Electrooxidation reactions of methanol and ethanol on Pt–MoO3 for dual fuel cell applications

Pt–MoO₃ was synthesized by microwave-assisted chemical reduction. The physicochemical characterization showed that the electrocatalyst contained nanoparticles of Pt and clusters of MoO₃. The average particle size of the catalytic material was 2.5 nm. The electrochemical results showed that the Pt–MoO₃/C was suitable to carry out the electrooxidation reactions of ethanol and methanol indistinctly, avoiding CO poisoning. It was possible to compare the results with commercial Pt/C. The synthesized material showed a better electrochemical performance. Different simulations were performed using the Nernst equation to evaluate the influence of temperature, internal resistance, and the current density losses as a function of the fuel used. The theoretical results indicated that the electrical power of the mono-cell improves by 21.5% when the energy vector is changed from methanol to ethanol at the maximum power point, obtaining an electrical potential change ΔE = 87.02 mV and a variation of the electric power of Δp = 114.14 mW cm^?2. The use of dual fuels could improve the performance of experimental fuel cells.     

A 6-DOF humanoid wall-climbing robot with flexible adsorption feet based on negative pressure suction

A wide range of dangerous and special tasks have witnessed the applications of wall-climbing robots, but they still cannot adapt well torough or sloping walls. This paper proposes a 6-DOF (degree of freedom) humanoid wall-climbing robot (HWCR) based on the principle of negative pressure suction. HWCR has the advantages of flexible adsorption feet, strong adaptability, strong anti-subversion performance, and high friction to the wall. We deduce mechanics formulas and carry out a parametric design of the foot structure so that it can meet the requirement of robot wall climbing. We use Fluent to analyze the flow field of the adsorption foot and determine the motor speed that can provide a reliable adsorption force. Using the D-H matrix to plan gait, we also design a compound cycloid-based foot trajectory to reduce the impact between the HWCR and the wall. Experiments on the uneven wall and sloping wall show that the vehicle can walk with an ideal gait, and the resistance value of the servo on each joint is much lower than the critical value, which ensures the smooth movement of the HWCR.     

Synergistic regulation of hydrogen adsorption/desorption via dual interfaces of Cu/Ni/Ni(OH)2 toward efficient hydrogen evolution reaction

Nickel-based catalysts have attracted tremendous attention as alternatives to precious metal-based catalysts for electrocatalytic hydrogen evolution reaction (HER) in virtue of their conspicuous advantages such as abundant reserves and high electrochemical activity. Nevertheless, a great challenge for Ni-based electrocatalyst is that nickel sites possess too strong adsorption for key intermediates H1, which severely suppresses the hydrogen-production activities. Herein, we report a hierarchical architecture Cu/Ni/Ni(OH)₂ consisting of dual interfaces as a high-efficient electrocatalyst for HER. The Cu nanowire backbone could provide geometric spaces for loading plenty of Ni sites and the formed Ni/Cu interface could effectively weakened the adsorption intensity of H1 intermediates on the catalyst surface. Moreover, the H1 adsorption could be further controlled to appropriate states by in-situ formed Ni(OH)₂/Ni interface, which simultaneously promotes water adsorption and activation, thus both Heyrovsky and Volmer steps in HER could be obviously accelerated. Experimental and theoretical results confirm that this interface structure can promote water dissociation and optimize H1 adsorption. Consequently, the Cu/Ni/Ni(OH)₂ electrocatalyst exhibits a low overpotential of 20 mV at 10 mA cm^?2 and an ultralow Tafel slope of 30 mV dec^?1 in 1.0 M KOH, surpassing those of reported transition-metal-based electrocatalysts and even the prevailing commercial Pt/C.     

Synthesis of thermoresponsive copolymer/silica-coated magnetite nanoparticle composite and its application for heavy metal ion recovery

To enhance chemical stability and suppress of aggregation of magnetite nanoparticles (MNPs), which are used as a support for thermoresponsive copolymer immobilization, silica coating of the MNPs is applied via the electrooxidation method. Although the resulting silica coated-MNPs also formed aggregates, the size distribution of the aggregate shifted to smaller size range. Because of that, the surface area available for copolymer immobilization increased approximately 6.7 times at maximum as compared with that of the uncoated MNPs. It contributed to the increase of the amount of the immobilized copolymer on the silica-coated MNPs, which is approximately four times larger than that on the uncoated MNPs. Fe₃O₄ dissolution test confirmed enhancement of chemical stability of MNPs. The thermoresponsive copolymer immobilized on the silica-coated MNPs shows the ability to recycle Cu(II) ion from Cu(II) containing solution by changing temperature with significantly shorter time than those in other thermoresponsive adsorbents in gel form.     

