Synthesis of heterocyclic metal complexes and their evaluation as marine antifoulants

4-Amino-3-thio-1,24-triazolidine (L₁) and 4-amino-5-thio-1,3,4-thiadiazole (L_II) as well as their metal complexes of the general formulae ML_I·2H₂O and ML_IICl (M; Pb(II), Cd(II) and Zn(II)) were prepared. With Sn(II), we obtained Sn(L_I)₂·2H₂O and SnL_IICl, respectively. The structures of the compounds were identified through elemental analysis, and IR and UV spectra measurements, in addition to thermal analysis in case of the metal complexes. The antifouling properties of the compounds were tested by their incorporation into paint formulations which were applied to PVC substrates and tested in water from Alexandria western harbour. When the compounds were added at 17·5% by volume, the coated panels were fouled after 3 months of immersion. The addition of 6·7% by volume of tributyltin oxide to 15·8% of the prepared compounds in one formulation elevated the paint efficiency and prevented fouling for 11 months. Paint containing solely tributyltin oxide at the same concentration was inactive against algae.     

Temperature and pressure effects on supercritical CO2 extraction of tomato seed oil

Tomato seed oil was extracted with supercritical carbon dioxide in a semibatch-flow extractor within the temperature range 313–343 K and the pressure range 10.8–24.5MPa. The extraction rates increased with pressure, but decreased with temperature increase because of the variation in solvent density and resultant differences in oil solubility. The fatty acid composition of the extracted oil was similar to that of soybean oil.     

Fractionation and characterisation for antioxidant activity of hydrolysed whey protein

Whey protein isolate (WPI) was hydrolysed for 1 h using Alcalase, Protamex and Flavourzyme. Native WPI, hydrolysed WPI and two commercial WPI hydrolysates were subjected to fractionation by size exclusion chromatography. Antioxidant activity of WPI fractions was measured with a liposome‐oxidising system (50 µM FeCl₃/0.1 µM ascorbate, pH 7.0). Lipid oxidation was measured as thiobarbituric acid‐reactive substances (TBARS). Gel electrophoresis and amino acid analysis were run to identify the peptide composition. The influence of amino acid composition on antioxidant activity was evaluated using multivariate analysis methods (correlation analysis, principal component analysis, multiple linear regression and discriminant analysis). TBARS assays indicated the presence of antioxidant activity in all protein fractions, including non‐hydrolysed WPI. For native and hydrolysed WPI samples the first fraction (> 45 kDa) showed a higher TBARS inhibition effect (24–27%) when compared with lower‐molecular‐weight fractions and hydrolysate mixtures. In contrast, for commercial WPI hydrolysates a higher inhibitory effect was found in most of the lower‐molecular‐weight fractions (30–55%). The ability of WPI fractions to delay lipid oxidation was found to be related to the prevalence of histidine and hydrophobic amino acids. Copyright © 2004 Society of Chemical Industry     

Influence of third monomer on the crystal phase transition behavior of ethylene-tetrafluoroethylene copolymer

Crystal phase transition between the low- and high-temperature phases has been investigated for ethylene (E)-tetrafluoroethylene (TFE) alternating copolymer (ETFE) containing the third monomeric species by the temperature dependent measurements of wide-angle X-ray diffraction (WAXD) and small-angle X-ray scattering (SAXS) and differential scanning calorimetry. Nonafluoro-1-hexene (NFH) and hexafluoropropylene (HFP) were chosen as the third monomers, where they are different in the side-branch length, -(CF₂)₃CF₃ and -CF₃, respectively. In the case of E/TFE/NFH copolymer (ET-C4F9), the crystal phase transition temperature of the original ETFE two-components copolymer was not very much affected by the existence of NFH in the range of NFH content from 0.7 to 3 mol%. Contrarily, the crystal phase transition temperature of E/TFE/HFP copolymer (ET-CF3) was found to decrease drastically with increasing HFP content. The melting temperature and the higher-order structure were also affected sensitively depending on the HFP content. This difference in phase transition behavior between ET-C4F9 and ET-CF3 copolymers is reasonably interpreted as follows: the short side groups (-CF₃) of HFP monomeric unit are included in the crystal lattice of E/TFE chains and the unit cell is expanded gradually with an increment of the HFP content, resulting in the decrease in phase transition point because of easier thermal motion of the chains. On the other hand, the long side groups [-(CF₂)₃CF₃] of NFH monomeric units are excluded out of the crystal lattice and located on the lamellar surfaces or in the amorphous region and do not affect very much the phase transition temperature even when the NFH content is increased. In association with such a change in crystal structure, the long period of stacked lamellar structure was found to decrease remarkably in the case of NFH, whereas it does not change very much for HFP, consistent with the interpretation of the above-mentioned WAXD data.     

