Effects of Neodymium Concentration on Optical Characteristics of Polycrystalline Nd:YAG Laser Materials

A neodymium-doped yttrium-aluminum garnet (Y₃A1₅O₁₂, YAG) (Nd:YAG) ceramic that contained 0.3–4.8 at.% neodymium additives and exhibited nearly the same optical properties as those of a single crystal was fabricated by a solid-state reaction method using high-purity powders. Although the integrated absorption intensity of the ²H_9/2+⁴F_5/2 bands simply increased as the neodymium concentration in the YAG ceramics decreased, the fluorescence intensity of the 2.4 at.% Nd:YAG ceramic was the strongest among Nd:YAG ceramics with various neodymium concentrations and a 0.9 at.% Nd:YAG single crystal. An oscillation experiment was performed on a continuous-wave (cw) laser with a diode-laser exciting system using those ceramics and the single crystal. The oscillation threshold and slope efficiency in that analysis were 309 mW and 28%, respectively, for the 1.1 at.% Nd:YAG ceramics and 356 mW and 40%, respectively, for the 2.4 at.% Nd:YAG ceramics. The lasing characteristics of the ceramics in the present work were superior to those of a 0.9 at.% Nd:YAG single crystal that was fabricated by the Czochralski (Cz) method.     

Stability,cure properties,and applicability as one part adhesives of systems of divalent metal salts of mono(hydroxyethyl) phthalate–anhydride–bisepoxide

Heterogeneous curable compositions of divalent metal salts of mono(hydroxyethyl) phthalate–anhydride–bisphenol A diglycidyl ether (BADG) systems were prepared by merely mixing these components at room temperature. Stability at room temperature and cure properties at high temperature of the compositions were investigated for evaluating their applicability as one part adhesive. It was found that the systems containing Mg were generally more stable than those containing Ca. Similarly, at 150°C the Ca-containing systems showed generally shorter gelation time than the Mg-containing ones, due to the fact that the Ca salt dissolves more rapidly and enters into the addition reaction with the anhydride, leading to the faster appearance of the catalytic activities of the Ca carboxylate group. Among the various combinations of components, the metal salt–succinic anhydride (SA)–BADG systems were stable at room temperature for more than 6 months and rapidly cured at high temperature, showing excellent adhesive properties. This result indicates that the SA-containing systems should be of interest in applications to one part adhesives.     

The cranial MRI in severe cerebral palsy: a comparative study with clinical data

The magnetic resonance examination was performed in 38 patients with severe cerebral palsy (CP; 15 males and 23 females) who had both motor delay (unable to move anywhere) and mental retardation (I. Q or D. Q below 30). Neuroimaging findings were compared with the CP type, etiology, and grade of understanding of language. Cranial magnetic resonance imagings (MRI) in CP were divided into five types. Type 1 : nine predominantly showed cyst-liked ventricles and periventricular hyperintensity on T2-weighted imaging (PVH) and only scarred basal ganglia and thalamus were visible. All suffered from neonatal asphyxia and the clinical type was rigospastic tetraplegia (RST). Type 2: eleven predominantly showed PVH and hyperintensity on T2-weighted (HT2) in basal ganglia and thalamus. All suffered from neonatal asphyxia and the clinical type was RST or rigospastic diplegia. Type 3: five showed PVH and three had cortical atrophy. All suffered from neonatal asphyxia and the clinical type was spastic diplegia. Type 4: four predominantly showed HT 2 in putamen and thalamus. Three had cortical atrophy. All suffered from neonatal asphyxia. The clinical type was athetotic CP (ATH). Type 5: nine predominantly showed HT 2 in globus pallidus. Four had cortical atrophy and two had hippocampal atrophy. All suffered from neonatal jaundice and the clinical type was ATH. All patients who suffered from neonatal asphyxia and spastic CP had MRI in PVH. All patients who suffered from neonatal asphyxia and ATH showed HT 2 in putamen and thalamus. Almost patients who suffered neonatal jaundice and ATH showed HT 2 in globus pallidus. With athetotic CP, cases with atrophy of the cerebral cortex or/and hippocampus were lower grade of understanding of language than no atrophy of both. The result of studies of MRI are in agreement with neuropathological findings.     

