The effect of Co, Pd and Pt ultrathin films on the kinetics of the formation of Ni-silicide by reactive diffusion is investigated. 50 nm Ni/1 nm X/ 50 nm Ni (X?=?Co, Pd, Pt) deposited on Si(100) substrates are studied using in-situ and ex-situ measurements by X-ray diffraction (XRD). The presence of Co, Pd or Pt thin films in between the Ni layers delays the formation of the metal rich phase compared to the pure Ni/Si system and thus these films act as diffusion barriers. A simultaneous silicide formation (δ-Ni2Si and NiSi phases) different from the classic sequential formation is found during the consumption of the top Ni layer for which Ni has to diffuse through the barrier. A model for the simultaneous growth in the presence of a barrier is developed, and simulation of the kinetics measured by XRD is used to determine the permeability of the different barriers. Atom probe tomography (APT) of the Ni/Pd/Ni system shows that the Pd layer is located between the Ni top layer and δ-Ni2Si during the silicide growth, in accordance with a silicide formation controlled by Ni diffusion through the Pd layer. The effect of the barrier on the silicide formation and properties is discussed.
Aluminoborate glasses have recently been found to feature high resistance to crack initiation during indentation due to a highly flexible network structure. In cesium aluminoborate glasses, it has been found that the use of a simple post-treatment, namely aging in a humid atmosphere, can further improve this resistance. To better understand the mechanical properties of this glass family upon humid aging, we here study the effect of aging conditions on the structure and mechanical properties of Li,K,Cs-aluminoborate glasses. As expected, we find that higher humidity and longer aging time cause more pronounced permeation of atmospheric water into the glasses. Due to their denser structure and stronger modifier-oxygen bonds, the humid aging has a relatively smaller effect on the mechanical properties of Li- and K-containing glasses relative to Cs-containing glasses, with the latter achieving an ultrahigh crack resistance. We find that the humid aging leads to the formation of a hydration layer in the Cs-aluminoborate glass surface, with a thickness of around 26 μm upon aging at 23 °C with 40% relative humidity for 7 days. Moreover, a remarkable indentation behavior, that is, the observation of μm-sized shear bands inside the imprint of the Cs-glass upon aging at 60% relative humidity is reported. Taken as a whole, the work provides guidelines for how to control the humid aging rate as a function of relative humidity and temperature to form a hydration layer and thus achieve improved crack resistance in such glasses. 相似文献
In this study, air filter base paper (P) was used as the receiving substrate, polyvinyl alcohol (PVA) and PVA/multi-walled carbon nanotube (MWCNT) spinning solutions were used to prepare electrospun air filter papers (P-PVA and P-PVA/MWCNT, respectively). Then, P-PVA/MWCNT was calendered under different pressures. The effect of MWCNTs on the surface performance of P-PVA/MWCNT was explored and the influence of calendering technology on their structure and filtration characteristics was analyzed. Electron scanning microscope observation showed that the PVA nanofibers on the surface of P-PVA/MWCNT had no beading, and MWCNTs weakened the surface electrostatic phenomenon and had a good micromorphology. During the calendering process, with an increase in pressure, the mean pore size and surface roughness of P-PVA/MWCNT decreased, the initial resistance increased, and the filtration efficiency changed slightly. 相似文献