Study on catalytic combustion of benzene over cerium based catalyst supported on cordierite

A series of MnCeOx catalysts supported on cordierite honeycomb (Cord) were prepared by a combustion synthesis method using Mn(NO3)2 , Ce(NO3 )2·6H2O and citric acid. The effect of the molar ratio of Mn/Ce, calcination time, the amount of citric acid and the effect of water vapor on the catalytic properties for the complete oxidation of benzene were investigated. These catalysts were characterized by X-ray diffraction (XRD), H 2 temperature-programmed reduction (H2 -TPR), O2 temperature programmed desorption (O2 -TPD) and scanning electron microscopy (SEM) techniques. The results indicated that the MnCeOx /Cord catalyst with Mn/Ce molar ratio of 1:1, calcining for 7h and M n+ /(citric acid) molar ratio of 6 exhibited the highest catalytic activity. When the concentration of benzene was 1500 ppm and the gaseous hourly space velocity was 20000h -1 , the conversion of toluene was 99.1% at the reaction temperature of 300 oC.     

Ce-Ni-Mn-O复合氧化物催化剂催化燃烧苯的性能研究

以堇青石蜂窝陶瓷为载体,以Ce(NO3)2、Ni(NO3)2和Mn(NO3)2为原料,采用柠檬酸浸渍法制备了负载型Ce-Ni-Mn-O复合氧化物催化剂,考察了Ce、Ni与Mn摩尔比、焙烧温度和焙烧时间对催化燃烧苯的性能影响,并采用比表面积分析仪(BET)、X射线衍射仪(XRD)、扫描电镜(SEM)对催化剂进行表征。实验结果表明,在系列催化剂中,n(Ce)/n(Ni)/n(Mn)=1∶0.5∶0.5,经500℃焙烧7h的催化剂表现出最佳的催化燃烧苯的活性,在300℃及体积空速为15000h-1条件下,即可促使浓度为4.8g/m3的苯催化转化率达到91.8%。     

早龄期加载对粉煤灰混凝土变形及强度的影响

研究了粉煤灰掺量、加载龄期和加载应力对粉煤灰混凝土早期变形及加载后强度变化的影响。研究结果表明：随着粉煤灰掺量增加,混凝土的变形量逐渐降低,当掺量为30%时,变形量减少了33.6%;随着加载龄期提前或加载应力增大,粉煤灰混凝土的早期变形量增大,其中,加载应力的影响尤其明显,60%加载应力（60%的标准养护条件下7 d轴心抗压强度）比20%加载应力下混凝土最终变形量增加了277.2%;混凝土初始加载时间提前或加载应力增大会导致加载后粉煤灰混凝土强度下降,加载应力比加载龄期对加载后粉煤灰混凝土强度的影响更明显。     

堇青石负载稀土铈基催化剂催化燃烧苯的性能研究

以堇青石蜂窝陶瓷为载体,以过渡金属Mn(NO3)2和稀土金属Ce(NO3)2·6H2O盐为原料,采用柠檬酸浸渍法制备负载型MnCeOx混合氧化物催化剂,考察Mn与Ce的摩尔比、焙烧温度与时间以及柠檬酸用量对催化燃烧苯性能的影响,应用正交实验设计方案优化最佳制备工艺参数,并采用X射线衍射仪(XRD)、H2-TPR和扫描电镜(SEM)对催化剂进行表征与分析。实验结果表明n(Mn)∶n(Ce)=19∶21,焙烧时间为7h,n(Mn+)∶n(柠檬酸)=6∶1的催化剂表现出最佳的催化活性,在300℃及体积空速为20000h-1条件下,催化燃烧浓度为1.5×10-3的苯,催化转化率可达99.1%。     

减水剂与石灰石粉复合胶凝材料的适应性研究

针对石灰石粉在掺合料混凝土中的应用所产生的外加剂与胶凝体系的适应性问题,采用饱和点和流动度的方法比较了减水剂与不同复合胶凝材料(石灰石粉-粉煤灰、石灰石粉-矿渣、石灰石粉-硅灰)的适应性影响规律.试验结果表明:不同复合胶凝材料组成的适应性存在显著差异,石灰石粉的掺入能够降低聚羧酸高效减水剂的饱和点;粉煤灰和矿渣的掺入对改善聚羧酸高效减水剂与石灰石粉-水泥胶凝体系的适应性有利;硅灰的掺入使得聚羧酸高效减水剂与石灰石粉-水泥胶凝体系的适应性变差;石灰石粉-粉煤灰的掺入,混凝土的早期强度降低,但是混凝土的后期强度得到提高.     

早龄期加载对粉煤灰混凝土变形及强度的影响

研究了粉煤灰掺量、加载龄期和加载应力对粉煤灰混凝土早期变形及加载后强度变化的影响。研究结果表明:随着粉煤灰掺量增加,混凝土的变形量逐渐降低,当掺量为30%时,变形量减少了33.6%;随着加载龄期提前或加载应力增大,粉煤灰混凝土的早期变形量增大,其中,加载应力的影响尤其明显,60%加载应力(60%的标准养护条件下7d轴心抗压强度)比20%加载应力下混凝土最终变形量增加了277.2%;混凝土初始加载时间提前或加载应力增大会导致加载后粉煤灰混凝土强度下降,加载应力比加载龄期对加载后粉煤灰混凝土强度的影响更明显。