电压对电刷镀三价铬镀层性能的影响

在45钢表面电刷镀得到三价铬镀层,镀液组成和工艺条件为:Cr2(SO4)36H2O 0.4 mol/L,甲酸铵0.5 mol/L,氨基乙酸0.5 mol/L,H3BO30.6 mol/L,NaH2PO2 H2O 0.3 mol/L,pH=1.5,温度50°C,镀笔移动速率15 cm/s。研究了电压对镀铬层显微结构、表面粗糙度、厚度、显微硬度和耐磨性的影响。随电压增大,镀层厚度增大,显微硬度和耐磨性均先提高后降低。电压为14 V时,镀层的表面平整,粗糙度为2.387μm,显微硬度为602 HV,耐磨性最好。     

Chromium evaporation and oxidation characteristics of alumina-forming austenitic stainless steels for balance of plant applications in solid oxide fuel cells

The chromium (Cr) evaporation behavior of several different types of iron (Fe)-based AFA alloys and benchmark Cr₂O₃-forming Fe-based 310 and Ni-based 625 alloys was investigated for 500 h exposures at 800 °C to 900 °C in air with 10% H₂O. The Cr evaporation rates from alumina-forming austenitic (AFA) alloys were ~5 to 35 times lower than that of the Cr₂O₃-forming alloys depending on alloy and temperature. The Cr evaporation behavior was correlated with extensive characterization of the chemistry and microstructure of the oxide scales, which also revealed a degree of quartz tube Si contamination during the test. Long-term oxidation kinetics were also assessed at 800 to 1000 °C for up to 10,000 h in air with 10% H₂O to provide further guidance for SOFC BOP component alloy selection.     

基于步冷试验的2.25Cr-1Mo-0.25V钢母材及焊缝回火脆化研究

对原始态、步冷态、脱脆态和脱脆步冷态2.25Cr-1Mo-0.25V钢母材及焊缝冲击试验结果进行分析,得到了母材和焊缝在不同状态下的韧脆转变温度vTr54.2和FATT以及脆化度ΔvTr54.2和ΔFATT。试验结果表明,步冷试验之后,母材发生较低程度脆化或脱脆现象,但是脆化度或脱脆度较低,表明母材具有良好的抗回火脆化性能;经脱脆试验后,母材和焊缝都发生较高程度的脱脆,表明材料的脆化主要是由于回火脆化引起的,脱脆试验使得材料的韧脆转变温度降低;脱脆步冷试验后,焊缝发生较高程度的脆化,焊缝对脱脆步冷试验的敏感性较高,脱脆步冷试验有效促进了焊缝的脆化。在相同脆化条件下,母材的脆化敏感性低于焊缝,焊缝更易发生脆化。     

Dependence of Lamellar Eutectic Growth with Convection on Boundary Conditions and Geometric Confinement: A Phase-Field Lattice-Boltzmann Study

Metallurgical and Materials Transactions B - Simulating eutectic growth with convection is challenging because of the enormous computing demand resulting from the required domain size compared with...     

Investigation of machining and wear performance of various diamond micro-grinding tools

The International Journal of Advanced Manufacturing Technology - The wear of micro-grinding tools less than 1 mm in diameter is crucial for achieving acceptable surface quality and accurate...     

防振条约束失效对蒸汽发生器传热管面内流弹失稳的影响研究

根据防振条布置以及面内支承连续失效个数，将防振条面内约束失效分析划分为多种工况，分析了不同工况下面内约束失效对传热管面内模态的影响，采用各位置阻尼在振型函数上进行加权平均的方法计算了各阶模态的阻尼比，进而研究了防振条面内不同约束对传热管面内流弹失稳的影响。分析结果表明，随着面内支承连续失效位置的增多，弯管段面内首阶模态频率不断降低，出现在弯管段的振型越加明显；弯管段面内首阶模态不一定是最大流弹失稳比值出现的模态，最大流弹失稳比值出现模态的振型几乎都出现在弯管段；随着面内支承连续失效位置的增多，面内流弹失稳比值不断增大，当连续3个及以上防振条面内约束失效时，将出现流弹失稳现象。     

Corrosion behavior of Cu–Sn bronze alloys in simulated archeological soil media

The corrosion behavior of synthetic Cu–Sn bronze alloys with six different Sn contents was examined through an electrochemical test and a synthetic test in a simulated corrosive medium. The mechanism of corrosion and the morphology of the corroded surfaces were characterized through field emission scanning electron microscopy equipped with energy-dispersive spectroscopy. At the corrosion potential, the corrosion behavior appears to be determined by the charge transfer step and the diffusion process. It was found that the bronze-IV (Cu–26.8Sn) specimen exhibited the best corrosion resistance, as evidenced by a low corrosion current density and a high impedance. This improvement resulted from an increase in the content of the Cu–Sn solid solution in the alloy, which was conducive to forming a relatively more protective passive film on the surface of the bronze alloy. This finding would be valuable in the anticorrosion protection of archeological artefacts after their excavation.     

钨系延期药预点火反应机理研究

通过程控升温模拟点火条件，根据ＤＳＣ图谱分析，找出主要反应区的温度范围。研究结果表明，钨系延期药预点火反应是一个真正的固－固反应。     

工艺条件对薄片陶瓷材料凝胶流延成型的影响

利用有机单体的聚合原理，成功进行了陶瓷薄片材料的凝胶流延成型。讨论了工艺条件对成型的影响。使用惰性气氛保护克服了单体聚合反应中的氧气阻聚问题，浆料在一定温度和气氛条件下能够顺利完成聚合反应。所成型的坯体具有良好的强度和柔韧性，在1550℃经2h烧结，烧结样品显微结构均匀，没有发现晶粒异常长大现象，烧结体致密度达到97．7％。     

DataSocket技术在远程测试中的研究与应用

本文介绍了一种实时数据传输技术-DataSocket,并给出了具体实例说明了如何将利用DataSocket技术来实现远程测试。