Characterization and electrochemical properties of CF4 plasma-treated boron-doped diamond surfaces

The effect of CF₄ plasma etching on diamond surfaces, with respect to treatment time, was investigated using scanning electron microscopy (SEM), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and electrochemical measurements. SEM observations and Raman spectra indicated an increase in surface roughening on a scale of 10–20 nm, and an increase in crystal defect density was apparent with treatment time in the range of 10 s to 30 min. In contrast, alteration of the diamond surface terminations from oxygen to fluorine was found to be rather rapid, with saturation of the F/C atomic ratio estimated from XPS analysis after treatment durations of 1 min and more. The redox kinetics of Fe(CN)₆^3−/4− was also found to be significantly modified after 10 s of CF₄ plasma treatment. This behavior shows that C–F terminations predominantly affect the redox kinetics compared to the effect on the surface roughness and crystal defects. The double-layer capacitance (C_dl) of the electrolyte/CF₄ plasma-treated boron-doped diamond interface was found to show a minimum value at 1 min of treatment. These results indicate that a short-duration CF₄ plasma treatment is effective for the fabrication of fluorine-terminated diamond surfaces without undesirable surface damage.     

High-efficiency finishing process for metal mold by large-area electron beam irradiation

A new finishing process for metal molds by large-area electron beam (EB) irradiation is proposed in this study. In the large-area EB irradiation equipment used here, an EB with high-energy density is irradiated without focusing the beam, and so the EB with a maximum diameter of 60 mm can be used for melting or evaporating metal surface instantly. Experimental results show that the surface roughness decreases from 6 μmRz to less than 1 μmRz in just a few minutes under proper machining conditions. The corrosion resistance of metal mold surface also could be greatly improved by large-area EB irradiation. Furthermore, the surface roughness of tilting surface close to 90° could be well improved. Therefore, large-area EB irradiation method has a possibility to become a high-efficiency finishing process for metal molds.     

Radiation damage induced in Si photodiodes by high-temperature neutron irradiation

Results are presented of a detailed study of the effects of high-temperature 4-MeV neutron irradiation on the performance degradation of Si pin photodiodes together with the radiation-induced defects, observed by deep level transient spectroscopy (DLTS). It was found that the dark current increases after irradiation, while the photocurrent decreases. After irradiation, two majority electron capture levels with (E _c–0.22 eV) and (E _c–0.40 eV) were induced in the n-Si substrate, while one minority hole capture level with (E _v+0.37 eV) was found. Additionally, the degradation of the device performance and the introduction rate of the lattice defects decreases with increasing irradiation temperature. For a 250 °C irradiation, the reduction of the reverse current is only 20% of the starting value. This result suggests that the creation and recovery of the radiation damage proceeds simultaneously at high temperatures.     

The result of a wall failure in-pile experiment under the EAGLE project

The WF (wall failure) test of the EAGLE program, in which 2 kg of uranium dioxide fuel-pins were melted by nuclear heating, was successfully conducted in the IGR (Impulse Graphite Reactor) of NNC/Kazakhstan. In this test, a 3 mm-thick stainless steel (SS) wall structure was placed between fuel pins and a 10 mm-thick sodium-filled channel (sodium gap). During the transient, fuel pins were heated, which led to the formation of a fuel-steel mixture pool. Under the transient nuclear heating condition, the SS wall was strongly heated by the molten pool, leading to wall failure. The time needed for fuel penetration into the sodium-filled gap was very short (less than 1 s after the pool formation). The result suggests that molten core materials formed in hypothetical LMFBR core disruptive accidents have a certain potential to destroy SS-wall boundaries early in the accident phase, thereby providing fuel escape paths from the core region. The early establishment of such fuel escape paths is regarded as a favorable characteristic in eliminating the possibility of severe re-criticality events. A preliminary interpretation on the WF test results is presented in this paper.     