Sub-50-nm physical gate length CMOS technology and beyond usingsteep halo

Sub-50-nm CMOS devices are investigated using steep halo and shallow source/drain extensions. By using a high-ramp-rate spike annealing (HRR-SA) process and high-dose halo, 45-nm CMOS devices are fabricated with drive currents of 650 and 300 μA/μm for an off current of less than 10 nA/μm at 1.2 V with T_ox^inv =2.5 nm. For an off current less than 300 nA/μm, 33-nm pMOSFETs have a high drive current of 400 uA/μm. Short-channel effect and reverse short-channel effect are suppressed simultaneously by using the HRR-SA process to activate a source/drain extension (SDE) after forming a deep source/drain (S/D). This process sequence is defined as a reverse-order S/D (R-S/D) formation. By using this formation, 24-nm nMOSFETs are achieved with a high drive current of 800 μA/μm for an off current of less than 300 μA/μm at 1.2 V. This high drive current might be a result of a steep halo structure reducing the spreading resistance of source/drain extensions     

Design optimization of tall tubular lead/acid cells based on an analysis of the reaction distribution

In order to estimate the discharge performance of tall lead/acid cells (with tubular positives), changes in current and potential distributions with discharge progress were calculated with a computer on the basis of plate resistance and the current—potential—time relationship between small facing parts of positive and negative plates. The taller the cell, the larger the voltage drop along the plates. Thus, the discharge time became shorter despite a large amount of available active mass remaining in the bottom part of the plates.Various current-collector designs were evaluated, e.g., one with varying resistance at each height; a side conductor placed along the plates and connected to them at the top, centre and bottom, etc. Results revealed an optimum collector design with which the maximum discharge capacity could be obtained. Furthermore, it was shown that the side conductor markedly improved the discharge performance because the active mass near the connecting parts was appreciably used.     

Discharge behaviour of electrodeposited PbO2 and Pb electrodes

The discharge behaviour of electrodeposited lead dioxide and lead electrodes was investigated under various conditions; the surfaces of the discharged electrodes were observed with a scanning electron microscope. Both the positive and negative electrodes were passivated by a covering of deposited lead sulphate crystals. The amount of lead sulphate required for passivation depended on the size of the crystals.     

Co-crosslinking blend of incompatible polymers VI: Poly(vinyl chloride) toughened with polyethylene via a co-crosslinking technique

A binary blend which consists of two incompatible polymers such as poly(vinyl chloride) and polyethylene has been performed through a partial co-crosslinking reaction with peroxide to give a co-crosslinked blend with a uniform dispersion of small polyethylene particles and with an improved mechanical property. The results are obtained through the formation of a co-crosslinked product which acts as a potential solid phase dispersant as well as a well-bonded reinforcing interlayer on polyethylene particles uniformly dispersed in poly(vinyl chloride) matrix. The resulting blends (PVC/PE=10/90 wt) give carbon spherules of 0.5 to 1m diameter through pressure-carbonization at 650° C for 1 h.     

Microstructure and superconducting properties of rapidly-quenched copper-based alloys containing immiscible lead and bismuth elements

Copper-based superconducting alloys including finely dispersed f c c lead or h c p (Pb- Bi) particles in f c c copper matrix have been obtained by rapid quenching (Cu-M)_100-x Pb_x and (Cu-M)_100-x (Pb_0.6Bi_{0.4 x} (M = aluminium, silicon or tin;x < 10 at%) alloys containing immiscible elements such as lead and bismuth. The particle size and interparticle distance were about 30 to 130 nm and 20 to 200 nm for had particles and about 30 to 60 nm and 30 to 150 nm for (Pb- Bi) particles. The transition temperature,T _c, was in the range of 3.2 to 5.5 K for the Cu-M-Pb alloys and 6.2 to 6.3 K for the Cu-M-Pb-Bi alloys. Critical magnetic field,H _c2, and critical current density,J _c, for the later alloys were 0.47 to 0.93T at 4.2 K and 1.1 × 10⁵ to 2.7 × 10⁵ Am^–2 at zero applied field and 4.21 K. The mechanism of the appearance of such a soft-type superconductivity for the rapidly quenched copper-based alloys was discussed, and inferred to be due to the formation of a percolation path of a superconducting lead or Pb-Bi phase along the grain boundaries, sub-boundaries and/or tangled dislocations where the lead or Pb-Bi phase precipitated preferentially, rather than the proximity effect based on lead or Pb-Bi particles.     

Study on triazine thiols. IV. Action of triazine thiols and their metal salts to peroxide

Decomposition of t-butylhydroperoxide was retarded by triazine thiols and their zinc salts, but accelerated by the copper salts of triazine thiols as well as sulfur compounds such as dithiocarbamates and mercaptobenzothiazolates. Triazine thiols and their zine salts are effective antioxidants for polyethylene crosslinked with peroxide and containing copper, and for protecting epichlorohydrin vulcanizates against attack by “sour” or hydroperoxide-containing gasoline.