Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

Composites based on hafnium carbide and reinforced with continuous naked carbon fiber with and without PyC interface were prepared at low temperature by precursor infiltration and pyrolysis and chemical vapor deposition method. The microstructure, mechanical property, cyclic ablation and fiber bundle push-in tests of the composites were investigated. The results show that after three times ablation cycles, the bending strength of samples without PyC interface decreased by 63.6 %; the bending strength of samples with PyC interface only decreased by 37.8 %. The force displacement curve of the samples with PyC interface presented a well pseudoplastic deformation state. The mechanical behavior difference of two kinds of composites was due to crucial function of PyC interface phase including protection of fiber and weakening of fiber/matrix interface.     

Pressure-induced transparency of MgO,Al2O3, AlN,and cBN ceramics at room temperature

The in situ axial X-ray diffraction patterns of four ceramic powder samples (MgO, Al₂O₃, AlN, and cBN) that were compressed in a diamond anvil cell under uniaxial non-hydrostatic conditions were recorded. The microscopic deviatoric stress as a function of the pressure was determined from the X-ray diffraction peak broadening analysis: the curves increased approximately linearly with the pressure at the initial compression stage and then levelled off under further compression. Pressure-induced transparency was observed in all of the samples under compression, and the pressure at the turning point on the curves of the microscopic deviatoric stress versus pressure corresponded to the pressure at which the samples became transparent. Analysis of the microstructural features of the pressure-induced transparent samples indicated that the compression caused the grains to fracture, and the broken grains bonded with each other. We demonstrated that the ceramics’ pressure-induced transparency was a process during which the grains were squeezed and broken, the pores were close between the grains, and the broken grains were re-bonded under compression.     

A mini review on two-dimensional nanomaterial assembly

Two-dimensional (2D) nanomaterials have attracted a great deal of attention since the discovery of graphene in 2004, due to their intriguing physicochemical properties and wide-ranging applications in catalysis, energy-related devices, electronics and optoelectronics. To maximize the potential of 2D nanomaterials for their technological applications, controlled assembly of 2D nanobulding blocks into integrated systems is critically needed. This mini review summarizes the reported strategies of 2D materials-based assembly into integrated functional nanostructures, from in-situ assembly method to post-synthesis assembly. The applications of 2D assembled integrated structures are also covered, especially in the areas of energy, electronics and sensing, and we conclude with discussion on the remaining challenges and potential directions in this emerging field.

     

9000m顶部驱动钻井装置结构选型研究

为大幅提高钻井效率,针对9 000 m钻井深度对顶驱的设计要求,通过比较顶驱装置关键部分几种典型的结构,提出适合该型号顶部驱动钻井装置的最优结构形式,为后续9 000 m钻井深度顶部驱动钻井装置的研究提供指导和借鉴。     

脉冲电沉积镍-铜合金

采用脉冲电沉积技术在304不锈钢表面制备Ni-Cu合金镀层,镀液组成和工艺条件为:NiSO4ꞏ6H2O 200g/L,CuSO4ꞏ5H2O 10 g/L,十二烷基硫酸钠0.2 g/L,柠檬酸钠80 g/L,糖精0.2 g/L,pH 4.0,温度25°C,搅拌速率30 r/min,平均电流密度40~120 mA/cm2,脉冲频率0~100 Hz,占空比20%~90%,时间30 min。研究了平均电流密度、脉冲频率和占空比对Ni-Cu合金镀层的元素组成、表面形貌和显微硬度的影响,得到较优的工艺参数为:平均电流密度40 mA/cm2,脉冲频率50 Hz,占空比60%。该条件下所得Ni-Cu合金镀层由质量分数分别为56.53%和43.47%的Ni和Cu组成,呈“菜花”状形貌,结晶细致、均匀,显微硬度为614.4 HV。     

海绵负载纳米Al2O3复合吸附剂去除水中硒研究

研究制备了海绵负载纳米Al2O3微球的复合吸附剂(NAS),并用于对Se(Ⅳ)和Se(Ⅵ)的吸附。结果表明,合成的纳米Al2O3微球(NAO)的平均尺寸为200~400 nm,在海绵上负载NAO会使其分散性更好。当NAO负载量分别为80 mg/g和60 mg/g时,NAS对Se(Ⅳ)和Se(Ⅵ)的吸附性能为佳,分别需要60、120 min达到平衡,适应pH为2~5;两者均符合准2级动力学模型;NAS对Se(Ⅳ)、Se(Ⅵ)的最大吸附容量分别为137.2、143.9 mg/g,能很好地与Freundlich模型拟合,说明NAS表面不均匀,且属于多层吸附。经过2次的循环,对Se(Ⅳ)和Se(Ⅵ)的去除率有所降低,但均仍保持在一定的水平,说明NAS可再生循环利用。NAS作为一种新型吸附剂去除水中Se具有较好的应用前景。     

WIRELESS BODY-AREA NETWORKS

The last decade has witnessed the convergence of three giant worlds:electronics,computer science and telecommunications.The next decade should follow this convergence in most of our activities with the generalization of sensor networks.In particular with the progress in medicine,people live longer and the aging of population will push the development of wireless person-     

Colostrum source and passive immunity transfer in dairy bull calves

Colostrum is essential for good neonate health; however, it is not known whether different calves absorb the nutrients from colostrum equally well. In this study, the absorption of protein, IgG, and γ-glutamyl transferase was compared in newborn dairy bull calves for 1 wk after feeding colostrum from different sources. Thirty-five Holstein-Friesian bull calves were randomly allocated into 3 groups and fed colostrum within 4 h after birth. Group A calves (n = 12) were bottle fed colostrum from their own dam for 3 d. Colostrum from these group A cows was also used as foster cow colostrum for the group B calves (n = 12), such that each group A and B calf pair received identical colostrum from each milking of the respective group A dam (10% of birth weight per day). The group C calves (n = 11) were fed 1 bottle (2 L) of pooled colostrum and transition milk (referred to as pooled colostrum), as was the standard practice on the dairy farm. The pooled colostrum was collected from the other dairy cows on the farm 0 to 4 d postpartum and stored at 4°C for less than 12 h. Blood was sampled from calves before the first feeding and at 1, 2, 3, and 7 d after birth. Levels of total solids, total protein, and IgG were higher in the dam colostrum than in the pooled colostrum. At birth, there were no differences between the calf groups for any measurements, and all calves had very low IgG levels. After receiving colostrum, the glucose, plasma γ-glutamyl transferase, serum total protein, and IgG concentrations increased significantly in all calves. There were no differences in any blood measurements at any time point between the pairs of group A and group B calves that received colostrum from the same cow except for the IgG concentration 2 d after birth. However, the group A calves had a higher total serum protein level and IgG concentration than the group C calves for all the time points after the first feeding. The group B calves had a higher IgG concentration than the group C calves on d 1, 2, and 7 after birth. Compared with groups A and B, there was no difference in the proportion of calves in group C that failed to have passive immunity transferred adequately based on the IgG threshold (<10 g/L). Thus, the calves receiving identical colostrum from the same cow had the same levels of IgG, and even the pooled colostrum provided sufficient transfer of IgG as the calves were fed within 4 h after birth.