Cyclic thermal shock resistance for MgAlON–MgO composites obtained with additions of spent MgO–C brick: Microstructure characteristics,thermal shock parameter and thermal shock mechanism

Thermal shock parameters (R, R''', R'''' and R_st) of MgAlON–MgO composites obtained with additions of spent MgO–C brick were calculated using measured mechanical properties and thermal expansion coefficient, determining their resistance to fracture initiation and crack propagation. The cyclic thermal shock experiments of MgAlON–MgO composites performed from 1398 K to ambient temperature indicate that as number of thermal shock cycle increases, retained strength ratio of MgAlON and MgAlON–4.2 wt%MgO sharply decrease and then keep constant, while that of MgAlON–10.5 wt%MgO and MgAlON–15.7 wt%MgO slowly decrease. The reason for the difference is that MgAlON and MgAlON–4.2 wt%MgO show low value of R''' and R'''', and high value of R and R_st. Moreover, precipitation of impurity containing Fe may play a positive role in improvement of thermal shock resistance of MgAlON–MgO composites. MgAlON?4.2 wt%MgO has the maximum retained strength (55 MPa) even after 5 thermal shock cycles, which is expected to be used in the metallurgical industry.     

快速近似计算Shapley值的归因解释方法

Shapley值归因解释方法虽然能更准确量化解释结果, 但过高的计算复杂度严重影响了该方法的实用性. 本文引入KD树重新整理待解释模型的预测数据, 通过在KD树上插入虚节点, 使之满足TreeSHAP算法的使用条件, 在此基础上提出了KDSHAP方法. 该方法解除了TreeSHAP算法仅能解释树结构模型的限制, 将该算法计算Shapley值的高效性放宽到对所有的黑盒模型的解释中, 同时保证了计算准确度. 通过实验对比分析, KDSHAP方法的可靠性, 以及在解释高维输入模型时的适用性.     

Manufacturing catalyst-coated membranes by ultrasonic spray deposition for PEMFC: Identification of key parameters and their impact on PEMFC performance

This study deals with the manufacturing of catalyst-coated membranes (CCMs) for newcomers in the field of coating. Although there are many studies on electrode ink composition for improving the performance of proton-exchange membrane fuel cells (PEMFCs), there are few papers dealing with electrode coating itself. Usually, it is a know-how that often remains secret and constitutes the added value of scientific teams or the business of industrialists. In this paper, we identify and clarify the role of key parameters to improve coating quality and also to correlate coating quality with fuel cell performance via polarization curves and electrochemical active surface area measurements. We found that the coating configurations can affect the performance of lab-made CCMs in PEMFCs. After the repeatability of the performance obtained by our coating method has been proved, we show that: (i) edge effects, due to mask shadowing - cannot be neglected when the active surface area is low, (ii) a heterogeneous thickness electrode produces performance lower than a homogeneous thickness electrode, and (iii) the origin and storage of platinum on carbon powders are a very important source of variability in the obtained results.     

Locating wind farm for power and hydrogen production based on Geographic information system and multi-criteria decision making method: An application

Hydrogen generation from renewable energy resources is considered as a suitable solution to solve the problems related to the energy sector and the reduction of greenhouse gases. The aim of this study is to provide an integrated framework for identifying suitable areas for the construction of wind farms to produce hydrogen. For this purpose, a combined method of Geographic Information System (GIS) and multi-criteria decision making (MCDM) has been used to locate the power plant in Yazd province. The GIS method in the present study consisted of two parts: constraints and criteria. The constraint section included areas that were unsuitable for the construction of wind farms to produce power and hydrogen. In the present study, various aspects such as physical, economic and environmental had been considered as constraints. In the criteria section, eight different criteria from technical aspects (including average wind speed, hydrogen production potential, land slope) and economic aspects (including distance to electricity grid, distance to urban areas, distance to road, distance to railway and distance to centers of High hydrogen consumption) had been investigated. The MCDM tool had been used to weigh the criteria and identify suitable areas. Analytic Hierarchy Process (AHP) technique was used for weighting the criteria. The results of AHP weighting method showed that economic criteria had the highest importance with a value of 0.681. The most significant sub-criterion was the distance to urban areas and the least significant sub-criterion was the distance to power transmission lines. The results of GIS-MCDM analysis had shown that the most proper areas were in the southern and central sectors of Yazd province. In addition, the feasibility of hydrogen production from wind energy had shown that this province had the capacity to generate hydrogen at the rate of 53.6–128.6 tons per year.     

