ZnO·2.7Al2O3 nanocomposite with high optical transparency

Here we report a transparent dual-phase ZnO·2.7Al₂O₃ ceramic. The composite is pore-free and consists of thin nanosheets with a spinel phase and a hexagonal phase, while the two phases match closely in both lattice and refractive index. Such features result in excellent optical transmittance (maximum value >80% in the visible spectrum) at comparable phase volume. This work may provide a new thought for the rational structural design of optical nanocomposites.     

Achieving fabrication of highly transparent Y2O3 ceramics via air pre-sintering by deionization treatment of suspension

An easy albeit quite effective deionization suspension treatment was adopted to alleviate the detrimental effects related to the hydrolysis of Y₂O₃ in an aqueous medium. Fabrication of highly transparent Y₂O₃ ceramics with a fine grain size via air pre-sintering and post–hot isostatic pressing (HIP) treatment without using any sintering additive was achieved using the treated suspensions. The hydrolysis issue of Y₂O₃ powder in an aqueous medium was effectively alleviated by using deionization treatment, and a well-dispersed suspension with a low concentration of dissolved Y³⁺ species was obtained. The dispersed suspensions were consolidated by the centrifugal casting method, and the green bodies derived from the suspension of 35.0 vol% solid loading showed an improved homogeneity with a relative density of 52.1%. Fully dense Y₂O₃ transparent ceramic with high transparency was obtained by pre-sintering consolidated green compacts at a low temperature of 1400°C for 16 h in air followed by a post-HIP treatment at 1550°C for 2 h under 200 MPa pressure. The sample had a fine average grain size of 690 nm. The in-line transmittance of the sample reached 83.3% and 81.8% at 1100 nm and 800 nm, respectively, very close to the theoretical values of Y₂O₃.     

Environmentally Friendly Graphene Inks for Touch Screen Sensors

Graphene-based materials have attracted significant attention in many technological fields, but scaling up graphene-based technologies still faces substantial challenges. High-throughput top-down methods generally require hazardous, toxic, and high-boiling-point solvents. Here, an efficient and inexpensive strategy is proposed to produce graphene dispersions by liquid-phase exfoliation (LPE) through a combination of shear-mixing (SM) and tip sonication (TS) techniques, yielding highly concentrated graphene inks compatible with spray coating. The quality of graphene flakes (e.g., lateral size and thickness) and their concentration in the dispersions are compared using different spectroscopic and microscopy techniques. Several approaches (individual SM and TS, and their combination) are tested in three solvents (N-methyl-2-pyrrolidone, dimethylformamide, and cyrene). Interestingly, the combination of SM and TS in cyrene yields high-quality graphene dispersions, overcoming the environmental issues linked to the other two solvents. Starting from the cyrene dispersion, a graphene-based ink is prepared to spray-coat flexible electrodes and assemble a touch screen prototype. The electrodes feature a low sheet resistance (290 Ω □⁻¹) and high optical transmittance (78%), which provide the prototype with a high signal-to-noise ratio (14 dB) and multi-touch functionality (up to four simultaneous touches). These results illustrate a potential pathway toward the integration of LPE-graphene in commercial flexible electronics.     

Preparation of transparent BaSO4 nanodispersions by high-gravity reactive precipitation combined with surface modification for transparent X-ray shielding nanocomposite films

BaSO₄ nanoparticles as important functional materials have attracted considerable research interests, due to their X-rays barrier and absorption properties. However, most of BaSO₄ nanoparticles prepared by traditional technology are nanopowders with broad size distribution and poor dispersibility, which may greatly limit their applications. To the best of our knowledge, the synthesis of transparent BaSO₄ nanodispersions was rarely reported. Here, we firstly present a novel and efficient method to prepare transparent and stable BaSO₄ nanodispersions with a relatively small particle size around 10 to 17 nm using a precipitation method in a rotating packed bed (RPB), followed by a modification treatment using stearic acid. Compared with the BaSO₄ prepared in a traditional stirred tank, the product prepared using an RPB has much smaller particle size and narrower size distribution. More importantly, by using RPB, the reaction time can be significantly decreased from 20 min to 18 s. Furthermore, the transparent BaSO₄-polyvinyl butyral nanocomposite films with good X-ray shielding performance can be easily fabricated. We believe that the stable BaSO₄ nanodispersions may have a wide range of applications for transparent composite materials and coatings with X-ray shielding performance for future research.     