The role of prostate specific antigen in diagnosis of localized adenocarcinoma of the prostate. Nara Uro-Oncology Research Group

The number of cases of prostate carcinoma (PCA) is steadily inceasing in Japan. The clinical application of a reliable tumor marker, prostate specific antigen (PSA) for the diagnosis, as well as the increasing elderly population in Japan may account for this increase. The subjects were patients at the Nara Medical University and its affiliated hospitals; 1) 687 cases without PCA were evaluated for age-specific PSA and the incidence of abnormal PSA following urological manipulations, 2) 135 cases with histological proven BPH by transurethral resection of prostate (TUR-P) were examined for PSA density (PSAD) and positive PSA rate in BPH, 3) 135 cases receiving a needle biopsy with suspicion of PCA were examined for the efficacy of PSA and PSAD and other parameters, and 4) 459 PCA cases treated between 1988 and 1994, were examined for specific PSA and PSAD values by stage and degree of cell differentiation. The PSA assay used in this study was MARKIT-M PA (normal range < or = 3.6 ng/ml). The PSA was decreased gradually with age in non-PCA patients, and abnormal PSA was found in 5.5% of these patients following manipulations. The average PSA was 2.95 +/- 2.03 ng/ml in 130 BPH patients (mean age: 71.1 +/- 7.0 years old. and average prostate volume: 32.9 +/- 16.1 ml). And abnormal PSA level (more than 3.61 ng/ml) was found in 22.3%. The mean PSAD was 0.1.0 +/- 0.06, and PSAD was below 0.15 in 86.1% of these BPH cases. Among the 135 cases receiving a needle biopsy, 33 cases had PSA values between 3.61 and 10.0 ng/ml. Of these cases, PCA was found in 18.5% of the 27 cases with a PSAD below 1.5, and in 33.3% of the 6 cases with a PSAD over 1.5. PSA and PSAD were proportionally increased with stage, and a significant difference in the PSA value was observed between stage B1 and B2, and stage C and D (P < 0.05). However, PSA and PSAD values were not significantly correlated with the cell differentiation in PCA stage A2-C. In total, PSA was 18.1 ng/ml in well, 23.9 ng/ml in moderately and 35.9 ng/ml in poorly differentiated type PCA. The positive rate of PSA was 22.3, 65.4 and 83.5%, that of prostate acid phosphatase (PAP) was 10.0, 17.8 and 45.8%, and that of GSM was 25.0, 14.7 and 68.4%, in BPH, stage A PCA and stage BPCA, respectively. In conclusion, PSA is the most reliable tool in the diagnosis of localized PCA. However, the differential diagnosis of BPH and localized PCA is difficult when the PSA value is between 3.61 and 10.0 ng/ml, and accurate staging of localized PCA is difficult with PSA or PSAD alone. At present, it is necessary to use all possible tools for the early detection of localized PCA, and to perform the needle biopsy in all PCA-suspicious cases.     

Extraction and implementation of muscle synergies in neuro-mechanical control of upper limb movement

This work faces the redundancy problem, a central concern in robotics, in a particular force-producing task by using muscle synergies to simplify the control. We extracted muscle synergies from human electromyograph signals and interpreted the physical meaning of the identified muscle synergies. Based on the human analysis results, we hypothesized a novel control framework that can explain the mechanism of the human motor control. The framework was tested in controlling a pneumatic-driven robotic arm to perform a reaching task. This control method, which uses only two synergies as manipulated variables for driving antagonistic pneumatic artificial muscles to generate desired movements, would be useful to deal with the redundancy problem; thus, suggesting a simple but efficient control for human-like robots to work safely and compliantly with humans.     

