Matrix Manipulation of Directly-Synthesized PbS Quantum Dot Inks Enabled by Coordination Engineering

The direct-synthesis of conductive PbS quantum dot (QD) ink is facile, scalable, and low-cost, boosting the future commercialization of optoelectronics based on colloidal QDs. However, manipulating the QD matrix structures still is a challenge, which limits the corresponding QD solar cell performance. Here, for the first time a coordination-engineering strategy to finely adjust the matrix thickness around the QDs is presented, in which halogen salts are introduced into the reaction to convert the excessive insulating lead iodide into soluble iodoplumbate species. As a result, the obtained QD film exhibits shrunk insulating shells, leading to higher charge carrier transport and superior surface passivation compared to the control devices. A significantly improved power-conversion efficiency from 10.52% to 12.12% can be achieved after the matrix engineering. Therefore, the work shows high significance in promoting the practical application of directly synthesized PbS QD inks in large-area low-cost optoelectronic devices.     

一类非齐次退化抛物方程的零可控性

介绍了解的适定性、Carleman估计、可观测性不等式和最优控制概念,通过推导证明存在一个控制函数,使原方程的解在t=T时为零,说明此方程具有零可控性.     

非光滑凸问题投影型对偶平均优化方法的个体收敛性

对于一般凸问题,对偶平均方法的收敛性分析需要在对偶空间进行转换,难以得到个体收敛性结果.对此,文中首先给出对偶平均方法的简单收敛性分析,证明对偶平均方法具有与梯度下降法相同的最优个体收敛速率Ο(lnt/t).不同于梯度下降法,讨论2种典型的步长策略,验证对偶平均方法在个体收敛分析中具有步长策略灵活的特性.进一步,将个体收敛结果推广至随机形式,确保对偶平均方法可有效处理大规模机器学习问题.最后,在L1范数约束的hinge损失问题上验证理论分析的正确性.     

离子型稀土矿山淋洗及尾水富集试验研究

对浸矿后离子型稀土原地浸矿场采用清水进行淋洗，在184天的清水淋洗过程中，尾水氨氮值从最开始的507mg/L，降低至140mg/L，淋洗尾水pH4.52~3.10。淋洗尾水采用两级反渗透膜分离，既回收有价资源稀土，又能使出水氨氮达标。结果表明，产水氨氮浓度稳定低于15mg/L，对稀土的截留率高于98.25%，浓水中稀土离子平均浓度313.4mg/L，可进一步回收稀土资源。     

非对称独塔混合梁斜拉桥的异形索塔不同状态力学性能分析

以一座跨度为314 m的不对称混合梁独塔斜拉桥为工程背景,首选建立整体桥梁有限元模型研究了不同施工阶段的桥梁结构受力特征;再通过实体有限元分析了"佛手"型曲线性索塔锚固区的局部应力分布规律.结果表明:最大悬臂状态的桥塔最大位移和应力要明显大于桥塔自立状态和满堂支架状态;桥塔最大变形在塔顶第一个锚固区,约为0.742 m;锚固区混凝土塔应力分布规律为从上到下、顺桥向从左到右应力增大,施工和成桥阶段最大应力分别为70.1 MPa和76.2 MPa.     

魏斯氏菌的研究进展

对魏斯氏菌属的分离鉴定、生物学特性、耐酸特性、抑菌特性、产胞外多糖特性、益生特性、组学研究及其在食品与医药方面的应用进行了综述,并为魏斯氏菌属的开发利用提供了建议。     

Fabrication of high-efficiency Yb:Y2O3 laser ceramics without photodarkening

High-efficiency Yb:Y₂O₃ laser ceramics were fabricated using the vacuum-sintering plus hot isostatic pressing (HIP) without sintering additives. High-purity well-dispersed nanocrystalline Yb:Y₂O₃ powder was synthesized using a modified co-precipitation method in-house. The green bodies were first vacuum sintered at a temperature as low as 1430°C and then HIPed at 1450°C. Finally, the samples were air annealed at 800°C for 10 h. Although no sintering aids were used, full density of the samples with excellent optical homogeneity and an inline transmission of 80% at 400 nm could be obtained. Moreover, photodarkening phenomenon was not detected in the ceramics. Preliminary laser experiment with the fabricated ceramics in a two-mirror cavity has demonstrated 32 W continuous-wave (CW) output at ∼1077 nm with an optical-to-optical conversion efficiency of 58.2%. To the best of our knowledge, this is so far the highest CW output power and optical-to-optical conversion efficiency achieved with the Yb³⁺-doped sesquioxide ceramics in a simple two-mirror cavity.