智能型抗震耐火钢Q420FRE焊接热影响区组织性能研究

采用Gleeble3800热模拟试验机对智能型抗震耐火钢Q420FRE焊接热影响区组织转变行为进行了研究。结果表明,在不同的焊接热循环条件下,Q420FRE焊接热影响区的组织均以粒状贝氏体为主,硬度变化不大,硬度平均值为HV0.2 185~207。随着冷却速度的减小,贝氏体铁素体板条宽度略有增加,从2.38μm增大到3.28μm;M-A组元含量先增大到2.32%,之后逐渐减少到0.80%;M-A组元尺寸变化不大,当t_(8/5)30 s时,约为1.25~1.28μm;当t_(8/5)50 s时,约为1.00~1.05μm。焊接热影响区组织的稳定性决定了智能型微合金化Q420FRE耐火钢具有优良的焊接性,可适用于大热输入量焊接。     

超低碳超高强X120管线钢焊接热影响区粗晶区的组织转变

采用热模拟试验方法分析了超低碳超高强X120管线钢焊接热影响区粗晶区的组织转变.粗晶区连续转变曲线（SH-CCT）表明,在较宽的冷却速度范围内（0.8～25℃/s）,X120管线钢粗晶区组织为贝氏体;当冷却速度小于0.8℃/s和大于25℃/s时,分别有少量准多边形铁素体和少量马氏体形成.热模拟焊接热输入在12～25 kJ/cm的范围时,粗晶区组织为贝氏体;硬度（276～297 HV 0.2）与室温冲击吸收功（208～225 J）稳定.结果表明,X120管线钢可适用较大范围热输入的焊接,这主要与超低碳设计有关.     

Q345FRE高铌耐火钢模拟焊接热影响区高温拉伸性能

采用热模拟方法,在Gleeble-3500试验机上进行了Q345FRE耐火钢在单道次不同峰值温度、多道次不同峰值温度、不同t_(8/5)时间下热影响区的600℃高温拉伸试验,研究了不同状态下热影响区的高温拉伸性能、二次高温拉伸及其变化规律。研究结果表明,在单道次和双道次的焊接热影响区中,模拟峰值温度870℃的不完全重结晶区,其600℃的高温屈服强度和抗拉强度最低;模拟峰值温度1 320℃的粗晶区,其600℃高温屈服强度和抗拉强度最高且高于母材的强度;模拟不完全结晶区,焊接热输入(t_(8/5)时间)对600℃高温屈服强度和抗拉强度的影响无明显规律,且当t_(8/5)≤80 s时,二次过火的热模拟不完全结晶区的强度没有降低。     

亚温淬火工艺对低碳低合金高强钢组织及性能的影响北大核心CSCD

对低合金高强钢分别进行淬火+回火(QT)热处理和淬火+两相区的亚温淬火+回火(QLT)三段式热处理,采用光学显微镜(OM)、扫描电镜(SEM)、电子背散射衍射(EBSD)方法等观察分析其显微组织形貌、组成相和大角度晶界的密度分布,并测试其力学性能。结果表明:相比于QT工艺,低合金高强钢在QLT工艺后,强度虽稍有下降,但低温冲击韧性显著提高,而且屈强比降低,表现出良好的综合力学性能。在发生奥氏体逆转变以及两相区等温过程中,亚温淬火工艺细化新生成的奥氏体晶粒尺寸、增加大角度晶界密度,使有效晶粒尺寸明显减小,残留奥氏体的含量明显增加。     

A new post-weld heat treatment to improve toughness of 9Cr-1Mo steel weld metals

9Cr-1Mo ferritic steels have been used in the conventional power generation plants due to their excellent creep resistance. However, one of the main obstacles in welding 9Cr-1Mo steels is the formation of undesirable coarse columnar grains in weld metal whieh ean severely compromise the toughness. A new post-weld heat treatment （PWHT） is developed in the present work. Unlike the conventional processes in which the post-weld heat treatment is carried out below Ac1 , the use of temperatures above the Ac1 of 9Cr-1Mo alloy is considered. The new PWHT at a temperature above Ac1 improves the toughness of 9Cr-1Mo weld metals effectively. The improvement in toughness is mainly due to refinement and homogenization of mierostruetures. Key words     

