Effect of microstructural features on the corrosion behavior of severely deformed Al–Mg–Si alloy

The aim of this study was to determine the influence of severe plastic deformation processing and the changes in microstructure resulting therefrom on the corrosion resistance of an Al–Mg–Si alloy. The alloy was processed using incremental equal channel angular pressing, which caused a reduction in grain size from 15 to 0.9 µm. The grain refinement was accompanied by an increase in the number of grain boundaries and dislocations, and by changes in grain orientation. However, there was no change in the size and number of intermetallic particles, which presumably resulted in a constant number of galvanic couplings. Electrochemical experiments revealed only slight differences between the samples before and after processing. Higher potential transients/oscillations upon immersion and increased corrosion currents in the vicinity of corrosion potential point to slightly higher reactivity of the most refined material. This indicates that intermetallic particles are the most crucial microstructural elements in terms of corrosion resistance. Their impact exceeds that of grain boundaries, in particular, at the stage of corrosion initiation. The development of corrosion attack is controlled more by the microstructure of the matrix as the grain refinement resulted in a less pronounced corrosion attack in comparison with the coarse-grained sample.     

Investigation on thermal conductivity and mechanical properties of Si3N4 ceramics via one-step sintering

High thermal conductivity Si₃N₄ ceramics were fabricated using a one-step method consisting of reaction-bonded Si₃N₄ (RBSN) and post-sintering. The influence of Si content on nitridation rate, β/(α+β) phase rate, thermal conductivity and mechanical properties was investigated in this work. It is of special interest to note that the thermal conductivity showed a tendency to increase first and then decrease with increasing Si content. This experimental result shows that the optimal thermal conductivity and fracture toughness were obtained to be 66 W (m K)^-1 and 12.0 MPa m^1/2, respectively. As a comparison, the nitridation rate and β/(α+β) phase rate in a static pressure nitriding system, i.e., 97% (MS10), 97% (MS15), 97% (MS20) and 8.3% (MS10), 8.3% (MS15), 8.9% (MS20), respectively, have obvious advantages over those in a flowing nitriding system, i.e., 91% (MS10), 91% (MS15), 93% (MS20) and 3.1% (MS10), 3.3% (MS15), 3.3% (MS20), respectively. Moreover, high lattice integrity of the β-Si₃N₄ phase was observed, which can effectively confine O atoms into the β-Si₃N₄ lattice using MgO as a sintering additive. This result indicates that one-step sintering can provide a new route to prepare Si₃N₄ ceramics with a good combination of thermal conductivity and mechanical properties.     

Design and fabrication of lutetium aluminum silicate glass and nanostructured glass for radiation detection

Flexible scintillating fiber plays an important role in X-ray radiation monitoring and high-resolution medical imaging, while construction of scintillating fiber derived from the commercial material system meet with limited success. Here, we report the design and successful fabrication of the Ce-activated lutetium aluminum silicate glass, nanostructured glass, and fiber, and explore their scintillating properties. The scintillating glass with optimized composition and optical properties is determined. The crystallization behavior of lutetium aluminum silicate glass is studied and the nanostructured glass embedded with orthorhombic Lu₂Si₂O₇ phase is successfully constructed for the first time. Importantly, the crystalline layer thickness of the nanostructured glass can be finely tuned and ~172.89% enhancement in the scintillating performance can be achieved. Furthermore, the fiber with large sized core is fabricated and its radiation response properties are tested. The results show that it exhibits high sensitivity and its scintillating emission is lineally dependent on the X-ray power, indicating the potential application for radiation detection.     

High-temperature oxidation behavior of monolithic Zr3[Al(Si)]4C6 and its composite incorporating 30vol% ZrB2-SiC: Providing a basis for broadening the service temperature

To provide a basis for the high-temperature oxidation of ultra-high temperature ceramics (UHTCs), the oxidation behavior of Zr₃[Al(Si)]₄C₆ and a novel Zr₃[Al(Si)]₄C₆-ZrB₂-SiC composite at 1500 °C were investigated for the first time. From the calculation results, the oxidation kinetics of the two specimens follow the oxidation dynamic parabolic law. Zr₃[Al(Si)]₄C₆ exhibited a thinner oxide scale and lower oxidation rate than those of the composite under the same conditions. The oxide scale of Zr₃[Al(Si)]₄C₆ exhibited a two-layer structure, while that of the composite exhibited a three-layer structure. Owing to the volatilization of B₂O₃ and the active oxidation of SiC, a porous oxide layer formed in the oxide scale of the composite, resulting in the degradation of its oxidation performance. Furthermore, the cracks and defects in the oxide scale of the composite indicate that the reliability of the oxide scale was poor. The results support the service temperature of the obtained ceramics.     

