Influence of fretting on the fatigue strength at the vise clamp-specimen interface

Fretting fatigue is one of the most important phenomena for inducing a significant reduction of fatigue strength and consequently, leading to unexpected failure accidents of the engineering structures even at very low stresses. In the present study, both plain and fretting fatigue tests with zero mean stress were carried out on two different types of steel, low-carbon steel and martensitic stainless steel, by means of a reversed bending fatigue testing machine. The drop in the fatigue strengths through fretting at vise clamp-specimen interface were significant for both tested steels. The fretting processes produced a reduction in fatigue strength of about 27% for low-carbon steel and 16% for martensitic stainless steel.     

Analysis of deformation processes in glassy polycarbonate using internal friction measurements during a tensile test

Internal friction has been measured by torsion at 1 Hz during tensile tests performed on glassy polycarbonate at room-temperature. Steady-state flow and transient effects have been studied during continuous tensile tests and strain-rate changes. During steady-state, internal friction and flow-stress vary in a similar way with strain-rate. But during transients, internal friction varies continuously while flow-stress passes through a maximum (or a minimum). These results are interpreted assuming that non-elastic deformation of glassy polymers requires some microscopic discontinuous processes such as motion of defects. Two parameters are considered: the velocity v and the density ρ of mobile defects. Assuming that the former is directly related to the flow stress, it has been shown that internal friction is related to the density of mobile defects ρ. This feature is used to interpret the different stages of a tensile test curve. Activation volumes for both velocity and density of mobile defects are calculated from experimental data.     

Effect of expandable graphite and ammonium polyphosphate on the thermal degradation and weathering of intumescent fire-retardant coating

This research aims to study the effect of ammonium polyphosphate and expandable graphite on the intumescent coating formulations (ICF). The coating presented in this research article is based on carbon source expandable graphite (EG), blowing agent melamine, acid source ammonium polyphosphate (APP), epoxy resin as a binder with polyamide amine. The stability of the developed coating was verified at 950°C for 1-hour fire test. The results showed that the coating is stable and well bond with the steel substrate. The char was characterized by using FESEM, XRD, FTIR, DTA, TGA, XPS, Py-GCMS and Weathering Test. The morphology of the char was studied by SEM of the coating after furnace fire test. XRD and FTIR show the presence of graphite, borophosphate; boron oxide and sassolite in the residual char. TGA and DTG disclosed that EG improved the residual mass of coating. XPS analysis showed the char residue of IF5-APP-EG contains carbon and oxygen contents 47.50 and 40.70, respectively. Py-GCMS analysis described that the IF5-APP-EG released less gaseous compounds. The weathering test illustrated that's the char expansion of coatings samples was decreased due to the presence of a humid environment and UV light. The IF5-APP-EG showed the maximum char expansion, lower substrate temperature and high residual weight among the studied formulations.     

Performance tuning of glass fiber/epoxy composites through interfacial modification upon integrating with dendrimer functionalized graphene oxide

In this study, glass fiber/epoxy composites were interfacially tailored by introducing polyamidoamine (PAM) dendrimer functionalized graphene oxide (GO) into epoxy matrix. Two different composites each containing varying loading fraction (0.5, 1.0, and 1.5 wt%) of GO and GO-PAM were fabricated via hot press processing. Composites were evaluated for interlaminar shear strength (ILSS), dynamic mechanical properties and thermal conductivity. The inclusion of 1.5 wt% GO-PAM resulted ~57.3%, ~42.7%, and ~54% enhancement in ILSS, storage modulus and thermal conductivity, respectively. Almost, ~71% reduction in coefficient of thermal expansion was also observed at same GO-PAM loading. Moreover, higher glass transition temperature was observed with GO-PAM addition. GO-PAM substantially improved fiber/matrix interfacial adhesion, which was witnessed through scanning electron microscopy. The enhanced thermo-mechanical performance was attributed to interfacial covalent interactions engendered by ring opening reaction between epoxy and amine moieties of PAM dendrimers. These multiscale composites with extraordinary functional properties can outperform conventional counterparts with improved reliability and performance.     

