Microstructure and Its Influence on Mechanical Behaviour of Directionally Solidified DZ38G Superalloy

The features of microstructure and theirinfluence on mechanical properties onstress-rupture as well as thermal fatigue ofdirectionally solidified DZ38G nickel-base su-peralloy have been investigated.It has beenfound that the contents of carbides on grainboundaries are increased and morphology of γ'-precipitates has been changed after testing.Particularly γ'-precipitates coalesced intoraft-like in morphology perpendicular to theapplied stress-axis have been observed thathas no detrimental effect on the stress-rupturebehaviour.The tendency of σ-formation hasalso been discussed.The σ-phase can be avoidedwhen the process parameters are chosenappropriately during solidification.     

C—Co—Cr三元中间合金的应用

一、前言 C-Co-Cr三元系合金的研究,是为了配制几种司太立特钴基高温铸造合金。在司太立特合金中,Stellitel、Stellite3、Stellite12、Stellite20、Stellite100和Stellite SF20等,含碳量均超过1.5～2.5％。含碳量这么高的钴基合金成分的配制,具有一定的难度。据有关资料报导,碳在钴中没有固态溶解性。     

约束性凝固参数对DZ38G合金定向结晶叶片组织和性能的影响

本文在生产条件下,研究了不同约束性凝固参数对 DZ38G 合金定向结晶叶片的组织和力学性能影响。结果表明:在4mm/min 的抽拉速度下,可以获得柱晶平直,发散度小的定向结晶叶片。型壳和浇注温度过高会导致合金中 Cr 元素损耗率的增加,叶片显微疏松增多,组织粗大,合金力学性能降低。型壳温度在1500—1550℃,浇注温度为1500—1540℃时,可以获得满意的组织和较高的力学性能,所铸定向结晶叶片已通过台架长期试车的考验。     

型壳耐火材料对无余量定向凝固叶片铸件质量的影响

本文阐述了电熔莫来石结合刚玉制成的型壳材料的显微结构和烧结特点,以及对型壳性能的影响。研究了定向凝固过程中型壳表面层耐火材料杂质和液态金属杂质对叶片铸件表面质量的影响。结果表明:电熔莫来石结合刚玉型壳材料是一种理想的适用于定向凝固型壳的耐火材料。     

DZ38G抗热腐蚀定向凝固叶片合金的组织与力学性能

本文利用“铸型移动法”定向结晶工艺研究了DZ38G抗热腐蚀定向凝固涡轮叶片合金的组织和力学性能。该合金含铬量为16wt％,对有害微量元素控制严格。研究结果表明:铸型温度为1500℃,移动速度在6～7mm/min条件下,可以获得按〔001〕平行方向排列的致密挺拔的柱状晶组织。采用1190℃,2hAC+1090℃,2hAC+850℃,24hAC热处理时,可以得到满意的综合性能。在与K38合金具有同样优良的抗热腐蚀条件下,使用温度比K38合金提高40～45℃。     

燃气轮机抗热腐蚀DD8单晶叶片材料及其应用研究

一、概述 抗热腐蚀单晶叶片材料DD8合金的研究工作,是西安航空发动机公司与金属研究所在共同研制WS9G2(13000马力)燃气发生器高压二级涡轮叶片材料DZ38G定向凝固叶片工作的基础上,为开发研制WS9G3(15000马力)燃气发生器涡轮叶片材料时,由设计部门提出来的。