Nano fibrillated cellulose-based foam by Pickering emulsion: Preparation,characterizations, and application as dye adsorbent

An ecofriendly and biodegradable porous structure was prepared from drying aqueous foams based on nano fibrillated cellulose (NFC), extracted from softwood pulp by subcritical water/CO₂ treatment (SC-NFC). The primary aim of this work was to use the modified SC-NFC as stabilizer for a water-based Pickering emulsion which upon drying, yielded porous cellulosic materials, a good dye adsorbent. In order to exploit the carboxymethylated SC-NFC (CMSC-NFC, with a degree of substitution of 0.35 and a charge density of 649 μeqv/g) as a stabilizer for water-based Pickering emulsion in subsequent step, an optimized quantity of octyl amine (30 mg/g of SC-NFC) was added to make them partially hydrophobic. A series of dry foam structures were prepared by varying the concentrations of treated CMSC-NFCs and 4 wt% was found to be the optimum concentration to yield foam with high porosity (99%) and low density (0.038 g/cc) along with high compression strength (0.24 MPa), superior to the conventionally extracted NFC. The foams were applied to capture as high as 98% of methylene blue dyes, making them a potential green candidate for treating industrial effluent. In addition, the dye adsorption kinetics and isotherms were found to be well suited with second order kinetics and Langmuir isotherm models.     

Microstructural and mechanical properties assessment of transient liquid phase bonding of CoCuFeMnNi high entropy alloy

The transient liquid phase (TLP) bonding of CoCuFeMnNi high entropy alloy (HEA) was studied. The TLP bonding was performed using AWS BNi-2 interlayer at 1050 °C with the TLP bonding time of 20, 60, 180 and 240 min. The effect of bonding time on the joint microstructure was characterized by SEM and EDS. Microstructural results confirmed that complete isothermal solidification occurred approximately at 240 min of bonding time. For samples bonded at 20, 60 and 180 min, athermal solidification zone was formed in the bonding area which included Cr-rich boride and Mn₃Si intermetallic compound. For all samples, the γ solid solution was formed in the isothermal solidification zone of the bonding zone. To evaluate the effect of TLP bonding time on mechanical properties of joints, the shear strength and micro-hardness of joints were measured. The results indicated a decrement of micro-hardness in the bonding zone and an increment of micro-hardness in the adjacent zone of joints. The minimum and maximum values of shear strength were 100 and 180 MPa for joints with the bonding time of 20 and 240 min, respectively.     

基于C#持久蠕变强度外推功能的实现

持久蠕变强度外推是预测材料在高温高压环境下工作寿命的有效方法。目前常用的外推方法有等温法和参数法。这两种方法都是通过在实验室中采用较短时间的试验，获取试验数据后，通过Excel或者MATLAB等数据处理软件进行数据的拟合处理和外推计算。这些数据归纳统计和数学建模的过程有时需要耗费试验人员的大量精力。介绍了持久蠕变强度外推的软件实现方法，该功能包含在持久蠕变试验设备配备的软件中，试验完成后，软件直接根据试验结果进行数据拟合和持久蠕变强度的外推计算，无需试验数据的统计和建模，大大提高了持久蠕变强度外推计算的效率。     

氯乙烯变温吸附装置的研究

介绍了采用变温吸附技术对氯乙烯进行干燥脱水的工艺流程及运行效果,阐述了变温吸附装置运行过程中出现的问题及相应的解决方法。     

Nanoraspberry-like palladium/spongy nickel oxide for electrooxidation of five light fuels

The spongy nickel oxide (SNO) was synthesized the solution combustion method. The SNO was selected as a promoter to boost the catalytic activity of nanoraspberry-like palladium (NRPd) toward electrooxidation of five light fuels (LFs): methanol, ethanol, formaldehyde, formic acid, and ethylene glycol. The X-ray powder diffraction, Fourier-transform infrared spectroscopy (FT-IR), scanning electron microscopy, and field emission scanning electron microscope techniques were used for the materials characterization. In comparison with nonpromoted Pd, the NRPd-SNO electrocatalyst shown an excellent efficiency in parameters like the electrochemical active surface area and anti-CO poisoning behavior. The turnover data and the parameters, including reaction order, activation energy, and the coefficients of electron transfer and diffusion, were evaluated for the each process of LFs electrooxidation. The outcome for NRPd-SNO activity toward LFs electrooxidation was compared to some reported electrodes. The SNO increases the removal of intermediates created in the oxidation of LFs that can poison the surface of palladium catalyst. This is due to the presence of the lattice oxygens in SNO structure and Ni switching between its high and low valances. The compatibility of the adsorption process of LFs on the surface of the NRPd-SNO catalyst with different isotherms was determined by studying the Tafel polarization and calculating the surface coverage.