铁对粉末冶金法制备铝基复合材料微观组织和力学性能及磁学性能的影响(英文)

研究铁对粉末冶金法制备铝基复合材料微观组织、力学性能及磁学性能的影响。利用机械混合制备含0,5%,10%和15%Fe(质量分数)的铝基复合材料。Al-Fe混合粉末经压制后在真空炉中600°C烧结1 h。XRD结果表明:在含有5%和10%Fe的试样中只有Fe和Al的衍射峰,而含有15%Fe的试样中则存在Al和Al13Fe4的衍射峰。实验结果表明:随着Fe含量的增加,材料的致密度和导热性变差。复合材料中的Fe可以提高其强度和硬度。材料的强化机制包括基体的晶粒细化,Fe颗粒的均匀分布以及Al13Fe4金属间化合物的形成。含有5%Fe试样的磁化强度为0.3816×10-3A·m2/g,对于含有10%Fe的试样,其磁化强度增加至0.6597×10-3A·m2/g,而对于含有15%Fe试样,其磁化强度降低至0.0702×10-3A·m2/g。这是由于在高铁试样中形成了反磁性的Al13Fe4金属间化合物导致磁化强度降低。     

Microstructural Effects on Fracture Behavior of Ferritic and Martensitic Structural Steels

The effect of microstructure on fracture behavior of 1Cr-0.5Mo and 9Cr-1Mo structural steels was evaluated. 1Cr-0.5Mo steel is used in steam pipes and superheater tubes of power stations. Its microstructure is typically comprised of bainite in a pre-eutectoid ferrite matrix with an average grain size of 10 μm. 9Cr-1Mo steel was developed for applications in steam power stations and as a candidate structural material for first-wall and blanket components of future fusion reactors. Its microstructure consisted of a fully martensitic structure with a prior austenite grain size of 25 μm. The fracture properties were measured using instrumented impact testing at temperatures between ?196 and 300 °C. The total impact fracture energy, the crack initiation and propagation energy, the dynamic yield strength, the brittleness temperature, and the cleavage fracture stress were measured. The bainitic-ferritic alloy steel exhibited much higher resistance to ductile fracture at high test temperatures, while its resistance to brittle fracture at low test temperatures was reduced compared to that of the fully martensitic alloy steel. The results were discussed in terms of the chemical composition and microstructure of the two steel types.