Fabrication and properties of pressure-sintered reaction-bonded Si3N4 ceramics with addition of Eu2O3–MgO–Y2O3

Dense pressure-sintered reaction-bonded Si₃N₄ (PSRBSN) ceramics were obtained by a hot-press sintering method. Precursor Si powders were prepared with Eu₂O₃–MgO–Y₂O₃ sintering additive. The addition of Eu₂O₃–MgO–Y₂O₃ was shown to promote full nitridation of the Si powder. The nitrided Si₃N₄ particles had an equiaxial morphology, without whisker formation, after the Si powders doped with Eu₂O₃–MgO–Y₂O₃ were nitrided at 1400 °C for 2 h. After hot pressing, the relative density, Vickers hardness, flexural strength, and fracture toughness of the PSRBSN ceramics, with 5 wt% Eu₂O₃ doping, were 98.3 ± 0.2%, 17.8 ± 0.8 GPa, 697.0 ± 67.0 MPa, and 7.3 ± 0.3 MPa m^1/2, respectively. The thermal conductivity was 73.6 ± 0.2 W m^?1 K^?1, significantly higher than the counterpart without Eu₂O₃ doping, or with ZrO₂ doping by conventional methods.     

境外炼化工程项目投标竞争者分析报价策略

全球炼化工程总承包市场呈现出垄断竞争型特征,欧美和日韩国际工程公司由于技术和报价竞争力较强,一直占据本行业高端市场,中国炼化工程企业尚有差距.文章综合考虑投标报价阶段竞争者分析路径,提出了随机型和不完全信息静态博弈综合集成分析的投标报价最优决策模型,并以中东海湾地区某炼化工程总承包项目为例,进行多维度的实证分析,提出模型的有效性和可行性,为中国炼化工程企业"走出去"高质量发展提供有益的决策支持和信息参考.     

Spectral radiance reconstruction from trichromatic camera responses based on orthogonal test and regularized algorithm

Reconstruction of spectral information based on multi‐channel image system is a significant problem in color reproduction, detection, and recognition. A spectral radiance reconstruction from trichromatic digital camera responses is researched in this article. The mapping relationship between the trichromatic imaging system response and the incident spectral radiance is analyzed. Then, in order to remove the ill‐posedness of the problem, a regularized constraint solution model of spectral radiance reconstruction matrix is established. And the spectral radiance can be reconstructed by spectral radiance reconstruction matrices and trichromatic imaging system response. Finally, the spectral radiance reconstruction matrix is estimated by the system radiometric calibration experiment. The input radiance is offered by a LCD display. A 3‐factor and 9‐level orthogonal test is designed for the calibration experiment, and a test set of 24 colors is used for precision analysis. The results show that the average relative mean error of our method is 8.69%, it is lower than that of Wiener filtering method by 2.84%. The method can reconstruct spectral radiance information effectively.     

Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

微纳层叠聚丙烯腈凝胶流动特性的数值模拟研究

建立了层叠流道的三维模型和有限元网格模型，根据流变测试数据，采用Polymat对物料的黏度模型参数进行拟合，并利用Polyflow软件对聚丙烯腈（PAN）凝胶在层叠流道内的三维等温流动过程进行了数值模拟分析。研究发现，当入口流量增大时，层叠流道出口速度的不均匀性增加；沿流动方向流道内压力逐渐降低，并在出口处降低至同一最低值；流道进出口压力差与入口流量大小具有正相关性；在流道的中心截面上剪切速率分布均匀，波动较小。     

BS960E高强钢激光-电弧复合焊接头氢脆行为研究

氢脆具有很强的微观组织敏感性,威胁着各类高强结构材料的安全服役.采用激光-电弧复合焊工艺对BS960E型高强钢进行焊接,并对接头在原位电化学充氢的条件下进行慢应变速率(10-5s-1)拉伸试验,结合微观组织和断裂特征进行分析并对接头的氢脆行为进行研究.结果 表明,焊接热循环所形成的富马氏体中的细晶区可以使接头表现出一定的氢脆敏感性,马氏体较大的氢扩散系数和较低的氢溶解度以及氢在晶界上的快速扩散是引起接头对氢脆敏感的主要原因,通过控制焊接工艺参数可抑制焊接热循环所引起的马氏体转变量,能够降低BS960E型高强钢激光-电弧复合焊接头的氢脆敏感性.     

Performance analysis of bit error rate of data link system under pulse LFM interference in time-varying rayleigh channel

Wireless Networks - In such mobile platforms as ships and aircraft, the detection and reconnaissance devices are near to the communication facilities. When working at the same time, they will...     

Achieving fabrication of highly transparent Y2O3 ceramics via air pre-sintering by deionization treatment of suspension

An easy albeit quite effective deionization suspension treatment was adopted to alleviate the detrimental effects related to the hydrolysis of Y₂O₃ in an aqueous medium. Fabrication of highly transparent Y₂O₃ ceramics with a fine grain size via air pre-sintering and post–hot isostatic pressing (HIP) treatment without using any sintering additive was achieved using the treated suspensions. The hydrolysis issue of Y₂O₃ powder in an aqueous medium was effectively alleviated by using deionization treatment, and a well-dispersed suspension with a low concentration of dissolved Y³⁺ species was obtained. The dispersed suspensions were consolidated by the centrifugal casting method, and the green bodies derived from the suspension of 35.0 vol% solid loading showed an improved homogeneity with a relative density of 52.1%. Fully dense Y₂O₃ transparent ceramic with high transparency was obtained by pre-sintering consolidated green compacts at a low temperature of 1400°C for 16 h in air followed by a post-HIP treatment at 1550°C for 2 h under 200 MPa pressure. The sample had a fine average grain size of 690 nm. The in-line transmittance of the sample reached 83.3% and 81.8% at 1100 nm and 800 nm, respectively, very close to the theoretical values of Y₂O₃.     

Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.