Al2O3包覆改善P2型Na2/3Fe1/2Mn1/2O2正极材料的存储性能

采用超声喷雾热解与高温固相烧结相结合的方法合成P2型Na_2/3Fe_1/2Mn_1/2O₂材料。通过X射线衍射仪、扫描电子显微镜和电化学充放电设备对材料的结构、形貌和电化学性能进行全面的表征。此外,在Na_2/3Fe_1/2Mn_1/2O₂表面包覆Al₂O₃薄层,该包覆层可以抑制Na₂CO₃·H₂O的形成,提高Na_2/3Fe_1/2Mn_1/2O₂材料的存储性能,从而改善其电化学性能。这种简单的表面改性方法为合成高性能钠离子电池正极材料提供了新思路。     

锂离子电池用LiVPO4F/C基正极材料的制备和性能（英文）

将H2C2O4·2H2O,NH4H2PO4,NH4VO3和LiF通过球磨反应、烧结,合成了LiVPO4F/C基正极材料。在这个过程中,草酸起还原剂和碳源的作用,利用热重、X射线衍射、扫描电镜、透射电镜和碳-硫分析等手段对合成的前驱体和材料进行检测和分析。XRD分析表明,球磨反应后所得到的前驱体为无定形态,而烧结后的材料中除了LiVPO4F的衍射峰外,还存在Li3V2(PO4)3和V2O3衍射峰。材料颗粒均匀,尺寸约2μm。透射电镜分析表明,合成的材料颗粒表面包裹着一层约2nm厚的无定形碳。在截止电压3.0～4.4V时,合成的材料在0.1C和10C倍率下的放电比容量分别为151.3和102.5mA·h/g。在10C倍率下循环50次后容量保持率为90.4%。在LiVPO4F和Li3V2(PO4)3的循环伏安曲线中可以明显看到V3+/V4+的氧化还原峰。     

快速共沉淀过程pH值对Ni_(0.8)Co_(0.1)Mn_(0.1)(OH)_2及LiNi_(0.8)Co_(0.1)Mn_(0.1)O_2性能的影响

采用快速共沉淀法制备Ni0.8Co0.1Mn0.1(OH)2前驱体,利用前驱体与LiOH.H2O的高温固相反应得到锂离子电池层状正极材料LiNi0.8Co0.1Mn0.1O2,探讨pH值对材料结构和电化学性能的影响。通过X射线衍射(XRD)、扫描电镜(SEM)和电化学测试对合成样品进行表征。结果表明,pH值为11.00~12.00时,合成的Ni0.8Co0.1Mn0.1(OH)2前驱体均无杂相;pH值为11.50时,合成的前驱体制备出的正极材料具有良好的电化学性能,0.1C倍率下首次放电比容量为192.4 mA.h/g;经过40次循环,容量保持率为91.56%。     

氯化焙烧-水浸法从锂云母矿提锂(英文)

采用氯化焙烧-水浸法处理锂云母矿,并对氯化处理温度、时间、氯化剂的类型及用量进行研究。条件优化实验表明,在锂云母、氯化钠、氯化钠的质量比为 1:0.6:0.4,氯化处理温度为 880 °C,氯化处理时间为 30 min时,锂的提取率可达 92.86%,钾、铷、铯的提取率分别为 88.49%、93.60%和 93.01%,。采用 XRD 对锂云母原矿及焙烧后物料的物相进行分析。XRD 结果分析表明,当将锂云母和混合氯化剂一起焙烧(氯化钙及氯化钠)时,所得物相为 SiO2、CaF2、KCl、CaSiO3、CaAl2Si2O8、NaCl 和 NaAlSi3O8。     

Physicochemical properties of a novel composite polymer electrolyte doped with vinyltrimethoxylsilane-modified nano-La2O3

Nano-La2O3 was modified with the vinyltrimethoxylsilane by hydrolysis and a novel poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) based composite polymer electrolyte doped with the modified nano-La2O3 was prepared by phase inversion method. The physicochemical properties were studied by SEM, FT-IR, XRD, TG and electrochemical methods. The results of FT-IR indicated that the nano-La2O3 was successfully modified with vinyltrimethoxylsilane. The XRD analysis showed that the incorporation of modified nano-La2O3 into the polymer electrolyte membranes could effectively reduce the crystallinity of PVDF-HFP, and the characterizations also suggested that thermal stability and electrochemical stability window could reach to 382°C and 5.1V, respectively; the reciprocal temperature dependence of ionic conductivity followed Vogel-Tamman-Fulcher (VTF) relation, ionic conductivity at room temperature was up to 3.5×10-3S/cm and lithium ions transference number was up to 0.42; the interfacial resistance increased at initial value about353Ω/cm2 and reached a steady value about 559Ω/cm2 after 5d storage at 30°C. The fabricated Li/As-prepared electrolytes/LiCoO2 coin cell showed excellent rate and cycle performances.     

废旧磷酸铁锂电池高值回收制备磷酸铁锂材料

针对传统湿法冶金回收废旧磷酸铁锂电池存在含磷废水排放量大、产品附加值低等问题，提出一种还原酸浸-沉淀-固相再生回收废旧磷酸铁锂正极材料的新方法。区别于传统氧化酸浸，本研究在浸出过程中加入有机还原剂，将铁元素以Fe²⁺的形式浸出到溶液中；然后，通过控制pH值制备Fe₃(PO₄)₂·8H₂O，以此作为再生LiFePO₄正极材料的前驱体，避免了后续混锂烧结过程中Fe³⁺还原不彻底、再生磷酸铁锂纯度低等问题。结果表明：通过控制浸出条件，Li⁺和Fe²⁺的浸出率分别达到98.15%和98.10%。利用氨水调控浸出液pH值，沉淀出形貌为一次片状簇拥成团状结构的Fe₃(PO₄)₂·8H₂O前驱体；最后，将Fe₃(PO₄)₂·8H₂O...