4.
5.
采用有机泡沫前驱体浸渍工艺制备Al2O3泡沫金属复合陶瓷.通过涂覆处理获得缺陷较少、结构均匀的泡沫金属复合陶瓷;采用Ni(NO3)2·6H2O液相包覆+氢气热还原技术对泡沫金属复合陶瓷体表面进行金属化处理.采用SEM、EDS研究了含镍泡沫陶瓷体的结构及金属化处理后的表面形貌.结果表明,镍颗粒均匀地分布在泡沫陶瓷骨架内部,骨架中心宏观孔保持通孔;经包覆处理后,金属层较均匀地附着于陶瓷表面. 相似文献
6.
采用SRV摩擦磨损试验机研究了球墨铸铁及三维网络Al2O3增强球墨铸铁基复合材料的干摩擦磨损性能,测量了球墨铸铁和复合材料在不同摩擦频率及载荷下的摩擦系数和磨损率;用扫描电镜观察磨损表面形貌,并分析了三维网络Al2O3对复合材料磨损机制的影响.结果表明:陶瓷与金属基体之间具有良好界面结合的三维网络Al2O3/球墨铸铁复合材料,其摩擦系数随载荷和摩擦频率的变化保持稳定;复合材料的耐磨性能远优于球墨铸铁,而且随着摩擦频率和载荷的增加,复合材料的抗磨损性能明显提高.这是由于复合材料中陶瓷与金属相之间三维空间结构和良好的界面结合有利于摩擦载荷的传递;金属基体中的石墨减摩作用保持摩擦系数的稳定;三维陶瓷骨架在磨损表面形成硬的微突体并起承载作用,制约了基体的塑性变形和高温软化,有利于磨损表面氧化膜的留存. 相似文献
7.
料浆包渗温度对渗Si层组织结构和性能的影响 总被引:1,自引:0,他引:1
纯铜表面预镀Ni,随后采用料浆包渗法,以SiO2粉为Si源,纯Al粉为还原剂,NaF和NH4Cl作为复合活化剂,Al2O3为惰性添加剂,蛋白质(鸡蛋清)为黏结剂,在Cu表面预先镀Ni层随后料浆包渗制备渗层。研究了包渗温度对渗Si层组织和力学性能的影响。结果表明:随包渗温度的增加,渗层组织出现以下转变:Ni31Si12→Ni31Si12+Ni2Si→Ni31Si12+Ni2Si+NiAl,包渗过程由渗Si为主转变为Si-Al为主;渗层硬度降低;摩擦因数由750℃时的0.17增加到950℃时的0.33。 相似文献
8.
为探明煅烧凝灰岩对水泥水化产物的影响,借助X射线衍射(XRD)、热重分析(TG)、傅里叶变换红外光谱(FTIR)等测试方法,分析了700℃下煅烧不同时间后凝灰岩的矿物组成及其对水泥水化产物和硬化体孔结构的影响.结果表明:煅烧后凝灰岩中的沸石水、结构水和吸附水被脱除,斜发沸石等沸石矿物架状结构发生破坏,形成无定形的SiO2和Al2O3;煅烧凝灰岩有助于水泥中的水化硅酸钙(C-S-H)、钙矾石(AFt)和单硫型水化硫铝酸钙(AFm)形成,且降低了C-S-H的钙硅比(n(Ca)/n(Si)),消耗了Ca(OH)2,水泥更易发生碳化;水化28 d后,煅烧凝灰岩水泥的孔隙率降低,孔径分布更细,从而提高了水泥强度. 相似文献
9.
A new style Ni-containing alumina ceramic foam based continuous three-dimensional interconnected skeleton was prepared by impregnating a polymeric sponge with aqueous ceramic slurry.Subsequently,alumina ceramic foam/steel metal matrix composites(MMCs) were prepared successfully by sand mold casting technique.The microstructure and mechanical properties of MMCs were investigated by SEM,EDS and compressive test.The results show that the depth of infiltration is about 40 μm to the bonding interface of ceramic/steel and the fracture strength σmax and plastic strain limit εp of composite are 520 MPa and 11.2%,respectively.The fretting wear mechanism of MMCs is mainly performed at the oxidative wear mode with lower load/friction frequency and the predominant oxidation wear together with slight adhesive wear and abrasive wear multiple mode with higher load/ friction frequency.Moreover,the infiltration bonding and continuous three-dimensional interconnected ceramic skeleton play a vital role in the stability of the bonding interface and excellent mechanical properties. 相似文献
10.
定向凝固制备CuAlNi形状记忆合金的研究 总被引:3,自引:2,他引:3
利用定向凝固设备,经过母合金的二次熔炼,可制备出具有柱状组织的CuAlNi形状记忆合金,并找到了在该试验装备下的最佳工艺参数。通过化学成分分析、DSC分析,得到该合金的成分及相变点,金相观察可以看到典型的柱状晶,记忆性试验比较了单晶,普通铸造、定向凝固组织的循环疲劳次数;分析了具有柱状组织的CuAlNi合金记忆性提高的原因。定向凝固组织可提高塑性加工性能、记忆稳定性、冷热循环次数,消除纵向晶界。 相似文献