Processing and properties of Nextel™ 720 fiber reinforced alumina-zirconia ceramic matrix composites

The continuous Nextel? 720 fiber-reinforced zirconia/alumina ceramic matrix composites (CMCs) were prepared by slurry infiltration process and precursor infiltration pyrolysis (PIP) process. The introduction of submicron zirconia powders into the aqueous slurry was optimized to offer comprehensively good sintering activity, high thermal resistance and good mechanical properties for the CMCs. Meanwhile, the zirconia and alumina preceramic polymers were used to strengthen the porous ceramic matrix through the PIP process. The final CMC sample achieved a high flexural strength of 200 MPa after one infiltration cycle of alumina preceramic polymer and thermal treatment at 1150 °C for 2 h. The flexural strength retention of the improved CMC sample was 104% and 89% respectively after thermal exposure at 1100 °C and 1200 °C for 24 h.     

风险矩阵法在A水泥工厂风险分级的应用初探

本文介绍“风险矩阵法”进行风险分级工作的基本思路，结合水泥厂的生产特点通过危险有害因素辨识，获得危险源分布情况，采用风险矩阵法对风险进行评估，按风险值将风险等级划分为重大风险、较大风险、一般风险和低风险，为水泥生产企业的安全风险分级工作提供参考。     

Unraveling specific role of carbon matrix over Pd/quasi-Ce-MOF facilitating toluene enhanced degradation

Metal organic frameworks (MOFs) derivatives represented by quasi-MOFs have excellent physical and chemical properties and can be applied for the catalytic combustion of volatile organic compounds (VOCs). In this work, Pd/quasi-Ce-BTC synthesized by simple one-step N₂ pyrolysis was applied to the oxidation of toluene, showing excellent toluene catalytic activity (T₉₀ = 175 °C, 30000 mL/(g·h)). Microscopic analyses indicate the formation and interaction of a carbon matrix composite quasi-MOF structure interface. The results show that the amorphous carbon matrix formed during the partial pyrolysis of Ce-BTC significantly improves the adsorption and activation capacity of toluene in the reaction, and constructs a reductive system to maintain high concentrations of Ce³⁺ and Pd⁰, which can facilitate the activation and utilization of oxygen in reaction. Quasi in-situ XPS proves that carbon matrix is indirectly involved in the activation and storage of oxygen, and Pd⁰ is the crucial active site for the activation of oxygen. Stability and water resistance tests display good stability of Pd/quasi-Ce-BTC. This work provides a potential method for designing quasi-MOF catalysts towards VOCs effective abatement.     

Predicting the mechanical properties of Cu–Al2O3 nanocomposites using machine learning and finite element simulation of indentation experiments

Micromechanics model, finite element (FE) simulation of microindentation and machine learning were deployed to predict the mechanical properties of Cu–Al₂O₃ nanocomposites. The micromechanical model was developed based on the rule of mixture and grain and grain boundary sizes evolution to predict the elastic modulus of the produced nanocomposites. Then, a FE model was developed to simulate the microindentation test. The input for the FE model was the elastic modulus that was computed using the micromechanics model and wide range of yield and tangent stresses values. Finally, the output load-displacement response from the FE model, the elastic modulus, the yield and tangent strengths used for the FE simulations, and the residual indentation depth were used to train the machine learning model (Random vector functional link network) for the prediction of the yield and tangent stresses of the produced nanocomposites. Cu–Al₂O₃ nanocomposites with different Al₂O₃ concentration were manufactured using insitu chemical method to validate the proposed model. After training the model, the microindentation experimental load-displacement curve for Cu–Al₂O₃ nanocomposites was fed to the machine learning model and the mechanical properties were obtained. The obtained mechanical properties were in very good agreement with the experimental ones achieving 0.99 coefficient of determination R2 for the yield strength.     

Piperine Targets Different Drug Resistance Mechanisms in Human Ovarian Cancer Cell Lines Leading to Increased Sensitivity to Cytotoxic Drugs

Our goal was to examine the anticancer effects of piperine against the resistant human ovarian cancer cells and to explore the molecular mechanisms responsible for its anticancer effects. Our study used drug-sensitive ovarian cancer cell line W1 and its sublines resistant to paclitaxel (PAC) and topotecan (TOP). We analyzed the cytotoxic effect of piperine and cytostatic drugs using an MTT assay. The impact of piperine on protein expression was determined by immunofluorescence and Western blot. We also examined its effect on cell proliferation and migration. We noticed a different level of piperine resistance between cell lines. Piperine increases the cytotoxic effect of PAC and TOP in drug-resistant cells. We observed an increase in PTPRK expression correlated with decreased pTYR level after piperine treatment and downregulation of P-gp and BCRP expression. We also noted a decrease in COL3A1 and TGFBI expression in investigated cell lines and increased COL3A1 expression in media from W1PR2 cells. The expression of Ki67 protein and cell proliferation rate decreased after piperine treatment. Piperine markedly inhibited W1TR cell migration. Piperine can be considered a potential anticancer agent that can increase chemotherapy effectiveness in cancer patients.     

