Preparation and properties of nano-sized SnO2 powder

1　INTRODUCTIONSnO2isoneofthemainmaterialsusedingassensor.Becauseofthehumidityandgassensingfunction,itattractsmoreandmoreattentions.Butthepresentproblemishowtoimprovethestabilityandsensibilityofgassensor.Researchershavetakenmanymeasurestoresolvethisproble…     

超细Fe3O4粒子表面包覆酞菁钴性质研究

本文研究了合成载氧体的金属有机化学液相淀积法制造工艺，所得产物经ＴＥＭ、ＸＰＳ、Ｍｏｓｓ－ｂａｕｅｒ谱和Ｂ－Ｈ仪等手段，研究了它的结构和磁性能。实验表明，酞青钴以薄层形式包覆在Ｆｅ＿３Ｏ＿４的表面，封闭了Ｆｅ＿３Ｏ＿４的表面孔洞，稳定了Ｆｅ＿３Ｏ＿４的物相，增强了磁性能。     

孤岛油田西区聚合物驱开发研究

孤岛油田西区注聚区1997年3月投入注聚后，高渗层得到有效封堵，吸水剖面得到明显改善。注聚期间，通过实施注聚区外围水井降水或停注、油井放大生产压差和调整注聚井注入速度等开发措施，扩大了聚合物波及体积，聚合物驱取得了明显效果。     

FW调剖技术及应用

应用FW调剖技术有针对性地对 119口非钻停井区注水井采取了 4种精细调剖方案 ,对比了化学浅调剖应用前后注水井层间矛盾的缓解 ,纵向上吸水剖面的改善 ,注水量和吸水指数的变化及渗流能力的变化。结果表明 ,注水井化学浅调剖后 ,井区的连通油井明显受效 ,获得较高的增油量 ,水驱的开发效果得到改善。化学浅调剖可以有效地封堵高渗透层 ,扩大低渗透层注入水的波及体积 ,减缓注水井层间矛盾 ,实现了对注水井吸水剖面的有效调整 ,这对深化注水结构调整、挖掘各类油层潜力、提高储量动用程度有显著的效果。     

气液固三相相平衡热力学模型与计算方法

原油中含有大量的高分子有机固相物质，因此，要准确地描述油气体系相平衡，必须对气液固三相相平衡进行研究，在对高分子有机烃类沥青沉降机理有了一定的认识的基础上，提出了大的交互作用系数，可以描述沥青与原油中轻质不相容性的程度。根据对油气烃类混合物体系的一般性认识与提出的沥青组分特征化方法，导出了与之相应的有其自身特殊性的气液沥青三相相平衡物料平衡方程组，用考虑沥青沉降三相闪蒸数值算法，对沥青沉降进行有效的理化模拟计算，此外，结合实例分析，给出了沥青质参考逸度的计算，饱和压力和沉降量的拟合方法。     

高温预析出对Al-Zn-Mg系铝合金时效硬化和应力腐蚀的影响

研究了高温固溶后降温处理工艺对中强可使预析出LC52和7039铝合金的组织、时效硬化和应力腐蚀的影响。金相观察发现,高温预析出可优先在晶界处产生,并提高随后时效状态下晶界析出相的不连续分布程度,温度降低到一定程度晶内和晶界产生大量析出。合金拉伸性能和应力腐蚀结果表明,预析出在保持强度和塑性的同时,可提高抗应力腐蚀性能。而预析出温度降低,合金强度呈下降趋势。     

Continuous precipitation of calcium sulfate dihydrate from waste sulfuric acid and lime

Precipitation of calcium sulfate dihydrate, gypsum, from (i) a pure sulfuric acid/lime suspension and (ii) a waste sulfuric acid/lime suspension in a continuous pilot plant in the temperature range from 40 °C to 80 °C was studied. It was observed that in the case of waste sulfuric acid with a high content of Mg²⁺ and Fe²⁺ ions, several hours after the beginning of the precipitation, partial dissolution of the product and modification of the crystals from needle‐ and plate‐like to agglomerated structures occurred. It is suggested that the secondary changes occur due to the increased concentration of Mg²⁺ and Fe²⁺ ions in the reactor. Below 60 °C, and above 70 °C plate‐like and needle‐like single crystals respectively were formed. The mean size (d₅₀) of the crystals was found to increase with increasing temperature and decrease with the initial concentration of lime. Gypsum produced between 70 °C and 80 °C is suitable for further processing for construction plaster. In a precipitation process with pure sulfuric acid only single perfect needle‐like crystals occurred. Copyright © 2005 Society of Chemical Industry     

服装低密度聚乙烯热熔胶化学粉碎的研究

服装粘合衬布的生产需要低密度聚乙烯热熔胶的微细粉末,介绍了对该热熔胶的化学粉碎技术所进行的实验研究,表明采用适当的助剂种类和用量以及适宜的工艺过程,通过化学粉碎可以得到合格的粉末产品。     

化学事故危害评估

根据化学事故危害的主要影响因素对化学事故进行危害评估,考查了危害纵深、人员杀伤率、危害地域估算、爆炸燃烧事故危害等内容。     

种分Δαk与种分首槽αk的关系

针对烧结法和拜尔法种分槽的 Δαk 变化进行了概述 ,阐述了种分 Δαk 与种分首槽 αk 的关系。