在gleeble 1500D热模拟试验机上以应变速率为0.01 s-1和1s-1,变形温度为350℃和400℃,对AZ61镁合金热压缩变形,并对变形试样显微组织进行了研究。结果表明:热变形过程中发生了不同程度的动态再结晶,得到不完全再结晶组织。变形温度和应变速率对再结晶程度、再结晶晶粒尺寸均匀性有明显影响;以较低的温度配合高的应变速率,热变形后发生再结晶晶粒均匀细小;变形温度高且应变速率高时,发生动态再结晶的区域变小,再结晶晶粒尺寸偏大且极不均匀,低温高速热变形有利于获得均匀细小的再结晶组织。 相似文献
2.
3.
Effects of various Mg-Sr master alloys on microstructural refinement of ZK60 magnesium alloy 总被引:1,自引:0,他引:1
The effects of various Mg-Sr master alloys(conventional as-cast,rapidly-solidified,rolled and solutionized) on microstructural refinement of ZK60 magnesium alloy were investigated.The results indicate that the refinement efficiency of various Mg-Sr master alloys in ZK60 alloy is different.The rolled Mg-Srmaster alloy is found to have relatively higher refinement efficiency than the conventional as-cast,solutionized and rapidly-solidified Mg-Sr master alloys.After being treated with the rolled Mg-Sr maste... 相似文献
4.
5.
利用光学显微镜、扫描电镜、X射线衍射分析仪、热/力模拟试验机、拉伸试验机等研究了Mg-1.9Zn-0.9Mn-xNd合金铸态组织与性能。结果表明:Mg-1.9Zn-0.9Mn合金组织为α-Mg+α-Mn+MgZn,当含钕量大于0.22 mass%时合金中出现了Mg-ZnNd三元合金相T_1(六方晶格)和T_2(斜方晶格);随含钕量增加,三元合金相数量增大,屈服强度及显微硬度随之增加,但当三元合金相形态由不连续的块状向断网状和网状转变后,受力时晶间产生裂纹,使抗拉强度及断后伸长率降低;在热压缩试验中合金发生了不完全再结晶,钕使峰值应力从50.8 MPa提高到92.4 MPa,并且使动态再结晶晶粒细化。 相似文献
6.
7.
Mg-9Sr中间合金的组织及其对AZ31镁合金组织细化的影响 总被引:1,自引:0,他引:1
对Mg-9Sr中间合金的组织及其对AZ31镁合金组织细化的影响进行了研究.研究结果表明:常规铸态、热处理态和快速凝固态Mg-9Sr中间合金的组织均由(-Mg和Mg17Sr2相组成,但合金组织中枝晶的尺寸和Mg17Sr2相的数量和形态存在一定的差异.不同状态Mg-9Sr中间合金对AZ31镁合金均有很好的细化效果,其中热处理态Mg-9Sr中间合金的细化效果最好,其次依次是常规铸态和快速凝固态Mg-9Sr中间合金.在Sr加入量为0.1%和熔体保温时间为60 min条件下,添加热处理态Mg-9Sr中间合金可使AZ31镁合金获得46 μm的最小平均晶粒尺寸. 相似文献