High-performance polymer alloys of polybenzoxazine and bismaleimide

Two series of high-performance polymer alloys were prepared by mixing typical benzoxine monomers, 3-phenyl-3,4-dihydro-2H-1,3-benzoxazine (P-a) or 6,6-(1-methylethyliden)-bis-(3,4-dihydro-3-phenyl-2H-1,3-benzoxazine) (B-a), with a typical bismaleimide, 4,4-bismaleimidodiphenyl methane by various ratios followed by thermal treatment up to 240 °C. DSC and IR of the alloys were examined to follow the curing reaction. These analyses showed that the obtained polymer alloys are AB co-cross-linked polymer networks through the formation of ether linkage between the hydroxyl group of polybenoxazine and the double bond of bismaleimide. Viscoelastic analysis and softening temperature measurement revealed that the polymer alloys have much higher glass transition temperatures than those of each homopolymer. The thermal stability also increased with the increase of bismaleimide content as evidenced by TGA.     

Properties of indium oxide/tin oxide multilayered films prepared by ion-beam sputtering

The preparation and characterization of indium oxide (InO _x )/tin oxide (SnO _y ) multilayered films deposited by ion-beam sputtering are described and compared with indium tin oxide (ITO) films. The structure and the optoelectrical properties of the films are studied in relation to the layered structures and the post-deposition annealing. Low-angle X-ray diffraction analysis showed that most films retained the regular layered structures even after annealing at 500° C for 16 h. As an example, we obtained a resistivity of 6×10^–4 cm and a transparency of about 85% in the visible range at a thickness of 110 nm in a multilayered film of InO _x (2.0 nm)/SnO _y (0.2 nm)×50 pairs when annealed at 300° C for 0.5 h in air. Hall coefficient measurements showed that this film had a mobility of 17 cm² V^–1 sec^–1 and a carrier concentration (electron density) of 5×10²⁰ cm^–3.     

Modification of mesophase pitch by blending Part 2 Modification of mesophase pitch fibre precursor with thermoresisting polyphenyleneoxide (PPO)

Polyphenyleneoxide was blended in amounts of 5 or 10 wt% into petroleum-derived mesophase pitch to reinforce the pitch fibre before the oxidative stabilization to achieve better handling properties. Although polyphenyleneoxide was fusible but hardly soluble in the mesophase pitch even at a spinning temperature of 350° C, blended pitch could be smoothly spun into pitch fibre 10m diameter, as could the parent pitch. Fibrous polyphenyleneoxide of less than 1m diameter was homogeneously dispersed in the pitch fibre, being arranged along the fibre axis. Such fibrous polyp henyleneoxide reinforced the pitch fibre considerably. The fibrous substances at the centre of the fibre disappeared in the carbonized fibre at 1300° C after oxidation at 250° C, although some short ones were observed in the skin region of the fibre, suggesting that polyphenyleneoxide was co-carbonized to be assimilated with mesophase pitch at the centre of the fibre, where the effects of oxidation may be rather limited. The oxidation reactivity and its mechanical strength after carbonization were slightly lower in comparison with those of the parent mesophase pitch.     

Role of Acetic Acid Added to the Reaction Media for the Enantio-differentiating Hydrogenation of Methyl Acetoacetate Over a Tartaric Acid-modified Nickel Catalyst

The role of acetic acid added to the reaction media for the enantio-differentiating hydrogenation of methyl acetoacetate over a (R,R)-tartaric acid-in-situ-modified nickel catalyst was studied from the viewpoint of the hydrogenation rate during repeated runs. The hydrogenation of methyl acetoacetate on the “enantio-differentiating sites” of a tartaric acid-modified nickel catalyst was specifically accelerated by the acetic acid added to the reaction media to increase the enantio-differentiating ability of the catalyst. In order to increase the enantio-differentiating ability, the addition of acetic acid to the reaction media was required in each run during the repeated use of the catalyst.