additional stresses induced during thermal spraying process and deformation potentials in the numerical model.     

多晶硅表面金属催化化学腐蚀法制绒研究现状

在多晶硅太阳能电池的生产过程中, 金刚线切割技术(Diamond wire sawn, DWS)具有切割速度快、精度高、原材料损耗少等优点, 受到了广泛关注。金刚线切割多晶硅表面形成的损伤层较浅, 与传统的酸腐蚀制绒技术无法匹配, 金属催化化学腐蚀法应运而生。金属催化化学腐蚀法制绒具有操作简单、结构可控且易形成高深宽比的绒面等优点, 具有广阔的应用前景。本文总结了不同类型的金属催化剂在制绒过程中的腐蚀机理及其形成的绒面结构, 深入分析和讨论了具有代表性的银、铜的单一及复合催化腐蚀过程及绒面结构和电池片性能。最后对金刚线切割多晶硅片表面的金属催化化学腐蚀法存在的问题进行了分析, 并展望了未来的研究方向。     

Investigation on thermal conductivity and mechanical properties of Si3N4 ceramics via one-step sintering

High thermal conductivity Si₃N₄ ceramics were fabricated using a one-step method consisting of reaction-bonded Si₃N₄ (RBSN) and post-sintering. The influence of Si content on nitridation rate, β/(α+β) phase rate, thermal conductivity and mechanical properties was investigated in this work. It is of special interest to note that the thermal conductivity showed a tendency to increase first and then decrease with increasing Si content. This experimental result shows that the optimal thermal conductivity and fracture toughness were obtained to be 66 W (m K)^-1 and 12.0 MPa m^1/2, respectively. As a comparison, the nitridation rate and β/(α+β) phase rate in a static pressure nitriding system, i.e., 97% (MS10), 97% (MS15), 97% (MS20) and 8.3% (MS10), 8.3% (MS15), 8.9% (MS20), respectively, have obvious advantages over those in a flowing nitriding system, i.e., 91% (MS10), 91% (MS15), 93% (MS20) and 3.1% (MS10), 3.3% (MS15), 3.3% (MS20), respectively. Moreover, high lattice integrity of the β-Si₃N₄ phase was observed, which can effectively confine O atoms into the β-Si₃N₄ lattice using MgO as a sintering additive. This result indicates that one-step sintering can provide a new route to prepare Si₃N₄ ceramics with a good combination of thermal conductivity and mechanical properties.     

Investigation the effect of FeNiCoCrMo HEA addition on properties of B4C ceramic prepared by spark plasma sintering

In this study, monolithic B₄C and B₄C-based ceramics incorporating FeNiCoCrMo dual-phase (FCC and BCC) high entropy alloys (HEAs) were produced by spark plasma sintering (SPS). The effect of additives on the densification behavior, mechanical properties, microstructures, and phase evaluation of the samples were investigated. X-ray analysis confirmed the existence of FCC structured HEA and depletion of BCC structured HEA, after high-temperature reaction between B₄C-HEAs. The addition of HEAs enhanced the densification behavior by liquid phase sintering. Furthermore, hardness and fracture toughness values of the samples increased with increasing HEAs content. Fracture toughness and hardness values for all composites were higher than the monolithic B₄C. A combination of the highest density (∼99.22 %) and the best mechanical properties (32.3 GPa hardness and 4.53 MPa m^1/2 fracture toughness) was achieved with 2.00 vol.% HEA addition.