The Experiments of Modulated Toroidal Current were done on the HT-6M tokamak and HT-7 superconducting tokamak. The toroidal current was modulated by programming the Ohmic heating field. Modulation of the plasma current has been used successfully to suppress MHD activity in discharges near the density limit where large MHD m = 2 tearing modes were suppressed by sufficiently large plasma current oscillations. The improved Ohmic confinement phase was observed during modulating toroidal current (MTC) on the Hefei Tokamak-6M (HT-6M) and Hefei superconducting Tokamak-7 (HT-7). A toroidal frequency-modulated current, induced by a modulated loop voltage, was added on the plasma equilibrium current. The ratio of A.C. amplitude of plasma current to the main plasma current △Ip/Ip is about 12% ~ 30%. The different formats of the frequency-modulated toroidal current were compared. 相似文献
2.
以ZL114A合金舱段壳体铸件为研究对象,对其铸造工艺进行设计,并通过相关的数值模拟和工艺试验分析,确定了局部激冷及较高压差下凝固的舱段壳体低压铸件工艺方案和工艺参数。对低压铸造成形ZL114A合金舱段壳体铸件的窗口部位进行剖切取样测试分析,发现经固溶和双级时效处理后,其抗拉强度为349 MPa,屈服强度为288 MPa,伸长率为7.7%,达到了设计要求。 相似文献
3.
4.
5.
6.
研究了预时效温度和时间对ZL114A合金微观组织和力学性能的影响。结果表明:低温预时效温度和时间对ZL114A合金的组织有着一定影响,预时效工艺为110℃×2 h的合金组织中α-Al枝晶细化,共晶硅相呈细小的颗粒状均匀弥散地分布于枝晶和二次枝晶间。低温预时效温度和时间对ZL114A合金的各项力学性能有一定的影响,预时效工艺为110℃×1 h的ZL114A合金抗拉强度最大,达到331.7 MPa,伸长率最好,达到11%。110℃×2 h预时效工艺的ZL114A合金屈服强度最大,为266 MPa,较未预时效处理合金的屈服强度提高了65 MPa,提升幅度为32%,将低温预时效与正常热处理工艺相配合,可有效提高ZL114A合金的质量和生产效率。 相似文献
7.
8.
针对某航空厂采用传统砂型铸造试制盒子铝铸件存在的周期长、铸件表面质量差、尺寸精度难以满足要求及成品率低等问题,采用ProCAST进行了铸造工艺数值模拟优化,及选区激光烧结(SLS)直接制备其整体覆膜砂型/砂芯,在5天内完成了铸造工艺方案优化及2件铸件的浇注,得到了冶金质量好、几何尺寸合格、表面粗糙度(Ra)为6.3μm及尺寸精度为CT6~8级的复杂曲面盒子铝铸件,完全满足使用要求,实现了航空盒子铝铸件的精密砂型快速铸造。 相似文献
9.
10.
结合真空差压铸造特点,采用专业流体软件ANSYS Fluent中标准是k-ε模型对铝合金真空差压充型过程进行数值模拟,对某复杂薄壁铝合金壳体铸件进行了试制,并对模拟结果进行了验证与讨论.充型模拟结果表明,随着真空压力降低,真空度越高,铝合金液态金属的充型速度加快,充填形态更为平稳,无明显波动现象;在真空度为20 kPa时,铝合金铸件充型完整,卷气和裹气现象明显减少.实际结果与充型过程的模拟预测相符合. 相似文献