Raman and X-ray photoelectron spectroscopy study on the influence of La2O3 on the melt structure of SiO2–CaO–Al2O3–MgO

In order to gain more insights into the influence of rare earth elements on the melt structure of SiO₂–CaO–Al₂O₃–MgO glass ceramics, Raman and X-ray photoelectron spectroscopy techniques were used to study the influence of La₂O₃ on the Si–O/Al–O tetrahedron structure within SiO₂–CaO–Al₂O₃–MgO–quenched glass samples in this study. Results showed that some Raman peak shapes at low frequencies (200–840 cm^?1) changed significantly after the addition of La₂O₃, compared to the high frequency (840–1200 cm^?1) region that corresponds to the [SiO₄] structure, suggesting that the depolymerization of the low-frequency T–O–T (T=Si or Al) structure was more prevalent with La³⁺ addition. Besides, the depolymerization extent of the Si–O/Al–O tetrahedral network varied when the melt composition altered. Most notably, depolymerization is the most significant at a low CaO/SiO₂ ratio (0.25) and a high Al₂O₃ content (8%). Meanwhile, La³⁺ can promote the transformation of Si–O–Si and Al–O–Al bonds to the Si–O–Al ones, thereby forming a complex ionic cluster network interwoven with Si–O and Al–O tetrahedrons.     

Corrosion behavior of under‐, peak‐, and over‐aged 6063 alloy: A comparative study

The mechanical property of age‐hardenable Al‐alloys is governed by the state of ageing, which determines the microstructure and consequently, their corrosion behavior which is a vital aspect for a number of applications. This article presents a comparative assessment of corrosion behavior of under‐, peak‐ and over‐aged Al‐Mg‐Si alloy. Corrosion characteristics have been determined via immersion tests in 0.1 M ortho‐phosphoric acid solution and intergranular corrosion (IGC) tests. Corroded surfaces are examined by field emission scanning electron micrographs‐energy dispersive spectroscopy and 3D optical profilometer. The obtained results reveal that the corrosion rate at a specific immersion time as well as the depth of IGC increases in the order for under‐, peak‐, and over‐aged states. Irrespective of the state of ageing, corrosion loss increases linearly but the rate of corrosion decreases rapidly with increasing immersion time. The dominant mode of corrosion in under‐aged alloy is identified as localized pitting, while peak‐aged is highly susceptible to IGC in contrast extensive pitting corrosion is observed for over‐aged alloy. The observed differences in corrosion behavior are explained considering characteristics of precipitates. Formation of β (Mg₂Si) in case of over‐aged alloy and presence of inclusions like AlFeMnSi particles are found to accelerate pitting corrosion.     

Precipitation location of secondary phase and microstructural evolution during static recrystallization of as-cast Ti-25V-15Cr-0.3Si titanium alloy

The microstructural evolution and precipitation location of the secondary phase of an as-cast Ti-25V-15Cr-0.3Si titanium alloy were investigated via isothermal compression experiments and heat treatment. The average aspect (length-to-width) ratio, average area and size of the grains at different heat treatment temperatures and holding time were analyzed and the effects of deformation and annealing time on the grain area and size were considered. It was found that the grain size was strongly influenced by the height reduction and holding time. Grain growth was significant when annealing time increased from 10 min to 2 h at 950 °C and height reduction of 30%; however, grain growth was minimal at annealing time between 2 and 4 h. Many dispersion particles were observed to form in continuous chains; the precipitation location was confirmed to be along initial grain boundaries, and the dispersion particles were identified to be Ti₅Si₃ phase by TEM.     

焊丝中Si元素含量对铝合金接头裂纹敏感性的影响规律及机理

使用扫描电镜、能谱、温度场实时采集等测试方法，研究了焊丝中Si含量对AA6063铝合金GMAW焊接头热裂纹敏感性的影响规律及机理. 结果表明，当焊丝为纯铝时，鱼骨试样的焊缝中心会出现细长的焊接裂纹；当焊丝中的Si含量为4.5% ~ 6%时，裂纹的长度变短，但是开裂距离明显增加；当焊丝中的Si含量达到11% ~ 13%时，试样焊缝无裂纹出现. 随着Si含量的不断提高，合金易出现裂纹的凝固温度区间先增大后减小；焊丝中Si含量的不同还会影响凝固后期金属液的流动性，使得焊缝晶界处的物相成分和形态都有明显的区别；同时，Si含量的提高会使得接头的冷却速度先增加后减小，从而导致应力状态改变，热裂纹敏感性先升高后降低.