软锰矿氧化硫化钡制高纯碳酸锰和氢氧化钡工艺研究

软锰矿同硫化钡溶液在较低温度下进行氧化还原反应，当硫化钡含量控制在26-75g／L范围内，软锰矿与硫化钡的物质的量比为2．5-3，反应时间50-60min，软锰矿被硫化钡还原为MnO，其还原率可达93．5％以上；还原后的锰用硫酸浸取，溶液经除杂后，与碳酸铵反应而制成高纯碳酸锰。硫化钡则被氧化为氢氧化钡，经蒸发、结晶而制得入水氢氧化钡，其回收利用率高速95％。     

硫化氢吸收液的电化学分解条件研究

理想的脱硫工艺应满足体积小、费用低、净化度高、无二次污染等要求。在碱性溶液吸收微量硫化氢时同步进行电解，可有效减小设备体积，并将硫化氢转变为氢气和硫磺，不产生恶性气味。为此，实验研究了温度、浓度、电流密度、pH值等因素对电解阳极过程的影响，确定了适宜的电解条件，并在该条件下进行了吸收实验。结果表明，在最佳电解条件下，硫化钠溶液能充分吸收天然气中经变压吸附提浓的硫化氢（800 mg/m³），吸收率大于99.9％。     

Enhanced Photoelectrochemistry in CdS/Au Nanoparticle Bilayers

Three different configurations of Au‐nanoparticle/CdS‐nanoparticle arrays are organized on Au/quartz electrodes for enhanced photocurrent generation. In one configuration, Au‐nanoparticles are covalently linked to the electrode and the CdS‐nanoparticles are covalently linked to the bare Au‐nanoparticle assembly. The resulting photocurrent, φ = 7.5 %, is ca. 9‐fold higher than the photocurrent originating from a CdS‐nanoparticle layer that lacks the Au‐nanoparticles, φ = 0.8 %. The enhanced photocurrent in the Au/CdS nanoparticle array is attributed to effective charge separation of the electron–hole pair by the injection of conduction‐band electrons from the CdS‐ to the Au‐nanoparticles. Two other configurations involving electrostatically stabilized bipyridinium‐crosslinked Au/CdS or CdS/Au nanoparticle arrays were assembled on the Au/quartz crystal. The photocurrent quantum yields in the two systems are φ = 10 % and φ = 5 %, respectively. The photocurrents in control systems that include electrostatically bridged Au/CdS or CdS/Au nanoparticles by oligocationic units that lack electron‐acceptor units are substantially lower than the values observed in the analogous bipyridinium‐bridged systems. The enhanced photocurrents in the bipyridinium‐crosslinked systems is attributed to the stepwise electron transfer of conduction‐band electrons to the Au‐nanoparticles by the bipyridinium relay bridge, a process that stabilizes the electron–hole pair against recombination and leads to effective charge separation.     

Scale Up from Small Oven-Drying Tests of Mineral Concentrate to Pilot-Scale Drying with a Heated Pad

While Fickian diffusion models are commonly used in other applications, there are few reports of them being applied to the batch drying of a mineral concentrate. Diffusion coefficients estimated from small-scale oven-drying tests were used to predict the drying behavior of a concentrate sample 1 m × 1 m in area and 50 cm deep, with a heated bottom pad. These pilot-scale tests included both daily turning of the sample and turning every three days. The excellent quantitative agreement between the predicted and observed pilot-scale behavior gives a high level of confidence in the model predictions and suggests that a Fickian diffusion model is adequate to predict the behavior of mineral concentrates at the low moisture contents used here.     

镍层耐硝酸腐蚀性测试——一种简单的预先探测ENIG镍层“黑盘”现象的测试方法

随着更加精细的SMT、BGA等表面贴装技术的运用,化学沉镍金(ENIG)作为线路板最终表面处理得到了越来越广泛的应用,同时可怕的“黑盘”现象也随之更广泛地“流行”起来,直接导致贴装后元器件焊接点不规则接触不良。为了贯彻执行最好的流程控制和采取有效的预防措施,了解这种焊接失败的产生机理是非常重要的,及早的观测到可能发生“黑盘”现象的迹象变得同样关键。本文介绍了一种简单的预先探测ENIG镍层“黑盘”现象的测试方法-镍层耐硝酸腐蚀性测试,这种测试可以用于作为一种常规的测试方法监测一般化学沉镍溶液在有效使用寿命范围内新鲜沉积的镍层的质量。利用Weibull概率统计分析在不同的金属置换周期(MTO)下镍层的可靠性能表现。结合试验结果得出了一个镍层耐硝酸腐蚀性的判定标准。     

湿硫化氢环境下的球罐腐蚀状况分析

在湿硫化氢环境下 ,尤其储存介质中的硫化氢含量超标时 ,很容易对储存容器壳体 (含焊缝和母材 )造成硫化氢应力腐蚀或氢鼓包。作者较仔细分析了 1 0 0 0m3 丙烯球罐产生硫化氢应力腐蚀开裂和40 0m3 LPG球罐产生氢鼓包的原因。提出了此类设备在设计选材、设备制造、施工安装和使用维护等环节应注意的问题。     

用硫酸铁铵容量法测定钛精矿中二氧化钛含量

样品在过氧化钠熔融、水浸取及盐酸酸化后，在盐酸和硫酸介质中，隔绝空气，用金属铝将钛(Ⅳ)还原至钛(Ⅲ)，以硫氰酸盐为指示剂，用硫酸铁铵标准溶液滴定。     

熔融碳酸盐燃料电池阴极材料的导电性

通过交流阻抗方法研究了熔融碳酸盐燃料电池阴极材料锂镍氧化物、锂钴氧化物和锂铁氧化物的导电性能。结果表明:锂镍氧化物电极的导电性最好,锂钴氧化物电极的导电性次之,锂铁氧化物电极的导电性最差;它们的导电性都随着温度的升高而按指数规律增加;在合成锂钴氧化物(或锂铁氧化物)的过程中,使Li2CO3轻微过量,可以提高锂钴氧化物(或锂铁氧化物)电极的导电性,而且在同一温度下,随着nLi∶nCo(或nLi∶nFe,摩尔比)值的增大,锂钴氧化物(或锂铁氧化物)电极的导电性显著增加。     

固定化微生物脱除工业酸性废气中H_2S的研究

以H 2软性填料作为氧化亚铁硫杆菌的固定化载体 ,构成了固定床生物反应器。在一定操作条件下 ,考察了固定床生物反应器对Fe2 +的氧化速率 ,最大可达 7.6 7g/ (L·h)。并对固定床生物反应器运行中在载体表面形成的络合物进行了研究 ,X射线衍射证明此络合物为黄钾铁矾 [KFe3(SO4 ) 2 (OH) 6]。