Eu3+‐doped glass as a color rendering index enhancer in phosphor‐in‐glass

A new method for improving color rendering index (CRI) and low correlated color temperature (CCT) in high‐power white‐light‐emitting diodes (WLEDs) is proposed. We used a configuration of phosphor‐in‐glass (PIG) and studied light output changes with the increment in concentration of yellow‐emitting Y₃Al₅O₁₂:Ce³⁺ (YAG:Ce³⁺) phosphor. The PIG was coupled on the top of blue‐light‐emitting diodes (LED) chip (465 nm). To compensate the lack of red emission in the phosphor, Eu³⁺‐doped tellurium glass with different europium content was employed as a red emitter. The suitable contents of YAG:Ce³⁺ and Eu³⁺ were 7.5 weight percent (wt%) and 3 mol percent (mol%), respectively. The CRI value went from 72 to 82, whereas the CCT was reduced from 24 933 to 6434 K. The proposed structure can improve CCT as well as CRI of WLEDs just by placing a glass on top.     

Dual color tuning in Ce3+-doped oxyfluoride ceramic phosphor plate for white LED application

Ceramic phosphor plates of cerium (Ce³⁺)-doped oxyfluoride were fabricated by the solid-state reaction method. These phosphors exhibit efficient emission, with the novel feature of color tuning by varying both the doping concentration and excitation wavelength. As the Ce³⁺ concentration increases, the excitation spectrum broadens by a factor of 1.6, and the excitation peak wavelength shifts from 390 to 435 nm, and there is a variation in excitation energy of ~ 10%. Luminescence spectrum of low Ce³⁺ concentration samples is tuned from blue to green with the change of excitation wavelength. The emission peak exhibits a shift of 58 nm into the red spectral region, varying the Ce³⁺ concentration from 0.05 to 0.1 mol% ; whereas this shift is only 6 nm when Ce³⁺ content changes from 0.25 to 1 mol%. Photoluminescence (PL) quantum yield has achieved 76%. The crystal structure was examined using X-ray diffraction to explain its possible influence on the redshift luminescence. A proof of concept of white LED was constructed using a 450 nm blue LED chip with an oxyfluoride phosphor plate, showing a luminous efficacy (LE) of 64 lm/W with a color rendering index of 74.     

Effect of BaF2 addition on luminescence properties of Er3+/Yb3+ co-doped phosphate glasses

Er~(3+)/Yb~(3+) co-doped phosphate glasses(P_2O_5-Al_2O_3-BaO-BaF_2-K_2O-Er_2O_3-Yb_2O_3) with varying BaF_2 content,were prepared by a conventional melt quenching technique and their spectroscopic properties were examined through the Raman, absorption, emission and decay measurements. Raman spectra(350-1400 cm~(-1)) of the Er~(3+)/Yb~(3+) co-doped phosphate glasses with varying BaF_2 content, were recorded upon laser excitation at 785 nm. Near infrared luminescence spectra were measured in the1400-1600 nm region under 970 nm diode laser excitation and characteristic band was observed at1533 nm corresponding to ~4Ⅰ_(13/2)→~4Ⅰ_(15/2) transition of Er~(3+) ion. The decay curves for the ~4Ⅰ_(13/2) level of Er~(3+)ion, were measured and the lifetime is found to decrease from 7.94 to 7.70 ms when BaF_2 content increases from 0 to 8 mol% and then increases up to 7.83 ms with further increase in BaF_2 content(12 mol%). The emission cross-section.lifetime and figure of merit for the ~4Ⅰ_(13/2)→~4Ⅰ_(15/2) transition of Er~(3+) ion were evaluated and compared to the other host matrices. The upconversion luminescence was measured and intense red emission was observed for all the studied samples.