C105管桩混凝土设计参数取值的探讨

通过试验得出了C105混凝土100 mm×100 mm×100 mm立方体非标准试件抗压强度换算系数以及C105混凝土的标准方差和强度变异系数。采用理论计算,得到了棱柱体抗压强度与立方体抗压强度的比值α_c1,并与试验实测平均值进行了比较,验证了理论计算方法的可行性。此外,通过对比分析,探讨了直接外延法和引用公式法两种C105混凝土设计参数计算方法的正确性,研究结果可为C105管桩混凝土的设计和应用提供参考。     

Thermal shock effects on the impact resistance,tolerance and flexural strength of alumina based oxide/oxide ceramic matrix composites

In this study the effects of thermal shock on the impact damage resistance, damage tolerance and flexural strength of Nextel 610/alumina silicate ceramic matrix composites were experimentally evaluated. Composite laminates with balanced and symmetric layup were gradually heated to 1200°C in an air-based furnace and held for at least 30 min before being removed and immersed in water at room temperature. The laminates were then subjected to low velocity impacts via a hemispherical steel impactor. The resultant damage was characterized non-destructively, following which the laminates were subjected to compression tests. Three-point bend tests were also performed to evaluate the effect of thermal shock on the flexural strength and related failure modes of the laminates. Thermally shocked laminates showed smaller internal damage and larger external damage areas in comparison to their pristine counterparts. For the impact energy and resultant damage size considered, the residual compressive strengths for the thermally shocked and pristine laminates were similar.     

Formation of single-crystalline BaTiO3 nanorods from glycolate by tuning the supersaturation conditions

We have studied peculiarities in the formation of single-crystalline barium titanate (BaTiO₃) nanorods from a glycolate-mediated complex via a single-step hydrothermal process under different supersaturation (S_R) conditions. X-ray diffraction (XRD) showed the formation of pure BaTiO₃ with an S_R of above 19. The tetragonality for the BaTiO₃ (c/a) reached 1.013 at S_R = 19–29 and dropped to 1.010 for S_R = 39. According to the transmission electron microscopy (TEM) and XRD analyses, the rod-shaped particles exhibited single crystallinity and crystal growth along the [001] plane. With scanning electron microscopy (SEM), the morphological evolution from a plate-shaped intermediate precursor (S_R = 6–9) to a rod-shaped product with an aspect ratio of 6–9 (S_R = 19–29), and to non-polar material with an irregular structure (S_R = 39), was observed. The negative slope, linear dependence of the particles’ width and length on the supersaturation level in the range S_R = 19–39 was established for the first time. The replacement of the prevailing crystallization mechanism from in-situ topotactic transformation into dissolution-precipitation above S_R = 19 was observed. It was shown that with a simple regulation of the S_R, the structural and morphological characteristics of the obtained BaTiO₃ nanoparticle can be effectively tuned.     

Fine-diameter Si–B–C–N ceramic fibers enabled by polyborosilazanes with N–methyl pendant group

Given the superior thermal stability and electromagnetic features, continuous Si–B–(C)–N ceramic fibers have displayed great potential to fulfill the increasing demand for the high-temperature structural and functional materials. Manufacture of such ceramic fibers depends heavily upon the design of processable polymer precursors. Herein, a class of polyborosilazanes (PBSZs) with high spinnability were created through a facile one-pot synthesis. The trade-off between spinnability and ceramic yield of PBSZs was overcome by using heptamethyldisilazane and hexamethyldisilazane as the co-condensing agents to polymerize silicon and boron chloride monomers. The optimal PBSZs can fabricate continuous Si–B–C–N fibers with homogeneous diameter of 7.9 ± 0.5 μm and high ceramic yield of 80 wt%. Experimental characterization and quantum chemical computation revealed the mechanistic pictures of the impact of pendant groups on the polycondensation, melt spinning, and pyrolyzing process. These insights improve our understanding of spinnable pre-ceramic polymers for exploiting high-performance nitride ceramic fibers.