贺海燕 《武汉理工大学学报(材料科学英文版)》2009,24(3):359-362
Fatigue-free Bi3.2La0.8Ti3O12 ferroelectric thin films were successfully prepared on p-Si (100) substrates using metalorganic solution deposition process. The orientation and formation of 5-layers thin films
were studied under different processing conditions using XRD. Experimental results indicate that increase in annealing time
at 700 °C after preannealing for 10 min at 400 °C can remarkably increase (200)-orientation of the films derived from the
precursor solutions with two contents of citric acid. Meanwhile, high content of citric acid increases the film thickness
and is conducive to the a-orientation of the films with the preannealing, and low concentration of the solution is conducive to the c-orientation of
the films without the preannealing. 相似文献
3.
论述了由不同制备工艺获得的Fe2O3陶瓷及各种添加剂下表面羟基和吸附氧的形成和性质,分析了表面羟基和吸附氧的酸碱性对气湿特性的影响。 相似文献
4.
应用Sol-gel法成功合成了纳米SrTiO3粉体。酞酸丁酯和氯化锶为金属离子源,先驱体以甲醇为溶剂、柠檬酸为螯合剂、乙酰丙酮为稳定剂、聚乙二醇和聚乙烯醇为模板。干先驱体经700℃1h烧成后得到纯的SrTiO3粉体。研究了表面活性剂对粉体的粒子尺寸和形貌的影响。合成粉体的聚乙二醇诱导了均匀的较小的圆形粒子。聚乙烯醇则使合成粉体为较大尺寸的长板柱状的粒子。 相似文献
5.
应用sol-gel法成功地低温合成了超细BaFe12O19磁粉。先驱体氢氧化物在醇:水比为1:1.7、Ba^2+和Fe^3+以的离子摩尔比为1.15:12的溶胶溶液中(以氢氧化钠NaOH为沉淀剂)制得。采用两步热处理法,先驱体氢氧化物在300℃预热处理1h,再在800℃热处理5h,X射线衍射分析(XRD)分析表明形成了BaFe12O19磁性粒子,粒子尺寸为42.0nm,接近理论单畴尺寸40nm。 相似文献
6.
7.
以对氨基苯磺酸、苯酚和甲醛为主要原料,采用碱性合成线路制备了氨基磺酸系高效减水剂,并将之应用于99氧化铝陶瓷料浆中。研究了单体比例、单体浓度、交联剂用量、反应体系初始pH值、反应时问和反应温度等因素对减水效果的影响。结果表明:所制备的减水剂对99氧化铝陶瓷料浆具有明显的减水效果,优于传统的陶瓷用减水剂。较佳的减水剂制备工艺为:对氨基苯磺酸:苯酚:甲醛=1:2:6(摩尔比);反应初始pH值为8.0;对氨基苯磺酸浓度为0.35mol/L;反应时间为4h;反应温度为90-95℃。 相似文献