亮色系建筑涂料色浆的研制及应用

阐述了自制亮色系色浆的必要性。介绍了自制亮色系色浆的颜料筛选,配方调整及其在建筑涂料中应用后对面漆性能的影响。     

Core–shell NTC materials with low thermal constant and high resistivity for wide-temperature thermistor ceramics

Core–shell structures have been proposed to improve the electrical properties of negative-temperature coefficient (NTC) thermistor ceramics. In this work, Al₂O₃-modified Co_1.5Mn_1.2Ni_0.3O₄ NTC thermistor ceramics with adjustable electrical properties were prepared through citrate-chelation followed by conventional sintering. Co_1.5Mn_1.2Ni_0.3O₄ powder was coated with a thin Al₂O₃ shell layer to form a core–shell structure. Resistivity (ρ) increased rapidly with increasing thickness of the Al₂O₃ layer, and the thermal constant (B) varied moderately between 3706 and 3846 K. In particular, Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ ceramic with 0.08 wt% Al₂O₃ showed the increase of ρ double, and the change in its B was less than 140 K. The Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ NTC ceramics showed high stability, and their grain size was relatively uniform due to the protection offered by the shell. The aging coefficient of the ceramic was less than 0.2% after aging for 500 hours at 125°C. Taken together, the results indicate that as-prepared Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ NTC ceramics with a core–shell structure may be promising candidates for application as wide-temperature NTC thermistor ceramics.     

Microstructural and electrical changes in Ca0.9R0.1CeNbMoO8 (R = Y,Sm, Nd,La) ceramics induced by rare-earth ion doping

Rare-earth ions doped Ca_0.9R_0.1CeNbMoO₈ (R = Y, Sm, Nd, La) ceramics have been successfully prepared by solid-state method, and their modifications to the microstructure and electrical properties are also investigated. The rare-earth ions doped ceramics exhibit the scheelite structure. With the increase in the radius of rare-earth ions, the lattice distortion and bond interaction will be enhanced, and the consistency of grain size will be reduced. The ceramics exhibit negative temperature coefficient (NTC) thermistor characteristics in the temperature range of 473 K-1273 K, and the activation energy decreases with the increase of the radius of rare-earth ions. Rare-earth ions doping can increase the content of Ce³⁺ ions and promote the conductivity of ceramics. Except for Sm³⁺-doped ceramics, the high-temperature aging rate of other ceramics is less than 2%. The existence of some metastable Sm²⁺ ions in Sm³⁺-doped ceramics not only increases the activation energy, but also reduces the high-temperature stability of the ceramics.     

Novel thermal-sensitive properties of NBT-BZT composite ceramics for high-temperature NTC thermistors

We found for the first time that (1 − x) Na_0.5Bi_0.5TiO₃-xBiZn_0.5Ti_0.5O₃ (NBT–BZT) composite ceramics showed negative temperature coefficient (NTC) at a high temperature. The NBT–BZT nanopowders were successfully prepared by Pechini method. Their ceramics were sintered at 1100°C. The NBT–BZT ceramic exhibited a good linear relationship between logarithm of electrical resistivity (Inρ) and reciprocal of absolute temperature (1000/T) at 250°C–1050°C. The obtained ρ₆₀₀, ρ₉₀₀, and B_600/900 constants of the NBT–ZBT NTC thermistors are approximately 5.92 × 10⁶ to 3.01 × 10⁴ Ω cm, 7.03 × 10³ to 7.60 × 10² Ω cm and 2.3 × 10⁴-1.3 × 10⁴ K, respectively. The electrical characteristics can be tuned to the desired value by changing the Na_0.5Bi_0.5TiO₃ content in the compound. The electrical conductivity in these compounds is due to the electron jumps between Ti³⁺ and Ti⁴⁺ and oxygen-ion conductivity. Results demonstrate a tremendous potential of the studied system for perovskite materials with NTC performance.     

Polymers dynamics of the nonfluoro,nano-brush repelling agent with self-stratifying property in water-based coatings

While perfluoroalkyl acids (PFAAs), also known as C8s, are used extensively in textile repellent coatings, concerns have arisen for their carcinogenicity and hazardous effects on the environment. In this study, a novel water-based, nonfluoro, and nanobrush textile repelling agent was prepared by conventional sol–gel chemistry using amorphous fumed silica and n-octyltriethoxysilane as the starting materials. Minimal interaction between the designed repelling agent and marketed water-based resins was confirmed using linear viscosity region (LVR) analysis and asymmetric-flow field-flow fractionation (AF4), suggesting the self-stratification potential of the repelling agent. More specifically, the repelling agent exhibited excellent compatibility and self-stratifying ability with a force-emulsified acrylic-based resin, affording a water contact angle of 104.3° when incorporated at 7% solid content. Performance tests carried out on thermoplastic polyurethane (TPU) revealed excellent adhesion (100/100) of a final formulation, and a significant increase in water contact angle from 80.1° to 103.8° after treatment. In addition, the fouling area after the removal of a submerged sample from a mixture of slurry, polymer, and oil decreased from 48 to 1% when the repelling agent was added. Moreover, the sludge-fouling property remained unchanged after 1000 cycles of abrasion. These findings demonstrate the potential of the described nonfluoro, nanobrush repelling agent as an environmentally safe alternative for use with commercial resins, in turn realizing a fully water-based hydrophobic coating. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48003.