Study of porosity tendency in the Cr-Ni austenitic weld based on inclusion''s characteristic in the droplet

The effect of nonmetallic inclusions in the droplet of the stainless steel covered electrode on the porosity was researched.The result shows that the nonmetallic inclusions in the droplet are spherical,their composition is different from the one of slag and the inclusions have the character of "inner formation".When the ratio of rutile to ilmenite in the coated material is increased, the droplet becomes coarse, the content of nonmetallic inclusion in the droplet decreases,and the porosity sensitivity in the weld metal also decreases.When the ratio of fledspar to ilmenite in the coated material is increased, the droplet becomes fine,the content of nonmetallic inclusion in the droplet increases, and the porosity sensitivity in the weld metal increases. When the ratio of Fe2O3 to ilmenite in the coated material is increased, the droplet becomes fine, the content of nonmetallic inclusion decreases, while the porosity sensitivity does not reduce.     

耐磨铸钢管ZG40CrNiMoMnSiRe的焊接

ZG40CrNiMoMnSiRe是一特种耐磨铸钢,目前没有成熟的焊接工艺。根据材料可焊性理论,通过对ZG40CrNiMoMnSiRe的碳当量、热影响区脆化及冷裂纹、热裂纹分析,提出了可行的焊接工艺及焊接质量控制方法,经焊缝外观检查、渗油试验及管道系统试验,焊接质量达到了有关标准要求。同类材料焊接可参考本工艺进行。     

国内外典型药芯焊丝的熔滴过渡及其工艺特性

采用高速摄影、平板堆焊以及化学分析等试验方法,测试、对比研究了国内外3种典型钛型渣系药芯焊丝的熔滴过渡及其工艺特性.结果表明,基于3种焊丝熔滴过渡特性与工艺性之间的关系,提出改善熔滴过渡特性新观点,即控制熔滴尺寸是必要条件,而控制"熔滴大角度过渡次数"、"熔滴存在时间和过渡间隔均匀性"、"熔滴依附渣柱过渡次数"等指数是充分条件,二者缺一不可.药芯焊丝的非轴向排斥滴状过渡形态、渣柱直接进入熔池,以及电弧区焊丝接口纵向张开现象,可能导致焊接冶金反应不完全和冶金过程新变化.熔滴过渡区的渗Si反应使熔滴氧化增氧,熔滴被细化,有利于改善熔滴过渡特性.3种典型药芯焊丝的熔滴过渡形态和电弧形态接近,然而过渡指数不尽相同,表现为B焊丝有3项工艺性指标领先,其机理在于控制熔滴过渡和电弧形态的"充分"、"必要"条件均占优势.     

焊接热循环下V-N 正火钢的V(C,N)粒子演变及微观组织分析

采用焊接热模拟方法研究了V-N微合金化正火容器钢在焊接热循环作用下的连续冷却相变;利用光学显微镜、扫描电镜分析了连续冷却相变组织及组成;通过透射电镜分析了V(C,N)析出粒子的形貌及尺寸;采用固溶度积公式计算了VN析出-时间-温度图。得到了模拟焊接热影响区粗晶区连续冷却曲线(SHCCT),给出了不同冷却条件下的室温组织及其组成,得出了V(C,N)的连续冷却过程中的临界析出t_(8/5)时间约为80 s。并讨论了V,N原子固溶及析出状态对连续冷却相变及微观组织形成的影响。     

改善高强韧管线钢焊接热影响区粗晶区韧性的现状与趋势

从高强韧管线钢的成分设计、微细夹杂物控制、奥氏体晶粒大小、热影响区微观组织、焊接工艺等几个方面阐述了各个因素对管线钢粗晶区韧性的影响,提出了改善高强韧管线钢焊接热影响区粗晶区韧性的思路与方法在于控制管线钢的合金元素、奥氏体晶粒大小、MnS的析出、控制中温转变组织以及特殊焊接工艺的开发。