Preparation of transparent Y2O3 ceramic via gel casting: Realization of high solid volume via surface modification

In this article, isocyanate was adopted to modify Y₂O₃ powder for the purpose of preparing transparent Y₂O₃ ceramics via gel casting. The modification could enhance the hydration resistance of Y₂O₃ powder through the steric hindrance effect. The coating mechanism can be proved by the infrared spectrum of the surface-modified Y₂O₃ powder. Modification could not only prevent Y₂O₃ particles from reacting with water, but also prevents agglomeration between particles. The viscosity of the slurry with a solid content of 52.7 vol% is only 0.48 Pa·s at the shear rate of 100 s⁻¹, which is suitable for preparing high-density compacts by gel casting. The transmittance of the sample (1840°C × 8 h, 1 mm thickness) at 1100 nm reaches 75%. The microstructure of the sintered body is dense with the average grain size of 6.5 μm without obvious impurities nor pores. Five mol% ZrO₂-doped Y₂O₃ transparent ceramic fairing with the diameter of 5 cm without defects was successfully fabricated by gel casting (52.7 vol% solid volume) and vacuum sintering (1840°C × 8 h).     

Fabrication of 0.24Pb(In1/2Nb1/2)O3-0.42Pb(Mg1/3Nb2/3)O3-0.34PbTiO3 transparent ceramics by conventional sintering technique

0.24Pb(In_1/2Nb_1/2)O₃-0.42Pb(Mg_1/3Nb_2/3)O₃-0.34PbTiO₃ transparent ceramics were fabricated by a conventional sintering technique. Through optimization of sintering conditions of calcination and sintering temperatures and time, the obtained ceramics showed high optical transmittance of 53% and 71% at light wavelengths of 1300 and 2000 nm, respectively. The ceramics showed a rhombohedral to tetragonal phase transition at ~120°C and a tetragonal to cubic phase transition at 222°C. These transition temperatures were higher than those of 0.67Pb(Mg_1/3Nb_2/3)-0.33PbTiO₃ ceramics. In addition, the ceramics had a ferroelectric hysteresis loop, a large piezoelectric constant d₃₃ of 407 pC/N, and a planar electromechanical coupling factor k_p of 52%. These results suggest that the transparent ceramics may be used as a temperature-stable, linear electro-optic material.     

Fabrication and characterizations of Cr3+-doped ZnGa2O4 transparent ceramics with persistent luminescence

0.5 at.% Cr:ZnGa₂O₄ precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa₂O₄ powders with an average particle size of 43 nm were obtained by calcining the precursor at 900℃ for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa₂O₄ ceramics with an average grain size of about 515 nm were prepared by presintering at 1150℃ for 5 h in air and HIP post-treatment at 1100℃ for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa₂O₄ ceramics with a thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa₂O₄ ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa₂O₄ transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m² after 30 min, which is far superior to that of Cr:ZnGa₂O₄ persistent luminescence powders.     

The effect of Nd3+ concentration on fabrication,microstructure, and luminescent properties of anisotropic S-FAP ceramics

Nd³⁺ doped strontium fluorophosphate (S-FAP), with chemical formula Sr₅(PO₄)₃F, nanopowders were prepared using the co-precipitation method. The prepared powders had no impurity phase with a grain size of about 30 nm and the doping limit of Nd³⁺ ions in strontium fluorophosphate is about 9 at.%. The morphology and particle size were determined by the doping concentration of Nd³⁺. Anisotropic Nd: S-FAP transparent ceramics with different Nd³⁺ doping concentrations were fabricated successfully by the simple hot-pressing method. The grain size of prepared S-FAP transparent ceramics decreased first and then increased with the increase of Nd³⁺ concentration. The 2 at.% Nd: S-FAP ceramic presented the highest optical transmittance at all wavelengths range. The characteristic transitions from the ground state to the excited states of Nd³⁺ ions were observed from the absorption spectra, and the absorption cross-section was calculated at 3.71 × 10^–20 cm². The influence of Nd³⁺ ion concentration on luminescence intensity and fluorescence lifetime was studied under 796 nm excitation. The strong emission of ⁴F_3/2→⁴I_9/2 transition in Nd: S-FAP was calculated by Judd–Ofelt (J-O) theory.     

Embedded Metal Oxide Plasmonics Using Local Plasma Oxidation of AZO for Planar Metasurfaces

New methods for achieving high-quality conducting oxide metasurfaces are of great importance for a range of emerging applications from infrared thermal control coatings to epsilon-near-zero nonlinear optics. This work demonstrates the viability of plasma patterning as a technique to selectively and locally modulate the carrier density in planar Al-doped ZnO (AZO) metasurfaces without any associated topographical surface profile. This technique stands in strong contrast to conventional physical patterning which results in nonplanar textured surfaces. The approach can open up a new route to form novel photonic devices with planar metasurfaces, for example, antireflective coatings and multi-layer devices. To demonstrate the performance of the carrier-modulated AZO metasurfaces, two types of devices are realized using the demonstrated plasma patterning. A metasurface optical solar reflector is shown to produce infrared emissivity equivalent to a conventional etched design. Second, a multiband metasurface is achieved by integrating a Au visible-range metasurface on top of the planar AZO infrared metasurface. Independent control of spectral bands without significant cross-talk between infrared and visible functionalities is achieved. Local carrier tuning of conducting oxide films offers a conceptually new approach for oxide-based photonics and nanoelectronics and opens up new routes for integrated planar metasurfaces in optical technology.