Mie scattering from sphere structures in polymer blends

Polymer blends of transparent poly(methyl methacrylate) and polystyrene become opaque due to light scattering at the boundaries of the two polymers. The polymer blend is light brown when it is illuminated by white light. The coloring depends on the spherical domain structures existing in the polymer blend. The coloring was analyzed by using the rigorous Mie theory. The Mie results were compared with the semiempirical results previously reported by the authors. The wavelength dependence of theoretical scattering efficiencies on radii of scattering spheres from 0.05 to 1.2 μm was obtained for polystyrene spheres in poly(methyl methacrylate) matrix, and vice versa. The scattering at the short wavelength region is stronger than at the long wavelength region. The scattering efficiencies become almost constant in the visible wavelength region for sufficiently large spheres.     

Aldol condensation of butanal over alkali metal zeolites

Alkali metal zeolites and metal oxides were used for the aldol condensation of n-butanal to 2-ethyl-2-hexenal. The order of activity at 150 °C and 1 atm. was: CsNaY > NaY > LiNaY > MgO >Al₂O₃. Selectivity to 2-ethyl-2-hexenal was 100% for both pure and mixed isomer feed. Infrared spectroscopic studies showed that stable catalysts were produced by propene pretreatments which blocked Lewis acid sites. Adsorption of ammonia and carbon dioxide on CsNaY during aldol condensation of n-butanal causes a decrease in rate. This result, along with the order of activity, suggests that the presence of both acid and basic sites produce higher activity than strongly basic MgO.Work performed at San Jose State University.     

High-aspect-ratio through-hole array microfabricated in a PMMA plate for monodisperse emulsion production

Microchannel (MC) emulsification is a promising technique for producing monodisperse emulsions consisting of highly uniform droplets. The authors developed a high-aspect-ratio microstructure (HARMST) made of poly(methyl methacrylate) (PMMA) as a new MC emulsification device. A PMMA straight-through MC array plate consisting of 31,250 through-holes with a 7.3 × 22.9-μm oblong section and a 200-μm depth was fabricated by a process of synchrotron radiation (SR) lithography and etching. Oblong MCs fabricated in a PMMA straight-through MC array were highly uniform with a coefficient of variation of less than 2%. The fabricated PMMA straight-through MC array plate was used to produce water-in-oil (W/O) emulsions. Monodisperse W/O emulsions with average droplet diameters of approximately 25 μm and a minimum coefficient of variation of 3.2% were produced via a hydrophobic PMMA straight-through MC array. The PMMA straight-through MC array plate also produced monodisperse W/O emulsions at droplet production rates of up to 1.7 × 10⁴/s. The PMMA straight-through MC array plates developed in this work are expected to expand the application field of emulsification using straight-through MC array plates, which have previously been made of single-crystal silicon.     

Production of monodisperse water-in-oil emulsions consisting of highly uniform droplets using asymmetric straight-through microchannel arrays

This paper reports the production of monodisperse water-in-oil (W/O) emulsions using new microchannel emulsification (MCE) devices, asymmetric straight-through MC arrays that were hydrophobically modified. The silicon asymmetric straight-through MC arrays consisted of numerous pairs of microslots and circular microholes whose cross-sectional sizes were 10 μm. This paper primarily focused on investigating the effect of the osmotic pressure of a dispersed phase (Π_d) on MCE. This paper also investigated the effects of the type of continuous-phase oils and the dispersed-phase flux (J _d) on MCE. The dispersed phases were Milli-Q water and Milli-Q water solutions containing sodium chloride. The continuous phases were decane (as control), hexane, medium chain triacylglyceride (MCT), and refined soybean oil (RSO) solutions containing tetraglycerin monolaurate condensed ricinoleic acid ester (TGCR) as a surfactant. At Π_d of exceeding threshold, highly uniform aqueous droplets with coefficients of variation of less than 3% were stably generated via hydrophobic asymmetric straight-through MCs. Monodisperse W/O emulsions with average droplet diameters between 32 and 45 μm were produced using the alkane–oil and triglyceride–oil solutions as the continuous phase. This work also demonstrated that the hydrophobic asymmetric straight-through MC array had remarkable ability to produce highly uniform aqueous droplets at very high J _d of up to 1,200 L m⁻² h⁻¹.