Effect of Varying Amount of Polyethylene Glycol (PEG-600) and 3-Aminopropyltriethoxysilane on the Properties of Chitosan based Reverse Osmosis Membranes

Chitosan and polyethylene glycol (PEG-600) membranes were synthesized and crosslinked with 3-aminopropyltriethoxysilane (APTES). The main purpose of this research work is to synthesize RO membranes which can be used to provide desalinated water for drinking, industrial and agricultural purposes. Hydrogen bonding between chitosan and PEG was confirmed by displacement of the hydroxyl absorption peak at 3237 cm⁻¹ in pure chitosan to lower values in crosslinked membranes by using FTIR. Dynamic mechanical analysis revealed that PEG lowers Tg of the modified membranes vs. pure chitosan from 128.5 °C in control to 120 °C in CS-PEG5. SEM results highlighted porous and anisotropic structure of crosslinked membranes. As the amount of PEG was increased, hydrophilicity of membranes was increased and water absorption increased up to a maximum of 67.34%. Permeation data showed that flux and salt rejection value of the modified membranes was increased up to a maximum of 80% and 40.4%, respectively. Modified films have antibacterial properties against Escherichia coli as compared to control membranes.     

Interval Finite Elements as a Basis for Generalized Models of Uncertainty in Engineering Mechanics

Latest scientific and engineering advances have started to recognize the need for defining multiple types of uncertainty. Probabilistic modeling cannot handle situations with incomplete or little information on which to evaluate a probability, or when that information is nonspecific, ambiguous, or conflicting [12], [47], [50]. Many interval-based uncertainty models have been developed to treat such situations. This paper presents an interval approach for the treatment of parameter uncertainty for linear static structural mechanics problems. Uncertain parameters are introduced in the form of unknown but bounded quantities (intervals). Interval analysis is applied to the Finite Element Method (FEM) to analyze the system response due to uncertain stiffness and loading. To avoid overestimation, the formulation is based on an element-by-element (EBE) technique. Element matrices are formulated, based on the physics of materials, and the Lagrange multiplier method is applied to impose the necessary constraints for compatibility and equilibrium. Earlier EBE formulation provided sharp bounds only on displacements [32]. Based on the developed formulation, the bounds on the system’s displacements and element forces are obtained simultaneously and have the same level of accuracy. Very sharp enclosures for the exact system responses are obtained. A number of numerical examples are introduced, and scalability is illustrated.     

Molecular genetics of Krabbe disease (globoid cell leukodystrophy): diagnostic and clinical implications

Galactocerebrosidase (GALC) is a lysosomal beta-galactosidase responsible for the hydrolysis of the galactosyl moiety from several galactolipids, including galactosylceramide and psychosine. The deficiency of this enzyme results in the autosomal recessive disorder called Krabbe disease. It is also called globoid cell leukodystrophy (GLD), because of the characteristic storage cells found around cerebral blood vessels in the white matter of affected human patients and animal models. Although most patients present with clinical symptoms before 6 months of age, older patients, including adults, have been diagnosed by their severe deficiency of GALC activity. More than 40 mutations have been identified in patients with all clinical types of GLD. While some mutations clearly result in the infantile type if found homozygous or with another severe mutation, it is difficult to predict the phenotype of novel mutations or when mutations are found in the heterozygous state. A high incidence of polymorphic changes on apparent disease-causing alleles also complicates the interpretation of the effects of mutations. The detection of mutations has greatly improved carrier identification among family members and will permit preimplantation diagnosis for some families. The molecular characterization of the naturally occurring mouse, dog, and monkey models will permit their use in trials to evaluate different modes of therapy.     

Microstructural evolution during friction surfacing of tool steel H13

Coatings of AISI H13 tool steel were made on low carbon steel by friction surfacing. Detailed microstructural studies and microhardness tests were carried out on the coatings. Studies revealed defect-free coatings and sound metallurgical bonding between the coating and the substrate. In addition, mechanical interlocking on a very fine scale was observed to occur between the coating and the substrate. Coatings exhibited martensitic microstructure with fine grain size and with no carbide particles. Coatings in as-deposited condition showed very high hardness (58 HRC) compared to the mechtrode material in annealed condition (20 HRC). Based on these findings, microstructural evolution during friction surfacing of H13 tool steel is discussed. The current work shows that friction surfaced tool steel coatings are suitable for use in as-deposited condition. Further improvements in coating microstructure and properties are possible with appropriate post-surfacing heat treatment.