Surface generation mechanism of ceramic matrix composite in ultrasonic assisted wire sawing

Ceramic matrix composites (CMC) are highly required in many fields of science and engineering. However, the CMC parts always have poor surface finish. This study attempts to improve cutting performance of CMC material by combing the advantages of ultrasonic assisted cutting and diamond wire sawing. Cutting force, surface roughness, machined edge and tool wear are analyzed based on experimental results. It shows that the oscillatory movement of tool edges provides positive effect on particle ejection and residual material reduction. Ductile chip formation can be achieved due to the small tip radius of grits. Obvious decrease in cutting force, surface roughness and tool wear are obtained. Moreover, burrs, fuzzing and fracture are reduced. Meanwhile, both the surface characteristics and shape accuracy are significantly improved. These results provide a valuable basis for application of ultrasonic assisted wire sawing and understanding of CMC cutting mechanisms.     

Thermoset IM-LSI-based C/C-SiC: Influence of flow direction and weld lines on microstructure and mechanical properties

The production of ceramic matrix composites (CMC) based on C/C-SiC is still very cost-intensive and therefore only economical for a few applications. The fabrication of the preforms involves many costs that need to be reduced. In this work, the shaping of the CFRP-preforms is realized by thermoset injection molding, which enables large-scale production. The polymeric matrix used is a multi-component matrix consisting of novolak resin, curing agent and lubricant. Six millimeter chopped carbon fiber with a proportion of 50 wt.% were used as a reinforcement. These ingredients are processed by an industrial equipment for compounding and injection molding in order to manufacture a CFRP demonstrator representing a brake disc. Test specimens are cut out of the demonstrator in different directions in order to investigate influences of flow direction and weld lines on microstructural and mechanical properties. Afterward, the CFRP samples were converted to C/C-SiC composites by the liquid silicon infiltration process. The article addresses the flow behavior of the compound during the injection molding and the building of the weld lines in the demonstrator. In addition, results of the directional dependence of the microstructural and mechanical properties within the fabricated disc in the different production steps are presented.     

Matrix Manipulation of Directly-Synthesized PbS Quantum Dot Inks Enabled by Coordination Engineering

The direct-synthesis of conductive PbS quantum dot (QD) ink is facile, scalable, and low-cost, boosting the future commercialization of optoelectronics based on colloidal QDs. However, manipulating the QD matrix structures still is a challenge, which limits the corresponding QD solar cell performance. Here, for the first time a coordination-engineering strategy to finely adjust the matrix thickness around the QDs is presented, in which halogen salts are introduced into the reaction to convert the excessive insulating lead iodide into soluble iodoplumbate species. As a result, the obtained QD film exhibits shrunk insulating shells, leading to higher charge carrier transport and superior surface passivation compared to the control devices. A significantly improved power-conversion efficiency from 10.52% to 12.12% can be achieved after the matrix engineering. Therefore, the work shows high significance in promoting the practical application of directly synthesized PbS QD inks in large-area low-cost optoelectronic devices.     

Multidirectional focus measure for accurate three-dimensional shape recovery of microscopic objects

Shape from focus (SFF) is a technique to recover the shape of an object from multiple images taken at various focus settings. Most of conventional SFF techniques compute focus value of a pixel by applying one of focus measure operators on neighboring pixels on the same image frame. However, in the optics with limited depth of field, neighboring pixels of an image have different degree of focus for curved objects, thus the computed focus value does not reflect the accurate focus level of the pixel. Ideally, an accurate focus value of a pixel needs to be measured from the neighboring pixels lying on tangential plane of the pixel in image space. In this article, a tangential plane on each pixel location (i, j) in image sensor is searched by selecting one of five candidate planes based on the assumption that the maximum variance of focus values along the optical axis is achieved from the neighborhood lying on tangential plane of the pixel (i, j). Then, a focus measure operator is applied on neighboring pixels lying on the searched plane. The experimental results on both the synthetic and real microscopic objects show the proposed method produces more accurate three-dimensional shape in comparison to conventional SFF method that applies focus measures on original image planes.     

Revealing the dimensional stability mechanisms of SiC/Al composite under long-term thermal cycling

Long-term thermal cycling causes irreversible dimensional changes of the material, which in turn affects the reliability of precision instruments. In this paper, dimensional stability mechanisms of SiC/Al composites during thermal cycling were revealed using high-precision thermal dilatometer, XRD and spherical aberration correction transmission electron microscope (Cs-TEM). First, how the factors including dislocations, internal stress and precipitates affect the dimensional change of SiC/Al composites were separately introduced. Then, the integrated effect of these factors affecting the dimensional stability of SiC/Al composites was further discussed. Among them, the integrated effect of dislocation-internal stress in SiC/pure Al composites leads to an increase in dislocation density and average lattice constant, which leads to an increase in dimensional change. The integrated effect of dislocation-internal stress-precipitates in SiC/2024Al composites leads to a decrease in the average lattice constant and some changes in the precipitation behavior (including the type, density and lattice constant of the precipitates), which ultimately leads to a decrease in dimensional change. The dimensional change of the two types of composites was semi-quantitatively estimated. Finally, the reasons for the significantly higher dimensional stability of the SiC/2024Al composites were given.